FP-LMTO study of structural, electronic, thermodynamic and optical properties of Mg x Cd1−x Se alloys

Bensaid D, Ameri M, El Hanani M D, Azaz Y, Bendouma D, Al-Douri Y, Ameri I

Materials Science Poland

|

2014

|

Vol. 32, No. 4

719--728

EN

Structural, electronic and optical properties of MgxCd1−xSe (0 6 x 6 1) are calculated for the first time using density functional theory. Our results show that these properties are strongly dependent on molar fraction of particular components – x. The bond between Cd and Se is partially covalent and the covalent nature of the bond decreases as the concentration of Mg increases from 0 % to 100 %. It is found that MgxCd1−xSe has a direct band gap in the entire range of x and the band gap of the alloy increases from 0.43 to 2.46 eV with the increase in Mg concentration. Frequency dependent dielectric constants ε1(ω),ε2(ω) refractive index n(ω) are also calculated and discussed in detail. The peak value of refractive indices shifts to higher energy regions with the increase in Mg. The larger value of the extraordinary refractive index confirms that the material is a positive birefringence crystal. The present comprehensive theoretical study of the optoelectronic properties of the material predicts that it can be effectively used in optoelectronic applications in the wide range of spectra: IR, visible and UV. In addition, we have also predicted the heat capacities (CV ), the entropy (S), the internal energy (U) and the Helmholtz free energy (F) of MgxCd1−xSe ternary alloys.

2

The efficiency of evolutionary optimization of magnetic properties of ternary alloy

Gwizdałła T.M.

Prace Naukowe Politechniki Warszawskiej. Elektronika

|

2006

|

z. 156

155-162

EN

The area of magnetism offers a wealth of possibilities to study different algorithmic approaches. The reason is the diversity of different forms which can be used to describe magnetic samples. One can start from the most simple Ising-like system which, being of physical origin, became an inspiration for many models in a various areas of science and the formulation of which fits ideally the earliest representations of genetic algorithms. The recent problems concern elaborate molecular structures, like eg. spin glasses where the character of interaction between the spins of the same type may be different depending on some random variable or mixed alloys which can have different stoichiometry or structure and therefore present visibly distinct magnetic characteristics. In this paper we will deal with the mixed magnetic ternary alloy - an analog of prussian blue. Some results concerning the physical conclusions coming from applying the evolutionary computation to analyse this material have already been published and here the attention will be paid to the influence of parameter change on the efficiency of procedure.

3

Analiza czynników wpływających na krystalizację eutektyki w stopie AI-Cu-Ag

Nocuń S., Konopka Z., Zyska A., Łągiewka M., Bober A.

Archiwum Odlewnictwa

|

2006

|

R. 6, nr 22

338-343

PL

Praca przedstawia analizę czynników determinujących rodzaj eutektyki podwójnej AI-Al_{2}Cu w potrójnym stopie AI-Cu-Ag. Czynniki jakie były analizowane to: entropia rozpuszczania faz eutektycznych, ułamek objętościowy danej fazy eutektycznej, prędkość wzrostu i gradient temperatury.

EN

In this paper it was shown the influence of the parameters such as: entropy of fusion, volume fraction, velocity of the unidirectional solidification on the lamellar eutectic obtained during unidirectional solidification. It was shown that all known parameters allow us to classify obtained eutectic into regular lamellar eutectic what was proven during the microscopy observations shown on the figure 1. There is also shown the disturbances occurred during increasing the velocity of the unidirectional solidification - shown on the figure 2. It can be estimated that this disturbances are occurred by evolution of the lamellar structure into the rod eutectic, or even loosing the regularity of the structure.

4

Growth of MOCVD HgCdTe heterostructures for uncooled infrared photodetectors

Piotrowski A., Madejczyk P., Gawron W., Kłos K., Pawluczyk J., Grudzień M., Piotrowski J., Rogalski A.

