The influence of the cooling method on shortening the cycle of multi-layer arc-surfacing of thin walls

Cegielski Paweł, Grześ Jarosław, Łacisz Wojciech

Welding Technology Review

|

2019

|

R. 91, nr 1

13--18

EN

The use of 3D printing methods in the industry is becoming more frequent and popular. It brings specific economic effects, enables quick and precise production of machine parts and devices. The article presents a fragment of research carried out in the Welding Engineering Department of the Warsaw University of Technology on the application of MAG arc welding for 3D printing. The MAG method was used to try to produce thin walls. The aim of the presented research was to determine the effect of the cooling method on shortening the time of manufacturing the 3D model of thin walls. The models were made using G3Si1 and 316LSi electrode wires. In the first part of the research, an interpass temperature of 50 °C, 100 °C and 150 °C, achieved by free cooling was adopted. In the second part, the interpass temperature was 100 °C and was achieved by forced cooling with a copper plate, a fan and a stream of compressed air. The greatest reduction in the time of manufacturing the 3D model of a thin wall was obtained for cooling using compressed air.

PL

Wykorzystanie w przemyśle metod drukowania 3D jest coraz częstsze i popularniejsze. Przynosi konkretne efekty ekonomiczne, umożliwia szybkie i precyzyjne wytwarzanie części maszyn i urządzeń. W artykule przedstawiono fragment badań prowadzonych w Zakładzie Inżynierii Spajania Politechniki Warszawskiej nad zastosowaniem napawania łukowego metodą MAG do drukowania 3D. Metodę MAG wykorzystano do prób wytwarzania cienkich ścian. Celem prezentowanych badań było określenie wpływu sposobu chłodzenia na skrócenie czasu wytwarzania modelu 3D cienkich ścian. Modele wykonano stosując druty elektrodowe G3Si1 i 316LSi. W pierwszej części badań przyjęto temperaturę międzyściegową równą 50 °C, 100 °C i 150 °C, osiąganą poprzez chłodzenie swobodne. W drugiej części temperatura międzyściegowa wynosiła 100 °C i osiągana była drogą wymuszonego chłodzenia za pomocą płyty miedzianej, wentylatora i strumienia sprężonego powietrza. Największe skrócenie czasu wytwarzania modelu 3D cienkiej ściany otrzymano dla chłodzenia za pomocą sprężonego powietrza.

2

The study of the surface quality of the thin wall bearing units to rolls roller seats pipe conveyor

Michalik P., Zajac J., Fabianova J., Mital D.

Advances in Science and Technology. Research Journal

|

2017

|

Vol. 11, no 2

192--197

EN

The article deals with the study of surface roughness of thin-walled houses bearing rollers for roller mills. The size and shape of the rear end housing was designed in order to measure the surface roughness of the inner cylindrical bearing surface with a wall thickness of 4, 5 and 6 mm. For comparison the roughness was measured also on the wall with a thickness 26 mm. The welded housing and the base plate was clamped in the machine vice jaw with a width of 150 mm. Material components bearing small house has been fine-grain weld able steel bearing S355. For finishing the hole with a diameter of 40 mm, a tool with a diameter of 32 mm was used with three cutting blades SDXT09M405R MM. Spindle speed was 1350 rev / min. Tool feed speed was 850 mm / min. The surface roughness was measured with a Mitutoyo SJ 400th.

3

Thin Wall Ductile Iron Castings as Substitutes for Aluminium Alloy Castings

Fraś E., Górny M., Lopez H.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 2

459--465

EN

The paper discusses the reasons behind current trends for substituting cast iron castings by aluminum alloys. In particular it is shown that it is possible to produce thin wall castings (control arms, cantilevers and rotors) made of ductile iron without the development of chills, cold laps or misruns, and with a strength to weight ratio of up 87 MPa cm3/g. In addition, austenitizing at 900 °C for 20 minutes and then austempering in a salt bath at 350 °C for 15 minutes promotes the development of a fully ausferritic matrix in thin wall castings with a the strength to weight ratio increase of up to 154 MPa cm3/g. Finally, it is shown that thin wall castings made of ductile or austemperded cast iron can be lighter and with superior mechanical properties then their substitutes made of aluminum alloy.

PL

W pracy omówiono przyczyny aktualnego trendu zastępowania odlewów z żeliwa przez odlewy ze stopów aluminium. W szczególności wykazano, że możliwe jest wytworzenie odlewów cienkościennych (wahacze, wsporniki, wirniki), wykonanych z żeliwa sferoidalnego bez zabieleń, niedolewów i niespawów oraz posiadających wskaźnik wytrzymałości (stosunek wytrzymałości do gęstości) wynoszący do 87 MPa cm3/g. Ponadto zastosowanie obróbki cieplnej polegającej na austenityzacji w temperaturze 900°C przez 20 minut oraz hartowaniu izotermicznemu w kąpieli solnej w temperaturze 350°C przez 15 minut powoduje otrzymanie osnowy austerrytycznej w odlewach cienkościennych, co zwiększa wskaźnik wytrzymałości do 154 MPa cm3/g. Z przeprowadzonych badań wynika, że odlewy z żeliwa sferoidalnego mogą być lżejsze od ich substytutów ze stopów aluminium, a przy tym charakteryzować się podobnymi lub lepszymi właściwościami mechanicznymi.

4

Thin wall ductile iron castings: technological aspects

Fraś E., Górny M., Kapturkiewicz W.

Archives of Foundry Engineering

|

2013

|

Vol. 13, iss. 1

23--28

EN

The paper discusses the reasons for the current trend of substituting ductile iron castings by aluminum alloys castings. However, it has been shown that ductile iron is superior to aluminum alloys in many applications. In particular it has been demonstrated that is possible to produce thin wall wheel rim made of ductile iron without the development of chills, cold laps or misruns. In addition it has been shown that thin wall wheel rim made of ductile iron can have the same weight, and better mechanical properties, than their substitutes made of aluminum alloys.