The impact of magnetron source power on mechanical properties and phase composition of TiB2 coatings

Rydzewski M., Kacprzyńska-Gołacka J., Słomka Z., Mazurkiewicz A., Smolik J.

Problemy Eksploatacji

2016

no. 4

53--61

PVD coatings are widely used in the tool industry. They use hard materials, such as carbides, borides, and nitrides of metallic elements, because these materials have good wear resistance and stability at elevated temperatures. Titanium diboride-TiB2 is a very interesting compound used for coatings in the tool industry. The results of the analysis of research directions in the field of coatings and layers with special operating properties (high hardness, good thermal and electrical conductivity, and good corrosion resistance) indicate that coatings and layers based on TiB2 are one of the most effective materials that improve tool durability. The paper presents the mechanical properties of TiB2 coatings obtained using the magnetron sputtering method in the function of sputtering process power of TiB2 target. The paper includes hardness and Young' s modulus measurements performed with nanoindentation method, and phase composition analysis, and the evaluation of the microstructure and topography using a Hitachi TM3000 scanning electron microscope.

Powłoki PVD znajdują powszechne zastosowanie w przemyśle narzędziowym. Do ich wytwarzania stosuje się twarde związki takie jak: węgliki, borki, azotki metali, które charakteryzują się dobrą odpornością tribologiczną oraz stabilnością w podwyższonej temperaturze. Dwuborek tytanu - TiB2 jest bardzo interesującym materiałem powłokowym, cieszącym się dużym zainteresowaniem w przemyśle narzędziowym. Analiza literatury w zakresie powłok funkcjonalnych (powłok o dużej twardości, dobrym przewodnictwie cieplnym i elektrycznym, dobrej odporności korozyjnej) wskazuje TiB2 jako jeden z najbardziej efektywnych materiałów zwiększających trwałość narzędzi przeznaczonych do obróbki powierzchniowej stopów metali nieżelaznych. W artykule przedstawiono właściwości mechaniczne powłok TiB2 otrzymanych z wykorzystaniem metody rozpylania magnetronowego w funkcji mocy rozpylania targetu TiB2. Artykuł zawiera pomiary twardości oraz modułu Younga, analizę struktury fazowej, badania mikrostruktury oraz badania odporności na pękanie cienkich powłok.

Protective coatings based on Zr-Ti-Si-N their physical and mechanical properties and phase composition

Kirik G., Kozak C., Opielak M.

Przegląd Elektrotechniczny

2012

R. 88, nr 10a

319-321

Hard and super hard coatings of Zr-Ti-Si-N of from 2.8 to 3.5 um thickness were fabricated using vacuum arc source with (HF) stimulation. Six series of samples with various Zr and Ti content were studied. The samples were annealed in vacuum and in air at 1200oC. It was found that films with a high Zr and Ti content were thermally stable up to 1180 C. At the same time, a thin oxide layer of 180 to 240nm was found in the surfaces, which protected the sample from destruction. A size of grains of a substitution solid solution (Zr, Ti)N varied from (10 – 12)nm to 25nm, but Ti concentration in the solid solution increased. In the process of annealing, hardness of the best series of samples increased from 39.6 š 1.4GPa to 53.6GPa, which seemed to indicate that a spinodal segregation along grain interfaces was finished. Tribotechnical characteristics of coatings were measured for various contents of basic elements Zr, Ti, and Si. The work was funded by the project of NAS of Ukraine “Nanomaterials, Nanotechnologies, Nanosystems”.

Twarde i supertwarde powłoki Zr-Ti-Si-N o grubości od 2,8 do 3,5 um zostały wytworzone wykorzystując próżniowe źrodło łuku ze stymulacj. HF. Przebadano sześć serii próbek o rożnej zawartości Zr oraz Ti. Próbki zostały wygrzane w prożni i w powietrzu w temperaturze 1200 C. Wykazano, że warstwy z wysoką zawartości. Zr oraz Ti były stabilne termicznie do temperatury 1180 C. W tym samym czasie cienka warstwa tlenku o grubości od 180 do 240nm została zidentyfikowana w obrębie powierzchni, które ochraniały próbkę przed zniszczeniem. Rozmiar ziaren substytutu roztworu stałego (Zr, Ti)N zmieniał się od (10 . 12)nm do 25nm, jednakże koncentracja Ti w roztworze stałym wzrastała. W procesie wygrzewania twardość najlepszej serii próbek wzrosła od 39,6 +- 1,4GPa do 53,6GPa, co wydaje się wskazywać, że oddzielanie spinodalne wzdłuż interfejsu ziaren zostało zakończone. Charakterystyki trybo techniczne powłok zostały zmierzone dla różnych zawartości podstawowych pierwiastków Zr, Ti, oraz Si. Badania zostały sfinansowane ze środków ukraińskiego projektu NAS "Nanomateriały, Nanotechnologie, Nanosystemy". (Powłoki ochronne wytworzone w oparciu o Zr-Ti-Si-N . właściwości mechaniczne i skład fazowy).