Bulletin of the Polish Academy of Sciences. Technical Sciences

|

2005

|

Vol. 53, nr 2

139-149

EN

In the paper recent progress at VIGO/MUT (Military University of Technology) MOCVD Laboratory in the growth of Hg1-xCdx Te (HgCdTe) multilayer heterostructures on GaAs/CdTe substrates is presented. The optimum conditions for the growth of single layers and complex multilayer heterostructures have been established. One of the crucial stages of HgCdTe epitaxy is CdTe nucleation on GaAs substrate. Successful composite substrates have been obtained with suitable substrate preparation, liner and susceptor treatment, proper control of background fluxes and appropriate nucleation conditions. The other critical stage is the interdiffused multilayer process (IMP). The growth of device-quality HgCdTe heterostructures requires complete homogenization of CdTe-HgTe pairs preserving at the same time suitable sharpness of composition and doping profiles. This requires for IMP pairs to be very thin and grown in a short time. Arsenic and iodine have been used for acceptor and donor doping. Suitable growth conditions and post growth anneal is essential for stable and reproducible doping. In situ anneal seems to be sufficient for iodine doping at any required level. In contrast, efficient As doping with near 100% activation requires ex situ anneal at near saturated mercury vapours. As a result we are able to grow multilayer fully doped (100) and (111) heterostructures for various infrared devices including photoconductors, photo electromagnetic and photovoltaic detectors. The present generation of uncooled long wavelength infrared devices is based on multijunction photovoltaic devices. The technology steps in fabrication of devices are described. It is shown that near-BLIP performance is possible to achieve at c.a 230 K with optical immersion. These devices are especially promising as 7.8-9.5-J-[mu]m detectors, indicating the potential for achieving detectivities above 10 do potęgi 9 cmHz1/2/W.

5

Wpływ prędkości krystalizacji kierunkowej na odległość międzypłytkową eutektyki w stopie Al-Ag-Cu

Konopka Z., Nocuń S. N.

Archiwum Odlewnictwa

|

2004

|

R. 4, nr 14

243-248

PL

W pracy przedstawiono wyniki pomiarów odległości międzypłytkowej [alfa] eutektyki w potrójnym stopie AI-Ag-Cu w zależności od zmiany prędkości wzrostu eutektyki podczas procesu krystalizacji kierunkowej. Dokonane pomiary potwierdzają prawo wzrostu eutektyki regularnej [alfa]^2 x V=const.

EN

In this paper it was shown the measurements results of the spacing between eutectic lamellae [alfa] in the ternary AI-Ag-Cu alloy according to changes of the velocity of the unidirectional solidification. Results show that the eutectic growth law [alfa]^2xV=const. is true.

6

Wysokotemperaturowa korozja siarkowa stopów TiAlNb i TiAlAg

Przybylski K., Prażuch J., Maziarz W., Dutkiewicz J.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 4-5

213--218

PL

Zbadano kinetykę siarkowania dwu- i trójskładnikowych stopów TiAl o składach: Ti-48Al, Ti-52Al-2Nb, Ti-51,2Al-5Nb, Ti-48,4Al-10Nb, Ti-45,9Al-15Nb i Ti-49Al-2Ag (%, at.) w temperaturze 900 stopni Celsjusza w parach siarki w zakresie ciśnień p(S2) od 10 do 1000 Pa. Stopy TiAl, TiAlNb i TiAlAg, otrzymane metodą mechanicznej syntezy (MS), miały budowę krystaliczną i zawierały dwie główne fazy: gamma-TiAl and alfa2-Ti3Al, o wielkości ziaren od około 0,2 do 1 mikrometra. Zidentyfikowano w nich również pewne ilości alfa-Ti oraz związków AlNb3 i Ag3Al. Siarkowanie stopów TiAlNb i TiAlAg w ww. warunkach przebiegało według prawa parabolicznego lub paraboliczno-liniowego w zależności od czasu reakcji siarkowania. Szybkość siarkowania wzrastała ze wzrostem zawartości niobu w zakresie od 2 do 15 % at. Nb. W przypadku stopu Ti-49Al-2Ag szybkość siarkowania była znacznie większa w porównaniu do stopu Ti-49Al-2Nb, co prawdopodobnie spowodowane było tworzeniem się ciekłej fazy Ag-Al. Zgorzeliny siarczkowe powstałe na międzymetalicznych fazach TiAlNb o zawartości niobu od 2 do 15% at. oraz na TiAl-2Ag były wielofazowe i składały się z trzech różnych warstw. Najbardziej zewnętrzna warstwa siarczkowa zbudowana była z Al2S3 z niewielką ilością siarczków tytanu. Następna warstwa składała się głównie z siarczków tytanu. Natomiast warstwa wewnętrzna zbudowana była z mieszaniny siarczków tytanu i siarczku glinu. W zgorzelinach tych zidentyfikowano następujące fazy siarczkowe: Al2S3, TiS, Ti3S4, TiS2 i Ti5S8, w zależności od warunków reakcji siarkowania (p(S2)=10/1000 Pa). Mikrostrukturę na przekrojach poprzecznych i skład fazowy produktów reakcji siarkowania badano metodą mikroskopii skaningowej (SEM), mikroanalizy rentgenowskiej (EDS) i dyfrakcji promieni rentgenowskich (XRD).

