Thermally Hardened Moulding and Core Sands with Hydrated Sodium Silicate Designed for Al Alloy Castings

Major-Gabryś K. A., Grabarczyk A. P., Dobosz S. M.

Archives of Foundry Engineering

|

2018

|

Vol. 18, iss. 3

132--137

EN

The necessity of obtaining high quality castings forces both researchers and producers to undertake research in the field of moulding sands. The key is to obtain moulding and core sands which will ensure relevant technological parameters along with high environmental standards. The most important group in this research constitutes of moulding sands with hydrated sodium silicate. The aim of the article is to propose optimized parameters of hardening process of moulding sands with hydrated sodium silicate prepared in warm-box technology. This work focuses on mechanical and thermal deformation of moulding sands with hydrated sodium silicate and inorganic additives prepared in warm-box technology. Tested moulding sands were hardened in the temperature of 140ºC for different time periods. Bending strength, thermal deformation and thermal degradation was tested. Chosen parameters were tested immediately after hardening and after 1h of cooling. Conducted research proved that it is possible to eliminate inorganic additives from moulding sands compositions. Moulding sands without additives have good enough strength properties and their economic and ecological character is improved.

2

Opracowanie podstaw technologii umacniania cieplnego prętów i walcówki ze stali spawalnych o granicy plastyczności powyżej 500 MPa, metodami umacniania strukturalnego i wydzieleniowego

Żak A., Marcisz J.

Prace Instytutu Metalurgii Żelaza

|

2006

|

T. 58, nr 3

61-63

PL

Celem pracy było opracowanie podstaw technologii umacniania cieplnego po odkształceniu na gorąco, umożliwiającej wytwarzanie prętów do zbrojenia betonu o właściwościach mechanicznych i technologicznych spełniających stawiane prętom o wysokiej ciągliwości klasy B500SP. W ramach pracy przeprowadzono próby walcowania i umacniania cieplnego prętów o średnicach 8, 10, 12 i 16 ze stali o zmiennej zawartości węgla, podwyższonej zawartości krzemu i ze stali z mikrododatkiem wanadu z zastosowaniem, różnych parametrów chłodzenia wodnego bezpośrednio po walcowaniu. Próby walcowania i umacniania cieplnego wykonano na przemysłowej linii w Ferrostalu Łabędy. Na podstawie uzyskanych wyników badań właściwości prętów ustalono zakres składu chemicznego stali oraz wstępne wartości parametrów chłodzenia pozwalające na spełnienie wymagań stawianych prętom o podwyższonej plastyczności.

EN

The purpose of this paper was to develop the foundations for technology of thermal hardening after hot deformation to allow making concrete reinforcement bars with mechanical and technological properties that would meeet the requirements for high-ductility bars of B500SP grade. As apart of the paper rolling and thermal hardening testy of bars with diameters of 8,10,12 and 16, made from steel with changing carbon content, increased silicon content and from steel with microadditive of vanadium, were carried out using different parameters of water cooling applied immediately after rolling. The rolling and therrmal hardening tests were carried out on the industrial line in Ferrostal Łabędy. Based on the results of testing the bar properties, the range of chemical constitution of the steel and preliminary values for the cooling parameters that would allow the requirements for enhanced ductility bars to be met were defined.

3

Modyfikowane warstwy azotowane wytwarzane w procesie regulowanym, połączonym z utwardzaniem cieplnym podłoża.

Sułkowski I., Tacikowski J., Senatorski J., Michalski J.

Inżynieria Materiałowa

|

2000

|

R. XXI, nr 6

449-452

PL

Podjęte badania dotyczyły wytwarzania, budowy i własności tribologicznych zmodyfikowanych warstw o złożonej strukturze martenzytyczno-bainitycznej otrzymanych w procesie regulowanego azotowania gazowego połączonego z dalszym utwardzaniem cieplnym. W badaniach stosowano stal węglową gat. 45. Badania metaloznawcze warstw obejmowały wpływ parametrów azotowania i utwardzania cieplnego na końcowy efekt umocnienia: twardość powierzchniową, grubość warstwy umocnionej oraz rozkład twardości w warstwie i własności tribologiczne. Zastosowana obróbka umożliwiła wytworzenie na stali 45 umocnionej warstwy o twardości dochodzącej przy powierzchni do 900 HV i grubości do 1 mm, przy twardości powierzchniowej ok. 800 HV10. Wyniki badań wskazały na istotny wpływ grubości pierwotnej warstwy azotowanej na kształtowanie się własności tribologicznych utwardzanych stali.

EN

The undertaken research work referred to obtaining the modified layers with martensitic-bainitic structure and to investigation of their structure and tribological properties after controlled gas-nitriding process joint with thermal hardening. In this investigations carbon steel 45 is used. Investigations of nitrided layers embraced influence of parameters of nitriding and thermal hardening on final effect of consolidation: hardness of surface, thickness of strengthened layer and microhardness profiles in the layer as well as tribological properties. The treatment made possible obtaining the hardened layer on the 45 steel surface with hardness up to 900 HV and thickness up to 1 mm, by hardness of surface 800 HV10. The results of investigation show an essential influence of thicknesses of primary nitrided layers on the formation of tribological properties of hardened layers.