Degradation of La2Zr2O7thermal barrier coatings

Mikuśkiewicz M., Moskal G., Jasik A.

Ochrona przed Korozją

2018

nr 6

155--158

The degradation process of La2Zr2O7 thermal barrier coatings (TBC) was presented in this paper. This system was deposited by air plasma spraying (APS) on AMS5599 alloy and on a NiCrAlY bond-coat. A scope of tests consisting of isothermal oxidation in air atmosphere at 1100°C for 500 h was performed. Detailed microstructural tests were carried out after 2, 10, 48, 175 and 500 hours of exposure. These tests included microstructure evaluation of a ceramic layer in both coating types, while particularly taking into account phenomena, which occur in a TGO (thermally growth oxide) zone. Evaluation of TGO zone growth was worked out and obtained results were compared with data for conventional TBC layers, which were deposited from 8YSZ powders.

W prezentowanym artykule przedstawiono proces degradacji powłok termoizolacyjnych TBC typu La2Zr2O7 Układ ten został wytworzony metodą natrysku plazmowego (APS) na stopie AMS5599 z międzywarstwą NiCrAlY. Zakres badań obejmował statyczne utlenianie próbek w atmosferze powietrza o temperaturze 1100° C przez 500 godzin. Szczegółowe badania mikrostruktury przeprowadzono po 2, 10, 48, 175 i 500 godzinach ekspozycji. Testy te obejmowały ocenę mikrostruktury warstwy ceramicznej obu typów, ze szczególnym uwzględnieniem zjawisk zachodzących w strefie TGO. Dokonano oceny wzrostu strefy TGO, a uzyskane wyniki porównano z danymi dla konwencjonalnych warstw TBC, które zostały osadzone z proszków 8YSZ.