EN

The sulphidation behaviour of binary Ti-48Al and ternary Ti-52Al-2Nb, Ti-51.2Al-5Nb, Ti-48.4Al-10Nb and Ti-45.9Al-15Nb (at. %) alloys were studied in sulphur vapour atmosphere at 900 degrees centigrade in the pressure range of 10/1000 Pa. Binary TiAl and ternary TiAlNb, TiAlAg intermetallic alloys were prepared by mechanical alloying (MA) process. After annealing at 1250 degrees centigrade for 2 hrs in vacuum all three kinds of alloys were crystalline including two main phases gamma-TiAl and alpha2-Ti3Al with grain size in the range from about 0.2 to 1 micrometre. Some amounts of alpha-Ti, AlNb, and Ag3Al were also detected. In the present study the influence of niobum and silver additions to TiAl on the sulphidation kinetics, microstructure and chemical composition was investigated. Sulphidation of the TiAlNb and TiAlAg alloys in sulpur vapour atmosphere at 900 degrees centigrade in the pressure range of 10/1000 Pa followed a parabolic or parabolic-linear rate law depending on the time of reaction. The amounts of sulphidation increased with increasing addition of niobum in the range from 2/15 at. %. In the case of Ti-49Al-2Ag alloy sulphidation kinetics was much faster in comparison with other alloy compositions, caused probably by an Ag-Al liquid phase formation. The sulphide scales formed on TiAlNb with 2/15 at. % of Nb and TiAl-2 at. % Ag alloys had multi-layered structures of three different layers. It was observed that outermost sulphide layer is rich in Al2S3 with addition of some amount of Ti-sulphides and outer layer is rich in Ti-sulphides. The inner layer consisted of a mixture of Ti-sulphides and Al2S3. Ti-sulphides were represented by TiS, Ti3S4, TiS2, Ti5S8 depending on the sulphidation conditions, p(S2)=10/1000 Pa. The cross-sectional microstructure and phase composition of the reaction products were examined by scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDS), and X-ray diffraction analysis (XRD).

7

Wpływ składu chemicznego i parametrów mechanicznego wytwarzania na mikrostrukturę stopów na osnowie fazy gama-TiAl

Dymek S., Wróbel M., Blicharski M.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 4-5

182--188

PL

W pracy wytworzono stopy o następującym składzie chemicznym (% at.): TiAl48, TiAl45Cr5 i TiAl45V5. Syntezę stopów przeprowadzono metodą mechanicznego stopowania proszków czystych metali Ti (99 %), Al (99,5 %), Cr (99,95 %) oraz V (99,5%). Proces stopowania wykonano w laboratoryjnym atritorze typu Szegvari w atmosferze argonu. Komorę roboczą młyna chłodzono ciekłym azotem lub wodą. Stwierdzono, że wydłużenie czasu chłodzenia ciekłym azotem oraz dodatek pierwiastków Cr lub V prowadził do szybszego rozdrobnienia mikrostruktury mielonych proszków i skrócenia całkowitego czasu procesu mechanicznego stopowania. Badania przy użyciu trasmisyjnego mikroskopu elektronowego dowodzą, że wszystkie proszki, nawet po krótkim czasie mielenia, miały mikrostrukturę nanokrystaliczną. Wpływ chromu na przebieg procesu mechanicznego stopowania różni się od wpływu wanadu. Podczas mielenia w tych samych warunkach wanad przechodzi szybciej do roztworu stałego Ti(Al). Po procesie mechanicznego stopowania proszki konsolidowano przez prasowanie na gorąco. Obecność trzeciego pierwiastka (Cr lub V) wpływa znacząco na morfologię i dyspersję tlenków w materiale skonsolidowanym. W stopie dwuskładnikowym tworzą się stosunkowo duże tlenki, podczas gdy w stopach trójskładnikowych rozkład tlenków jest bimodalny, tj. pomiędzy tlenkami dużymi występuje drobny dyspersoid tlenkowy o wielkości rzędu kilku nanometrów.

