The B-Li System. Calorimetric and Theoretical Studies

Dębski A., Braga M. H., Gąsior W.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 4

2513--2520

The standard enthalpy of formation of the B78Li22 alloy was measured with the use of the water reaction calorimetric method at 25 °C (298 K). An X-ray diffraction study of the prepared sample was conducted. The obtained diffraction pattern was different from the patterns for the B3Li and B14Li3 phases. The standard enthalpy of formation obtained for the B78Li22 alloy was -39.0 ± 0.7 kJ/mole of atoms. This value corresponds well with the formation enthalpies of the phases from the boron-lithium system. Theoretical calculations of the standard enthalpy of formation were conducted for the B78Li22 alloy and the phases from B-Li system, which were investigated earlier. A discussion of the deviations observed between both sets of data (experimental and calculated) was performed. Additionally, DTA studies were performed for 14 alloys of the concentrations from 40 to 100 at. % of Li.

Standardowa entalpia tworzenia stopu B78Li22 została zmierzona metodą kalorymetrii reakcyjnej wodnej. Próbka stopu po wyżarzaniu była poddana badaniom strukturalnym metodą dyfrakcji promieniowania rentgenowskiego. Uzyskany dyfraktogram jest inny od dyfraktogramów dla faz B3Li ora B14Li3. Zmierzona standardowa entalpia tworzenia stopu B78Li22 wyniosła -39.0 ± 0.7 kJ/mol atomów. Wartość ta dobrze koreluje z entalpią tworzenia faz z układu bor-lit. Przeprowadzone zostały również obliczenia teoretyczne standardowej entalpii tworzenia dla stopu B78Li22 oraz faz z układu B-Li, wcześniej badanych. Zaobserwowane rozbieżności między teoretycznymi i eksperymentalnymi wartościami entalpii tworzenia zostały przedyskutowane. Ponadto, wykonano pomiary DTA dla 14 stopów o stężeniach od 40 do 100 % at. Li.

Enthalpy of formation of intermetallic phases from Fe-Ni-Ti System. Comparative studies

Gąsior W., Dębski A.

Archives of Metallurgy and Materials

2012

Vol. 57, iss. 4

1095-1104

The solution calorimetric method was used for the measurement of the formation enthalpy of the binary FeTi and Fe2Ti intermetallic phases and of the FeNiTi2 phase from the region of the ternary B2 one. The FeNi and FeNiTi2 phases were prepared by levitation melting and the Fe2Ti phase - by melting the metals in a glove-box under high purity argon. The alloys obtained were identified by the X-ray diffraction analysis. The structural study of the alloys with the composition equal to the FeTi and Fe2Ti phase confirmed the mentioned phases mainly in the samples. In the case of the ternary alloy of the composition of the FeNiTi2 phase, a slight amount of iron was also found. The obtained values of the formation enthalpy equal as follows: -27.2±1.3 kJ/mole of atoms, -22.5±1.4 kJ/mole of atoms and -34.2±1.3 kJ/mole of atoms for the Fe2Ti, FeTi and FeNiTi2 phase, respectively.

Stosując kalorymetryczna metodę rozpuszczania zostały zmierzone entalpie tworzenia dwóch dwuskładnikowych faz międzymetalicznych FeTi i Fe2Ti oraz z obszaru fazy trójskładnikowej B2. Fazy FeTi i FeNiTi2 zostały przygotowane metoda lewitacyjnego topienia a faza Fe2Ti metoda metalurgiczna przez stopienie metali w komorze manipulacyjnej z atmosfera ochronna argonu wysokiej czystości. Otrzymane stopy były poddane identyfikacji metoda analizy dyfrakcji promieniowania rentgenowskiego. Badania te potwierdziły występowanie w próbkach dwuskładnikowych głównie faz FeTi i Fe2Ti. W przypadku stopu trójskładnikowego oprócz fazy FeNiTi2 została wykryta niewielka ilość żelaza. Zmierzone wartości entalpii tworzenia faz wynoszą: -27.2±1.3 kJ/mol atomów dla Fe2Ti, -22.5±1.4 kJ/mol atomów dla FeTi oraz -34.2±1.3 kJ/mol atomów dla FeNiTi2.