Dual-phase technology and properties of C-Mn steels

Lis J., Lis A., Kolan C.

Inżynieria Materiałowa

2004

R. XXV, nr 3

163-165

Structural steels grade 18 and 15V were processed to achieve dual-phase (DP) ferrite-martensite (FM) and ferrite-bainite/martensite (F-BM) microstructures or multi-phase structures (MP) via intercritical annealing and quenching in water. The CCT diagrams for 18 and 15V steels cooled from (alpha+gamma) region have been presented (Fig. 1). Microstructure observation by optical and transmission electron microscopy and X-ray diffraction revealed existence of retained austenite in DP and MP structures of 15V steel (Fig. 2-Fig. 6 and Table 1). High tensile strength properties and ductility of intercritical annealed 1063K/1800s or 1063K/3600s and quenched in water were achieved. The very good toughness at low temperature after additional tempering at 913K/3600s was determined for 16mm plates made of 15V steel (Table 2) with microstructure shown in Fig. 7.

Konstrukcyjne stale 18 i 15V wygrzewano międzykrytycznie i hartowano w wodzie w celu wytworzenia dwoistofazowej (DP) ferrytyczno-martenzytycznej (FM) i ferrytyczno-bainityczno /martenzytycznej (F-BM) mikrostruktury, bądź wielofazowej struktury (MP). Zaprezentowano wykresy CTPc stali 18 i 15V chłodzonych z zakresu (alfa+gamma) (Rys1). Poczyniono obserwacje mikrostrukturalne metodą optycznej i transmisyjnej mikroskopii elektronowej oraz metodą dyfrakcji rentgenowskiej ujawniono obecność austenitu szczątkowego w strukturach DP i MP stali 15V (Rys. 2 + Rys. 6 i Tab. 1). Uzyskano wysoką wytrzymałość i plastyczność chłodzonych w wodzie po wygrzewaniu międzykrytycznym 1063K/1800s lub 1063K/3600s blach 16mm ze stali 15V. Bardzo dużą ciągliwość w niskich temperaturach po dodatkowym odpuszczaniu blach w 913K/3600s przedstawiono w Tab. 2 a ich strukturę na Rys. 7.

Phase transformations in ULCB_Mn steel cooled from (alpha+gamma) range.

Kolan C., Lis A. K.

Inżynieria Materiałowa

2001

R. XXII, nr 4

458-461

The aim of the investigation was to establish the conditions for dual-phase microstructure formation which consists of bainite-martensite (BM) islands in ferrite matrix of ultra low carbon bainitic steel (ULCB_Mn) bearing about 3.7% Mn. The kinetic of austenite formation during the heating up at rate V5-8=0.6K/s process was determined to establish the temperature of intercritical annealing for a predetermined austenite content. The phase transformations of newly formed austenite within (alpha+beta) range during continuous cooling at a rate V8-5=0.6/30 K/s were studied. The intercritical annealing simulations were conducted for the commercially produced cold-rolled material. The influence of annealing temperature at (alpha+gamma) range and the volume fraction of BM islands formed during cooling down on the mechanical properties of sheets of 04G4Ti steel was established.

Celem badań było ustalenie warunków tworzenia się dwoistofazowej struktury złożonej z wysp bainityczno-martenzytycznych (BM) w osnowie ferrytycznej stali ULCB_Mn zawierającej około 3.7% Mn. Dla określenia temperatury międzykrytycznego wyżarzania oraz ilości nowopowstałego austenitu wyznaczono kinetykę przemiany alfa->gama dla V5-8=0.6K/s. Badano przemiany fazowe nowoutworzonego austenitu w zakresie (alfa+gama) dla warunków ciągłego chłodzenia w zakresie szybkości V8-5=0.6/30 K/s. Przeprowadzono symulację międzykrytycznego wyżarzania taśm zimnowalcowanych produkowanych przemysłowo. Określono wpływ temperatur wyżarzania w zakresie dwufazowym (alfa+beta) i różnej ilości wysp BM powstałych przy chłodzeniu na własności mechaniczne taśm ze stali 04G4Ti.