EN

Alloys with chemical compositions of TiAl48, TiAl45Cr5 and TiAl45V5 (% at.) were synthesized by mechanical alloying in a Szegvari-type attritor. The elemental powders of Ti (99 % pure), Al (99,5 % pure), Cr (99,95 % pure) and V (99,5 % pure) were used for the synthesis. The process was carried out in an argon atmosphere. The milling chamber was cooled during the process by liquid nitrogen or water. It was found that prolongation of cooling by liquid nitrogen as well as alloying by Cr or V results in faster refinement of microstructure of the milled powders and makes a reduction in the total time of mechanical alloying. Investigation by means of a transmission electron microscope revealed that all powder particles, even after short processing times, exhibit nanocrystalline microstructure. An influence of chromium on the course of the mechanical alloying process differs from an influence of vanadium. At the same processing parameters vanadium dissolves faster in titanium than chromium does. After the mechanical alloying process the powders were compacted by hot pressing. The presence of the third element (Cr or V) exerts an influence on morphology and dispersion of oxides in the consolidated material. In the TiAl48 binary alloy oxide particles are relatively big while in the ternary alloys oxide size exhibit a bimodal distribution, i.e. among large oxide particles small, on the order of nanometer size, particles were found.

8

Selective oxidation of Fe-Ni-Cr alloys.

Danielewski M., Filipek R., Milewska A.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 4

278-280

PL

W oparciu o model utleniania stopów dwuskładnikowych typu Ni-Pt, Wagnera oraz uogólnioną metodę dyfuzji wzajemnej Darkena (GDM) przeprowadziliśmy symulacje selektywnego utleniania stopów wieloskładnikowych. Uzyskane rozwiązanie pozwala badać ewolucje rozkładów koncentracji składników w układach zamkniętych i otwartych dla dowolnych warunków początkowych i brzegowych. Wykazaliśmy przydatność prezentowanej metody w obliczaniu zmian koncentracji składników przy powierzchni stopIzgorzelina (które są efektem reakcji na powierzchni stopu). Wykonane symulacje dyfuzji wzajemnej w selektywnie utlenianym stopie (Fe-48 Cr) i selektywnie siarkowanym stopie trójskładnikowym (Fe-18Cr-9Ni w % wag.) wykazują zadowalającą ilościową zgodność z wynikami eksperymentalnymi.

EN

The Wagner model of oxidation of binary Ni-Pt type alloys and the Generalized Darken Method of Interdiffusion (GDM) are combined to describe the selective oxidation of multicomponent alloys. The solution of the GDM enables one to obtain an exact expression for the evolution of component distributions in closed and open systems, for arbitrary initial distributions and time dependent boundary conditions. We show the usefulness of the presented method in estimating the changes of density of elements at the alloyIscale interface (a result of reaction at the interface). The simulations of the interdiffusion in selectively oxidized binary (Fe-48Cr) and selectively sulphidized ternary (Fe-18Cr-9Ni in wt.%) alloys show the qualitative agreement with the experimental results.

9

Portevin-Le Chatelier effect in rolled Al-Li based alloys.

Mizera J., Kurzydłowski K.J.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 3

125-129

EN

Studies were carried out on the Portevin-Le Chatelier (PLC) effect in binary, ternary and quarternary Al-Li alloys and in the commercial 8090 alloy. The correlation between the serration characteristic, the rolling degree and the straining orientation has been analysed. The fact that the presence of the Cu-containing precipitates intensifies the PLC effects suggests, that these are primarily related to the interactions between the dislocations and the semi-coherent T1(Al2CuLi) precipitates. The analysis of the PLC effect in AlLi alloys shows that the serrations in the stress-strain curve exhibit a profund degree of anisotropy. Most pronounced PLC effects are observed along the rolling and transverse directions.

