Influence of the Needle Depth and Frequency on the Thermal Insulation Performance of Pre-Oxidised Fibre Felts

Zhao Xiaoming, Liu Yuanjun, Liang Tenglong, Zheng Zhenrong

Fibres & Textiles in Eastern Europe

2020

Vol. 28, no. 4 (142)

57--66

In this paper, the influence of the needle depth and frequency on the thermal insulation performance of pre-oxidised fibre felts was mainly investigated. The results showed that pre-oxidised fibre felts of a needle depth of 8 mm at a room temperature and working temperature of 100-200 °C had the best thermal insulation performance, while fibre for those of different needle depths with increasing temperature, the steady-state temperature difference increased linearly. With an increasing needle frequency, the thickness and gram weight of the pre-oxidised fibre felts showed a decreasing trend, while the coefficient of thermal conductivity exhibited an increasing one. For pre-oxidised fibre felts of different needle frequencies with increasing temperature, the steady-state temperature difference showed a linearly increasing trend.

W pracy zbadano wpływ głębokości i częstotliwości igłowania na wydajność izolacji termicznej wstępnie utlenionych filców. Wyniki wykazały, że wstępnie utlenione filce igłowane na głębokość 8 mm w temperaturze pokojowej i temperaturze roboczej 100-200 °C miały najlepszą izolację termiczną. Wraz ze wzrostem częstotliwości igłowania grubość i gramatura wstępnie utlenionych filców wykazywały tendencję spadkową, podczas gdy współczynnik przewodności cieplnej wzrastał. W przypadku wstępnie utlenionych filców różnych częstotliwościach igłowania ze wzrostem temperatury różnica temperatur w stanie ustalonym wykazywała liniowo rosnący trend.

Influence of the Needle Number on the Heat Insulation Performance of Pre-oxidized Fibre Felts

Zhao X., Liu Y., Liang T.

Fibres & Textiles in Eastern Europe

2018

Vol. 26, no. 3 (129)

80--86

Many factors were needed to be considered to prepare pre-oxidised fibre felts with excellent heat insulation performance, and different production processes showed differences in the heat insulation performance of pre-oxidised fibre felts. In order to probe into the influence of the production process on the heat insulation performance of materials, a large number of experiments were needed to be carried out. For needle-punched nonwoven pre-oxidised fibre felts, web features, needle characteristics and the needle process will all affect the structure of pre-oxidised fibre felts, thus bringing a major influence on the heat insulation performance of pre-oxidised fibre felts. In this paper, the influence of the needle number on the heat insulation performance of pre-oxidised fibre felts was mainly studied. Results showed that an increase in the needle number will cause a decrease in the thickness and gram weight of pre-oxidised fibre felts, and a weakening trend in the heat insulation performance of pre-oxidiaed fibre felts with an increasing needle number at room temperature and at 100-200 °C was shown. Moreover when the needle number was 1 and 2, the pre-oxidised fibre needled felts had good heat insulation performance, and for pre-oxidized fibre felts at different needle numbers with increasing temperature, the temperature difference in a steady state increased linearly.

Aby przygotować filce z włóknami preoksydowanymi o doskonałymi właściwościami izolacyjnymi, należy wziąć pod uwagę wiele czynników, a różne procesy produkcyjne wykazały różnice w wydajności izolacji cieplnej filców włóknistych. Aby zbadać wpływ procesu produkcyjnego na parametry izolacji termicznej materiałów, konieczne było przeprowadzenie wielu eksperymentów. W pracy badano głównie wpływ liczby igieł na izolacyjność cieplną wstępnie utlenionych filców włóknistych. Wyniki pokazały, że zwiększenie liczby igieł spowodowało zmniejszenie grubości i gramatury filców włóknistych oraz osłabienie tendencji w zakresie izolacji cieplnej filców z włóknami preoksydowanymi wraz ze wzrastającą liczbą igieł w temperaturze pokojowej i w 100-200 °C. Ponadto, gdy liczba igieł wynosiła 1 i 2, pre-utlenione włókniny igłowane miały dobrą izolację cieplną, a dla wstępnie utlenionych filców włóknistych przy różnych numerach igieł ze wzrastającą temperaturą, różnica temperatur w stanie ustalonym wzrastała liniowo.