1

Combined effects of copper and oil treatment on the properties of Scots pine wood

Can A., Sivrikaya H.

Drewno : prace naukowe, doniesienia, komunikaty

|

2017

|

vol. 60, nr 199

89--103

EN

Due to its toxic effect on fungi, for the last 50 years copper has been one of the most widely used materials in the impregnation industry. The ban on CCA (copper-chrome-arsenic), known as an effective deterrent against fungi and insects, has led to the development of new and environmentally-friendly alternatives. Copper-azole (CuA), which is one of the most widely used of the newly-developed materials, is very effective against fungi and insects. However, one of its most serious problems is the fact that copper is leached from the wood. Various factors affect the leaching of copper from wood. One of the most important effects is the duration of fixation. In this study, samples impregnated with copper azole were exposed to a secondary impregnation process using tall oil and linseed oil 24 hours and 5 days, respectively, after the first impregnation. The effects of different fixation durations and oiled impregnation procedures on Scotch pine were investigated. For this purpose, biological, physical and chemical analyses of the wood were performed. Moreover, the amount of copper residual after leaching was also examined. According to the results obtained, it was observed that the duration of fixation had no significant effect on the physical properties, and that the linseed oil improved the physical properties of the wood. Through the copper and oil combination, an improvement in the physical and biological properties of the wood was observed, as well as a decrease in the amount of copper leached out.

2

Wheat straw lignin as filler for rigid polyurethane foams on the basis of tall oil amide

Paberza A., Cabulis U., Arshanitsa A.

Polimery

|

2014

|

T. 59, nr 6

477--481

EN

Rigid polyurethane (PUR) foams with the apparent density in the range of 45—60 kg/m 3 were produced from tall oil polyol (TOP) and organosolv wheat straw lignin as filler. PUR foams were filled with lignin in the amount of 0—6.3 wt %. Mechanical properties, dimensional stability, water absorption and thermal conductivity of prepared foams were investigated. The use of lignin increased the content of renewable materials in the end product, reaching together with TOP the value of 23.6 wt %. The viscosity of polyol system and foaming process parameters (cream time, gel time, tack-free time and full rise time) were determined. The viscosity of polyol system rose exponentially when concentration of lignin in the PUR foam was increased. The maximum value of compressive strength (0.35 MPa parallel to the foaming direction) was reached in the PUR sample where the concentration of lignin in foam was 1.2 wt %. It was concluded that wheat straw lignin can be used as a filler to obtain rigid PUR foams having the characteristics of thermal insulation material.

PL

Stosując poliol z oleju talowego (TOP) oraz ligninę ze słomy pszenicznej jako napełniacz otrzymano sztywne pianki poliuretanowe (PUR) o gęstości pozornej 45—60 kg/msub>3. Wyznaczono właściwości mechaniczne, stabilność wymiarową, chłonność wody oraz współczynnik przewodzenia ciepła przygotowanych materiałów w zależności od zawartości ligniny (0—6,3 % mas.). Wprowadzenie ligniny spowodowało zwiększenie udziału surowców odnawialnych w końcowym produkcie, które razem z TOP osiągają 23,6 % mas. W ramach pracy wyznaczono lepkość przedmieszki poliolowej oraz parametry technologiczne procesu spieniania (czas startu, czas żelowania, czas wzrostu, oraz czas suchego lica). Lepkość przedmieszki poliolowej wzrastała wykładniczo wraz ze zwiększaniem zawartości ligniny. Największą wytrzymałość na ściskanie (0,35 MPa w kierunku równoległym do wzrostu pianki) otrzymano w przypadku pianki PUR o zawartości ligniny 1,2 % mas. Stwierdzono, że lignina ze słomy pszenicznej może być użyta jako napełniacz w procesie otrzymywania sztywnych pianek PUR mających cechy materiałów termoizolacyjnych.

3

Zastosowanie oleju talowego w przemyśle chemicznym

Formela K., Haponiuk J. T.

Przemysł Chemiczny

|

2012

|

T. 91, nr 6

1160-1163

PL

Olej talowy, produkt uboczny z procesu wytwarzania celulozy, stanowi źródło cennych surowców. Kwasy żywiczne i tłuszczowe otrzymane w wyniku destylacji frakcyjnej oleju talowego stosowane są obecnie w wielu gałęziach przemysłu. Na znaczeniu zyskuje również pozostałość podestylacyjna oleju talowego, zawierająca korzystne dla ludzkiego organizmu fitosterole. Dokonano przeglądu literatury naukowej oraz patentowej na temat zastosowania oleju talowego i jego pochodnych w przemyśle chemicznym.

EN

A review, with 53 refs., of tall oil uses in prodn. of plastics, coatings, biofuel and diet supplements.