PL

Analizie poddano zjawisko Portevin-Le-Chatelier (PLC) w modelowych (dwu-, trój- i czteroskładnikowym) oraz przemysłowym (8090) stopie na osnowie Al-Li. Badano zależność pomiędzy charakterem oscylacji a stopniem zgniotu i anizotropią blach. Obecność w mikrostrukturze badanych stopów wydzieleń zawierających Cu wzmacniających zjawisko PLC sugeruje, że jest ono głównie związane z oddziaływaniem pomiędzy dyslokacjami a półkoherentnymi wydzieleniami T1(Al2CuLi). Analiza zjawiska PLC w stopach na osnowie Al-Li wykazała, że oscylacje na krzywej rozciągania charakteryzują się dużym stopniem niejednorodności. Najintensywniejsze efekty PLC zaobserwowano w próbkach wyciętych wzdłuż kierunku walcowania i kierunku poprzecznego blachy.

10

Mechaniczna synteza i prasowanie na gorąco stopów na osnowie gama-TiAl.

Dutkiewicz J., Maziarz W.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 1

32-37

PL

Stop podwójny na osnowie fazy gama-TiAl o składzie chemicznym Ti-48Al oraz potrójne Ti-48,4Al-4,1Mn i Ti45,4Al-10Mn (liczby przed symbolem pierwiastka oznaczają % at.) poddano mechanicznej syntezie (MS) w wysokoenergetycznym młynie planetarnym typu Fritsch Pulverisette P5/4. MS przez okres 40 godzin spowodowała rozdrobnienie wyjściowych cząstek proszków do wielkości średniej około 8 mm oraz ujednorodnienie ich kształtu. Mechanizm rozdrabniania wieloskładnikowych cząstek oparty był na pracy utwardzenia oraz pękaniu w miejscach wzbogaconych w tytan. Dodatek manganu tylko w pierwszych etapach procesu wpływał na strukturę cząstek, powiększając ich wielkość poprzez lokowanie się w plastycznej osnowie aluminiowej. Badania przy użyciu dyfrakcji promieni rentgenowskich wykazały, że we wszystkich stopach nastąpiło utworzenie struktury amorficznej oraz roztworu stałego typu alfa-Ti(Al) oraz obserwowano tylko częściową rozpuszczalność manganu. Stosując metodę dopasowania stwierdzono, że względny udział fazy amorficznej po 40 godzianch mielenia w stopie Ti48Al wynosił 70%, podczas gdy w stopach Ti-48,4Al-4,1Mn i Ti-45,4Al-10Mn odpowiednio 72 i 78%. Prasowanie na gorąco proszków po procesie MS w temperaturze 1000 stopni Celsjusza pod ciśnieniem 35 MPa prowadziło do uzyskania materiałów litych o gęstości od 95-98% gęstości teoretycznej. Mikrostruktura próbek składała się z trzech oddzielnych stref różniących się morfologią i składem chemicznym, spowodowane to było dyfuzją węgla od grafitowej matrycy do próbki i tworzeniu TiC na jej powierzchni zewnętrznej. Strefy różniły się również porowatością, która malała w kierunku osi próbki. Wyżarzanie w próżni sprasowanych oraz dodatkowo obrobionych mechanicznie w celu zlikwidowania budowy strefowej w temperaturze 1300 stopni Celsjusza (stop podwójny) oraz 1250 stopni Celsjusza (stopy potrójne) spowodowało powstawanie struktur wielofazowych o średniej wielkości ziaren około 10 mm. W stopie podwójnym Ti-48Al występuje płytkowa dwufazowa struktura alfa2+gama(Ti3Al+TiAl) oraz drobne wydzielenia roztworu stałego alfa-Ti(Al). W stopach z dodatkiem manganu również przeważającą jest faza gama-TiAl, a dodatkowo występowały fazy alfa2-Ti3Al, Ti9Al23 oraz faza typu Lavesa Al17Mn50Ti33.

