The crystallographic texture formation in low carbon steel during asymmetric rolling was studied experimentally and analysed numerically. Modelling of plastic deformation was done in two scales: in the macro-scale using the finite element method ( FEM) and in crystallographic scale using the polycrystalline deformation model (LW model). The stress distribution in the rolling gap was calculated using FEM and next these stresses were applied in LW model of polycrystalline plastic deformation. It was found that the textures of central and surface layers of the sample are related by a rotation around the transverse direction; moreover, this rotation angle varies with the distance of the considered material layer from the sample surface. In general, the predicted textures agree very well with those determined by X-ray diffraction. Besides of texture change (departure from orthorhombic sample symmetry), the asymmetrical rolling modifies also the material microstructure.
PL
Zbadano doświadczalnie i numerycznie tworzenie się tekstur walcowania asymetrycznego w stali niskowęglowej. Modelowanie odkształcenia plastycznego przeprowadzono w dwóch skalach: w skali makro przy użyciu metody elementów skończonych (MES) i w skali krystalograficznej używajac modelu odkształcenia polikryształu (model LW). Rozkład naprężeń w kotlinie walcowniczej wyznaczony metodą elementów skończonych był następnie użyty w modelu odkształcenia LW. Stwierdzono, że tekstury warstwy powierzchniowej i środkowej związane są obrotem wokół kierunku poprzecznego, przy czym kąt obrotu zależy od odległości rozważanej warstwy materiału od powierzchni próbki. Ogólnie, tekstury przewidywane przez użyte modele pozostają w dobrej zgodności z teksturami zmierzonymi. Oprócz zmiany tekstury (odejście od rombowej symetrii próbki), walcowanie asymetryczne modyfikuje także mikrostrukturę materiału.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The present research concerns the rolling texture formation in the X2CrNiMoN22-6-3 steel, which chemical composition corresponds to the commercial mid-alloy duplex steel grade SAF 2205. The applied thermo-mechanical treatment included hot-rolling and subsequent solution annealing at the temperature 1150°C. After the preliminary treatment the two-phase structure consisted of about 40% of austenite volume fraction within the ferrite matrix. Subsequently the steel was cold-rolled within the range up to 85% of reduction, perpendicularly to the direction of hot-deformation. Analysis of the rolling texture formation in both constituent phases indicates that the examined steel shows tendency to develop the textures close to those in single phase steels. In both phases however the process proceeds in different way and the final textures display certain important differences in comparison to the typical ferrite and austenite textures. In the case of ferrite the major component of the initial texture remains stable up to high deformations and the final texture essentially does not exhibit the fibrous character. On the other hand a gradual formation of the texture close to an alloy-type texture is observed in austenite and the orientation changes proceed over a wide deformation range. It is concluded that the band-like morphology of the ferrite-austenite structure and the initial orientations resulting from the change of rolling direction strongly influence the formation of the final rolling textures.
PL
Prezentowane badania dotyczą rozwoju tekstury walcowania w stali X2CrNiMoN22-6-3, której skład chemiczny odpowiada średnio-stopowej stali duplex w gatunku SAF 2205. Zastosowana obróbka cieplno-mechaniczna obejmowała walcowanie na gorąco oraz przesycanie z temperatury 1150°C. Po obróbce wstępnej struktura dwufazowa składała się z okolo 40% austenitu w osnowie ferrytu. Następnie stal poddano walcowaniu na zimno w zakresie do 85% defonnacji, prostopadle do kierunku odkształcenia na gorąco. Analiza tworzenia się tekstur walcowania w obu składowych fazach wskazuje, że badana stal wykazuje tendencje do rozwoju tekstur zbliżonych do tych w stalach jednofazowych. Jednak w obu fazach proces ten zachodzi w odmienny sposób a koncowe tekstury wykazują pewne istotne różnice w porównaniu do typowych tekstur ferrytu i austenitu. W przypadku ferrytu, główna składowa tekstury początkowej pozostaje stabilna do wysokich odkształceń a tekstura końcowa zasadniczo nie wykazuje charakteru włóknistego. Z kolei w austenicie obserwuje się stopniowy rozwój tekstury zbliżonej do tekstury typu stopu a zmiany orientacji zachodzą w szerokim zakresie odkształceń. Stwierdzono, że pasmowa morfologia ferrytu i austenitu oraz orientacje początkowe wynikające ze zmiany kierunku walcowania wywierają istotny wpływ na tworzenie się końcowych tekstur odkształcenia.
3
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
In the present work the effect of the initial orientation distribution on texture development is analysed in two duplex type steels, X1CrNi24-6 and X4CrNiMo24-6-2, subjected to cold-rolling. Both steels under examination showed very different intensities of the initial textures after the preliminary thermo-mechanical treatment, namely; clearly defined strong textures of ferrite and austenite in steel X1CrNi24-6 and nearly random textures of both constituent phases in the case of steel X4CrNiMo24-6-2. Comparison of texture formation indicates that essentially both duplex steels show tendency to develop the rolling textures of the constituent phases close to those in single phase steels. In both cases however the process proceeds in different way and the final textures display certain important differences in comparison to the typical ferrite and austenite textures. In the case of the steel with strong initial orientations the formation of the rolling textures consists in spread of the starting textures however the major orientation components in both phases are stable up to high rolling reductions. On the other hand in the steel with random initial orientations a gradual formation of deformation textures is observed in the course of rolling with simultaneous formation of ferrite and austenite bands. It is concluded that in both cases the formation and character of the final deformation textures is strongly influenced by the band-like morphology of two-phase structure.
