Investigations of microstructure and phase transformations of Fe71.25Si9.5B14.25In5 alloy

Wojciechowska M., Ziewiec K., Ferenc J.

Metallurgy and Foundry Engineering

2017

Vol. 43, no. 1

67--72

The aim of this work was to study the microstructure and high-temperature phase transformations of the Fe71.25Si9.5B14.25In5 alloy. The alloy was remelted in a resistance furnace, and a sequence of melting and crystallization at a range of high temperatures was observed using a mid-wave infrared MWIR camera. The alloy was also investigated by differential thermal analysis (DTA). The microstructure of the alloy was studied using a scanning electron microscope SEM with an energy dispersive spectrometer (EDS). The results show that there is a clear partition into two liquids in the studied alloy. The ingot microstructure presents very strong segregation into the eutectic regions enriched in the Fe-Si-B and In-rich regions.

Celem pracy było zbadanie mikrostruktury oraz wysokotemperaturowych przemian fazowych zachodzących w stopie Fe71,25Si9,5B14,25In5. Proces przetapiania oraz krystalizacji stopu w piecu oporowym został zarejestrowany za pomocą kamery termowizyjnej pracującej w zakresie średniofalowej podczerwieni. Wykonano również różnicową analizę termiczną DTA badanego stopu. Mikrostrukturę zbadano przy użyciu skaningowego mikroskopu elektronowego SEM wyposażonego w spektrometr energii rozproszonej EDS. Wyniki wykazują, że w badanym stopie zachodzi wyraźny podział na dwie ciecze. Mikrostruktura wlewka zawiera składnik eutektyczny bogaty w Fe, Si i B oraz fazę wzbogaconą w In.

High-temperature corrosion resistance of steel-matrix composites

Sulima I., Homa M., Malczewski P.

Metallurgy and Foundry Engineering

2015

Vol. 41, no. 2

71--84

The results of corrosion studies of composite materials obtained by two methods of powder metallurgy are presented in the article. The main goal of the studies was to determine the high-temperature corrosion resistance of steel-matrix composites reinforced with 8 vol.% TiB2. Thermogravimetric analyses were conducted at 1100°C in air during a 24 h cycle. The microstructure of the composite after thermogravimetric studies was observed with a scanning electron microscope.

Praca prezentuje wyniki badań korozyjnych materiałów kompozytowych otrzymanych dwoma metodami metalurgii proszków (PM). Głównym celem pracy było określenie wysokotemperaturowej odporności korozyjnej kompozytów o osnowie stali austenitycznej umacnianych 8% obj. TiB2 . Przeprowadzono badania termograwimetryczne w temperaturze 1100°C w atmosferze powietrza w cyklu 24-godzinnym. Mikrostrukturę powierzchni kompozytów po badaniach termograwime- trycznych obserwowano przy użyciu skaningowej mikroskopii elektronowej