Numerical model of heterogeneity of the ductile cast-iron

Stransky K., Kavicka F., Dobrovska J., Stetina J., Sekanina B.

Prace Instytutu Metalurgii Żelaza

2009

T. 61, nr 5

137-141

An original three-dimensional (3D) model of solidification is used to describe the process of solidification and cooling of massive 500×1000×500 mm cast-iron castings. The castings are cast in sand moulds. The calculated mode of the kinetics of the temperature field of the casting is verified during casting with temperature measurements in selected points. The sizes and positions (xi, yi, zi, where i = 1,2,3 is the number of samples taken) of the experimental samples are exactly defined and corresponding with the decreasing rate of solidification. The experimental samples – 15 mm in diameter and 12 mm high – are metallographically analysed and also in terms of heterogeneity of the chemical composition. The coordinates xi, yi, zi characterise approximately – within an accuracy of +/- 5 mm – the centres of the samples. Successively, the local solidification time (i.e. the time the specified position of the casting, defined by the coordinates xi, yi, zi, remains within the temperature range between the liquidus and solidus) is also calculated using the 3D model. The following dependences are later determined according to the experimental and calculated data: the average size of the graphite spheroids rg, graphite cells Rb and the average distances among the particles of graphite Lg – always as a function of the local solidification time [xi, yi, zi]. Furthermore, it has been found out that the given basic characteristics of the structure of the cast iron rg, Rb and Lg are directly proportional to the logarithm of the local solidification time. The original spatial model of solidification can therefore be used in its first approximation for the assessment of the pouring structure of massive cast-iron castings.

Changes in selected structural characteristics of shape memory alloys

Breczko T., Kuś K., Szczepanek J.

Technical Sciences / University of Warmia and Mazury in Olsztyn

2004

nr 7

175-182

The first part of this paper presents some experimental results relating to the study of evolution of residual elastic fields in the TiNi alloy subjected to a cyclical reversible martensite transformation (thermal and mechanical loads). Two selected structural parameters were assumed to characterize residual stresses generated in the cycled material. The analysis was conducted in the high-temperature austenitic phase in categories of progressing shape memory degradation. Taking into account crystalline structure and changes in the phase composition, the TiNiCu amorphous ribbons were examined under various times of heat treatment (annealing). Measurements were performed using mainly X-ray diffraction (XRD) methods. Changes in selected diffraction profiles and mathematical computations provided the basis for determining the structural parameters of TiNi alloys, and changes in the crystalline structure of TiNiCu alloys.

W pierwszej części artykułu przedstawiono wybrane wyniki badań doświadczalnych ewolucji resztkowych pól sprężystych w stopie TiNi na skutek wielokrotnego powtarzania przemiany martenzytycznej (obciążanie termomechaniczne). Dwa wybrane parametry strukturalne przyjęto jako wielkości charakteryzujące naprężenia resztkowe generowane w obciążanym materiale. Analiza była prowadzona w wysokotemperaturowej fazie austenitu w kategoriach postępującej degradacji efektu pamięci kształtu. Mając na uwadze strukturę krystaliczną oraz zmiany składu fazowego, w stopie TiNiCu przeprowadzono obróbkę cieplną przy różnych czasach jej stosowania. W pomiarach stosowano głównie metody dyfrakcyjne. Na podstawie zmian w wybranych profilach rentgenowskich i korzystając z odpowiedniego aparatu matematycznego prześledzono w badanych materiałach wybrane parametry strukturalne (stopy TiNi) oraz zmiany w strukturze krystalicznej (stopy TiNiCu).