PL
Prezentowana praca dotyczy analizy wpływu orientacji wyjściowej na rozwój tekstur odkształcenia w dwóch stalach typu duplex, X1CrNi24-6 oraz X4CrNiMo24-6-2, poddanych walcowaniu na zimno. Obie badane stale wykazywały bardzo zróżnicowane intensywności tekstury wyjściowej po wstępnej obróbce cieplno-mechanicznej, tzn. wyraźnie określone silne tekstury ferrytu i austenitu w stali X1CrNi24-6 oraz niemal bezładne tekstury obu składowych faz w przypadku stali X4CrNiMo24-6-2. Porównanie tworzenia się tekstur wskazuje, ze zasadniczo obie stale duplex wykazują tendencję do rozwoju tekstur walcowania obu składowych faz zbliżonych do tych w stalach jednofazowych. Jednak w obydwu przypadkach proces ten zachodzi w odmienny sposób a końcowe tekstury wykazują pewne istotne różnice w porównaniu do typowych tekstur ferrytu i austenitu. W przypadku stali o silnej orientacji wyjściowej tworzenie się tekstur walcowania polega na stopniowym rozmyciu tekstur początkowych, niemniej główne orientacje składowe w obu fazach pozostają stabilne do wysokich odkształceń. Z kolei w stali o bezładnej orientacji wyjściowej w trakcie walcowania obserwuje się stopniowy rozwój tekstur odkształcenia równolegle z tworzeniem pasm ferrytu i austenitu. Stwierdzono, że w obu przypadkach pasmowa morfologia struktury dwufazowej wywiera istotny wpływ na tworzenie się i charakter końcowych tekstur odkształcenia.
4
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The present examination concerns a development of deformation textures in stainless steel of duplex type with strong initial texture. The ferritic-austenitic steel was subjected to cold-rolling within the range up to 90% of reduction. Different rolling conditions were applied employing three variants of rolling reductions per pass. The investigations included texture measurements, X-ray phase analysis and microstructure observations by means of optical microscopy. The occurrence of strong initial textures of both component phases was found after the preliminary thermo-mechanical treatment. Ferrite exhibited the {100}<001> cubic texture and the dominant component of the austenite texture was the {110}< 001> Goss orientation. The crystallographic relation between the major texture components of both phases was described by Bain orientation relationship. The experimental results indicate that formation of the ferrite-austenite banded structure in the course of cold-rolling along with the plastically compatible deformation of both phases result in the stability of major texture components up to high reductions and exert significant effect on the final rolling textures of ferrite and austenite.
PL
Przedstawione badania dotyczą rozwoju tekstur odkształcenia w stali nierdzewnej typu duplex o silnej teksturze wyjściowej. Stal ferrytyczno-austenityczną poddano walcowaniu na zimno zakresie do 90% deformacji. Zastosowano różne warunki walcowania wykorzystując trzy warianty odkształceń częściowych. Przeprowadzone badania obejmowały pomiary tekstur, rentgenowską analizę fazową oraz obserwacje mikrostruktury za pomocą mikroskopii świetlnej. Po wstępnej obróbce cieplno-mechanicznej stwierdzono występowanie silnej wyjściowej tekstury obu składowych faz. Ferryt wykazywał teksturę sześcienną {100}< 001> a w teksturze austenitu dominującą składową stanowiła orientacja Gossa {110}<001>. Relacje krystalograficzną pomiędzy głównymi składowymi wyjściowej tekstury obu faz opisywała zależność Baina. Uzyskane wyniki wskazują, że tworzenie się pasmowej struktury ferrytu i austenitu w trakcie walcowania na zimno przy równoczesnym plastycznie zgodnym odkształceniu obu faz prowadzi do stabilności głównych składowych tekstury do wysokich stopni odkształcenia wywiera istotny wpływ na końcowe tekstury walcowania ferrytu i austenitu.
The formation of texture and microstructure in polycrystalline Cu and Cu-5 wt.%Al alloy during two modes of homogenous rolling have been compared. two samples of each metal were rolled. one sample was rolled unidirectionally, while the other by reverse rolling. Some differences in the textures depending on the rolling mode have been observed in the range of deformation of the Cu-5 wt.%Al alloy where intensive twinning took place. It was also found that the texture of reverse rolling was more homogeneous across the thickness of the rolled alloy sheet than the texture of unidirectionally rolled material. no clear effect of the rolling mode on microstructure has been observed.