EN

The binary and ternary gamma-TiAl phase based alloys i.e. Ti-48Al., Ti-48.4Al-4.1Mn and Ti-45.4Al-10Mn alloys (in at. %) were mechanically alloyed (MA) in high energetic mill Fritsch Pulverisette P5/4. After 40 hours of milling the refinement of initial powder particle down to 8 micrometres and change of to close to spherical shape was observed. The refinement mechanism of multicomponent particles is based on the work hardening and fracture in places locally enriched in titanium. The addition of manganese increases the mean particle size in the first period of milling, as compare to binary Ti-48Al powder due to location of manganese particle in ductile aluminium matrix. The X-ray diffraction of these alloys showed that 40 hours of MA produces a mixture of amorphous and crystalline a-Ti(Al) solid solution phases containing manganese. The profile fitting procedure for quantitative analyse of diffraction curves showed that a fraction of the amorphous phase in powders was 70% in Ti-48Al alloy, 72% in Ti-48.4Al-4.1Mn and 78% in Ti-45.4Al-10Mn after 40 hours of milling. Hot pressing consolidation of these powders at 1000 degrees centigrade under 35MPa caused their densification up to 95-98% of theoretical density. In hot pressed samples three zones of different structure and phase composition were observed, due to the effect of carbon diffusion from the mould, causing TiC formation in the outer zone. The zones differ also in amount of pores, which decrease toward the centre of sample. The vacuum annealing at 1300 degrees centigrade (binary alloy) and at 1250 degrees centigrade (ternary alloys) of hot pressed samples with removed surface zones caused formation of multiphase structures with average grain size of about 10 mm. The binary Ti-48Al was characterized by two phase layered alpha2+gamma(Ti3Al+TiAl) structure and fine precipitates of alpha-Ti(Al) solid solution. In ternary alloys gamma-TiAl phase exists as a matrix and additional alpha2-Ti3Al, Ti9Al23 and Al17Mn50Ti33 phases were observed.

11

High temperature Cu-based shape memory alloys

Lelątko J., Morawiec H.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 4

540-543

PL

Badano nowy rodzaj stopów, wykazujących pamięć kształtu w wysokich temperaturach, opracowanych na bazie trójskładnikowego stopu Cu-Al-Nb. Wprowadzenie do stopu trójskładnikowego chromu, a szczególnie niklu i kobaltu daje możliwość obniżenia zakresu temperaturowego odwracalnej przemiany martenzytycznej. Jednakże, pierwiastki te powodują wydzielanie w martenzytycznej osnowie faz międzymetalicznych takich jak AlCo i NiAl oraz zmiany w składzie chemicznym fazy Nb(Al,Cu)2 - głównej fazy występującej w stopie trójskładnikowym. Obecność tych cząstek wpływa na zmiany własności mechanicznych oraz zjawisko pamięci kształtu badanych stopów.

EN

New type of Cu-Al-Nb base alloys containing additionally nickel, cobalt and chromium and showing high martensitic transformation temperatures has been developed. In this paper the temperatures of reversible martensitic transformation, mechanical properties and shape memory characteristics of these alloys are presented. Introducing chromium and specially nickiel and cobalt to the Cu-Al-Nb alloys gives a possibility to decrease the characteristic temperatures. However, these elements create in the martensitic matrix primary particles of intermetallic phases such as AlCo and NiAl and change the chemical composition of the Nb(Al,Cu)2-the main phase in the ternary Cu-Al-Nb alloy. Presence of precipitates results in change of the mechanical properties of these alloys.

12

Structural investigations of Al-Fe-Ti alloys formed by mechanical alloying under various conditions.

Krasnowski M., Matyja H.

Inżynieria Materiałowa

|

1998

|

R. XIX, nr 4

1163-1166

EN

There is increasing interest in the synthesis of aluminium-based alloys by mechanical alloying (MA). These materials possess a high specific strength and in high temperature applications, exhibit attractive mechanical properties. The aim of this work was to study the structural and phase transformations that take place during mechanical alloying of the ternary Al50Fe25Ti25 alloy in a high energy planetary ball mill. Two experiments were performed: one with an addition of ethanol and the other without any additional agent. The nanocrystalline composite powder, consisting of titanium carbide distributed in the Fe(Al) matrix was the final product of the process performed with the addition of ethanol. After milling without any agent an amorphous phase was observed to form. When this phase was then subjected to heating in a calorimeter the ternary phase tau2(Al2FeTi) and Fe(Al, Ti) solid solution appeared.