The slip-twin transformation in low stacking fault energy face-centred cubic single crystals.

Szczerba M.S., Ryś J.

Inżynieria Materiałowa

2001

R. XXII, nr 5

888-891

A change of dominant deformation system and its relation to strain hardening behaviour was examined in low stacking fault energy (SFE) face centred cubic (FCC) single crystals. Highly concentrated copper based Cu-Al alloy crystals were deformed at room temperature by tension and rolling. The main attention was focused on slip-twin transformation, where the dominant slip system is replaced by a new twin system. It was found that irrespective of the deformation process the onset of the deformation twinning follows the same rules and corresponds to the end of overshoot phenomena. Appreciable changes of crystal orientation and hence a significant redistribution of sufficiently high shear stresses operating in crystal lattice result in the activation of a new twin system. Structural and orientation changes as well as the mechanical properties examined in the deformed crystals suggest that FCC twin transformation may strongly control material properties at large plastic strains.

W pracy analizowano zmianę dominującego systemu deformacji i jej wpływ na własności mechaniczne w monokryształach Cu-Al o sieci regularnie ściennie centrowanej i niskiej enrgii błędu ułożenia. Jednofazowe stopy na bazie miedzi o wysokiej koncentracji Al zostały odkształcone w temperaturze otoczenia na drodze walcowania i rozciągania. Główną uwagę skupiono na transformacji poślizg-bliźniakowanie, gdzie dominujący system poślizgu zostaje zastąpiony przez nowy system bliźniakowania. Stwierdzono, że w obydwu procesach deformacji początek mechanicznego bliźniakowania można przewidzieć w oparciu o te same prawa i należy on do klasy zjawisk tzw. końca "overshootu". Znaczne zmiany orientacji kryształu a stąd istotna redystrybucja operujących w sieci kryształu wysokich naprężeń ścinających determinują aktywację nowego systemu bliźniakowania. Zmiany strukturalne i orientacji kryształu jak również przebieg zmian własności mechanicznych sugerują, że transformacja bliźniacza może w sposób istotny kontrolować właściwości materiału przy dużych deformacjach plastycznych.

Transformations of dominant deformation systems in copper single crystals

Szczerba M. S.

Archives of Metallurgy

2001

Vol. 46, iss. 1

53-64

A close relation between the origin of tensile instability and the onset of deformation stage IV of copper single crystals was found. The tensile instability in single glide oriented copper single crystals belongs to the end of the overshoot phenomena resulting from a change of dominant deformation system - the changeover from primary to conjugate slip dominance. The identical transformation in deformation mechanism was found to be responsible for the onset of stage IV of plastic deformation of copper single crystals tested in rolling. Structural and mechanical observations and 4.2 K electrical resistivity measurements performed on the deformed crystals show, that the change in deformation mechanism causes a significant decrease in the rate of work hardening, a sudden change in the rate of dislocation accumulation, and the redistribution of dislocation arrangements in crystal lattice. It is concluded that the transformation of dominant deformation systems may strongly control deformation properties of face centered cubic crystals at large plastic strains. Finally the low temperature slip-twin transformation is discussed in terms of the change of a dominant deformation system.

W pracy na przykładzie walcowanych i rozciąganych monokryształów miedzi wykazano, że początek IV-tego stadium deformacji oraz początek nicstatcczności rozciągania są zjawiskami fizycznie równoważnymi. W monokryształach miedzi o orientacji środka trójkąta podstawowego, niestateczność rozciągania należy do zjawisk kończących tzw. „overshoot” i wynika ze zmiany dominującego systemu deformacji – zamiana dominującego poślizgu pierwotnego na sprzężony. Identyczna transformacja w mechanizmie deformacji została znaleziona w walcowanych monokryształach miedzi. Przeprowadzone badania mechaniczne i strukturalne oraz pomiary oporności elektrycznej w temperaturze ciekłego helu pokazują, że transformacji dominującego systemu poślizgu towarzyszy znaczny spadek prędkości umocnienia, zmiana prędkości akumulacji dyslokacji oraz zmiana konfiguracji układów dyslokacji deformowanego kryształu. W pracy stwierdzono, że transformacja dominującego systemu poślizgu może istotnie kontrolować właściwości plastyczne kryształów regularnie ściennie centrowanych w obszarach dużych odkształceń plastycznych. W pracy podjęto również dyskusję nad niskotemperaturową transformacją typu poślizg-bliźniakowanie.