Estimation of lifetime of zirconia and zirconia-alumina composites using constant stress rate data

Wojteczko A., Lach R., Wojteczko K., Pędzich Z.

Composites Theory and Practice

2017

R. 17, nr 1

14--18

Ceramic failure, at stresses lower than those when KIc is reached, might be an effect of subcritical crack propagation. It occurs when the material is in service in the presence of water (even water vapour) for a long time. If this phenomenon leads to limiting its useful life, it is important to predict the lifetime of a ceramic component under specific conditions. Dynamic tests are suitable to determine subcritical crack growth parameters. Calculations are made to determine material behaviour under static loading on the basis of strength data. The paper presents the results for zirconia-alumina composites with 5, 15 and 50 vol.% inclusions to compare materials with different types of microstructures. Pure zirconia sintered bodies were used as the reference material.

Zniszczenie materiałów ceramicznych, przy obciążeniach niższych niż te, gdy osiągane jest KIc, może być efektem pękania podkrytycznego. Ma to miejsce, gdy materiał używany jest w obecności wody (również w postaci pary wodnej) przez długi czas. Jeśli to zjawisko prowadzi do ograniczenia czasu użytkowania, istotne jest, aby przewidzieć czas przeżycia elementu ceramicznego działającego w danych warunkach. Odpowiednie do wyznaczania parametrów pękania podkrytycznego są testy dynamiczne. Obliczenia wykonywane są w celu przewidzenia zachowania materiału pod stałymi obciążeniami na podstawie wyników wytrzymałości. Praca przedstawia wyniki dla kompozytów tlenek cyrkonu-tlenek glinu z 5, 15 oraz 50 obj.% wtrąceń w celu porównania materiałów o różnych typach mikrostruktur. Spieki z czystego dwutlenku cyrkonu zostały zbadane jako materiał odniesienia.

Cavitation wear of ceramics. Part 1, Mechanisms of cavitation wear of alumina and tetragonal zirconia sintered polycrystals

Pędzioch Z., Jasionowski R., Ziąbka M.

Composites Theory and Practice

2013

R. 13, nr 4

288-292

The usage of ceramic materials in applications endangered by intensive cavitation could limit erosion phenomena. In the presented work, cavitation erosion resistance of commonly used oxide phases (α-alumina, tetragonal zirconia) in structural application were investigated. Volumetric wear of both materials was compared to the wear rate of FeAl48 alloy. Both oxides were more resistant for cavitation than intermetallic phase. Observations by means of SEM technique showed that surface destructions run in a similar way for both investigated oxides. The degradation proceeded by removing of the whole grains from sintered body. However, in the alumina grains were removed from a wide area, opposite to the zirconia material, which was degraded in limited, ribbon-like areas. In this case destruction reached deeper than only the one grain into material.

Użycie materiałów ceramicznych w zastosowaniach, w których materiał narażony jest na intensywną kawitację, może ograniczyć zużycie. W prezentowanej pracy zbadano odporność na zużycie kawitacyjne powszechnie stosowanych faz tlenkowych (α-tlenku glinu i tetragonalnego dwutlenku cyrkonu). Zużycie objętościowe obu materiałów porównano ze zużyciem stopu FeAl48. Oba tlenki były odporniejsze na zużycie niż faza międzymetaliczna. Stwierdzono, że dwutlenek cyrkonu jest odporniejszy na erozję kawitacyjną. Obserwacje SEM pokazały, że destrukcja powierzchni przebiega w obu tlenkach w podobny sposób. Zniszczenie polega na usuwaniu całych ziaren ze spieków. Jednakże, ziarna tlenku glinu usuwane są jako monoziarnowa warstwa na stosunkowo dużej powierzchni, a ziarna dwutlenku cyrkonu usuwane są z obszarów wzdłuż nieregularnych linii na głębokość conajmniej kilku ziaren.