PL
W pracy porównano tekstury dwóch sposobów walcowania polikrystalicznych metali: miedzi i stopu Cu-5%Al. Dla kazdego z metali jednorodnie przewalcowano po dwie próbki.Dla jednej z nich, kierunek walcowania był taki sam w każdym przepuście (walcowanie jednokierunkowe). Dla drugiej próbki po każdym przepuście kierunek walcowania zmieniano na kierunek przeciwny (walcowanie rewersyjne). Sposób walcowania wplywał na teksturę jedynie w przypadku stopu Cu-5%Al, w tym zakresie odkształceń, w którym zachodziło intensywne bliźniakowanie. Dla stopu, stwierdzono większą jednorodność rozkładu tekstury na grubość płaskowników przewalcowanych rewersyjnie niż w przypadku płaskowników przewalcowanych jednokierunkowo. Nie obserwowano wyraźnego wpływu sposobu walcowania na mikrostrukturę.
The object of investigations was two-phase steel having the austenitic structure with ferrite precipitates (volume fraction about 10%). The material was subjected to cold rolling up to about 85% of deformation and subsequently annealed within the temperature range 750C+1000C. X-ray investigations included the phase analysis, measurements of pole figures and calculations of the orientation distribution functions (ODF's) for both component phases. The textures of austenite and ferrite after the final rolling reduction and succesive stages of annealing were analysed within the centre and surface layers of the sheets. Examination of the austenite recrystalization texture included additionally the analysis of orientation fibres and transformations of the experimental and ideal ODF's. From the texture analysis it results that mechanisms controlling the development of the austenite recrystallization texture is the selective growth of twins. texture simulations indicate that austenite rolling texture can be transformed into the recrystallization texture according to twin relation, i.e. by rotation through an angle (2n-1_x60 gr. about <111> poles. a certaincontribution of the oriented growth into the texture formation was also found. In that case relation between the recrystallization and deformation textures may be described by rotation 30-40gr./<111>. In both cases a variant selection of the rotation axis takes place. Based on the texture examination and the phase analysis it is additionally assumed that the phase transformation may exert some effect on the recrystallization textures of both componentp hases.
PL
Przedmiot badań stanowiła stal dwufazowa o strukturze austenitycznej z wydzieleniami ferrytu (udział objętościowy ok. 10%). Material poddano walcowaniu na zimno do ok. 85% odkształcenia a następnie wyżarzano w zakresie temperatur 750-1000C. Badania rentgenowskie obejmowały analizę fazową, pomiary figur biegunowych oraz obliczenia funkcji rozkładu orientacji (FRO) dla obu składowych faz. Tekstury austenitu i ferrytu, po końcowym stopniu odkształcenia oraz kolejnych etapach wyżarzania, analizowano w warstwach środkowej i powierzchniowej blach. Badania tekstury rekrystalizacji austenitu obejmowały dodatkowo analizę włókien orientacji oraz transformacje eksperymentalnych oraz idealnych FRO. Z analizy tekstury wynika, że mechanizmem kontrolujacym rozwój tekstury rekrystalizacji austenitu jest selektywny wzrost bliźniaków. Symulacje tekstury wskazują, że teksturę walcowania austenitu można przekształcić w teksturę rekrystalizacji zgodnie z relacją bliźniaczą, tj. poprzez rotacje o kat (2n-1)x60 st. wokół biegunów <111>. Stwierdzono również pewien udział mechanizmu zorientowanego wzrostu w tworzeniu tekstury rekrystalizacji. w tym przypadku relacje pomiedzy teksturami rekrystalizacji i odksztalcenia można opisać rotacją 30st-40st./<111>. W obu przypadkach ma miejsce selektywny wybór osi obrotu. W oparciu o badania tekstury oraz analizę fazową zakłada się ponadto, że pewien wpływ na tekstury rekrystalizacji obu skladowych faz może wywierać przemiana fazowa.
A development of deformation textures was investigated in two-phase steel containing about 10% of ferrite volume fraction. The steel of this type was subjected to cold-rolling within the range up to 90% of deformation by applying high and low reductions per pass. Results of X-ray measurements indicate at different mechanisms of the rolling texture formation depending on the applied mode of deformation. From the X-ray phase analysis and the examination of the orientation distribution functions it follows that deformation induced (gamma->alpha) phase transformation exerts significant effect on the texture development of both phases when small reductions per pass are employed.
PL
Badania dotyczyły rozwoju tekstur odkształcenia w stali dwufazowej zawierającej około 10% objętościowych ferrytu. Stal tego typu poddano walcowaniu na zimno w zakresie do 90% deformacji przy zastosowaniu dużych i małych odkształceń częściowych. Rezultaty badań rentgenowskich wskazują na różne mechanizmy tworzenia tekstur walcowania zależnie od zastosowanego sposobu odkształcenia. W oparciu o wyniki analizy fazowej oraz analizę funkcji rozkładu orientacji widocznym jest, że indukowana odkształceniem przemiana fazowa (gamma->alfa) wywiera istotny wpływ na rozwój tekstury walcowania obu faz przy zastosowaniu małych odkształceń jednostkowych.