Effects of Precipitation Hardedning in Co-Ni-Cr Alloy on Dissipative Motion of Dislocations by Amplitude-Dependent Internal Friction Measurements

Cosimati R., Mari D.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 4

3077--3082

The effects of precipitation hardening occurring in a Co-Ni-Cr alloy after annealing treatments have been studied by using mechanical spectroscopy. The amplitude-dependent internal friction (ADIF) due to the dissipative motion of dislocations reveals the presence of a threshold strain for weakly pinned dislocations. The change of ADIF curves and the increase of the elastic modulus after thermal cycles producing precipitates suggest that dislocations motion is hindered leading to increasing strength of the material. Precipitation is confirmed by the changes of thermoelectric power (TEP) and by hardness measurements showing a hardness increase at the same temperature as the maximum in TEP curve. The ADIF spectra as well as the interaction between dislocations and precipitates are interpreted by proposing a phenomenological model based on the Granato-Lücke theory.

Wpływ utwardzania wydzieleniowego występującego w stopie Co-Ni-Cr po wyżarzaniu zbadano za pomocą spektroskopii mechanicznej. Wewnętrzne tarcie zależne od amplitudy (ADIF) ze względu na rozpraszający ruch dyslokacji ujawnia obecność naprężenia granicznego dla słabo zakotwiczonych dyslokacji. Zmiana krzywych ADIF i wzrost modułu sprężystości po obróbce cieplnej wytwarzającej wydzielenia wskazują, że ruch dyslokacji jest utrudniony prowadząc do zwiększenia wytrzymałości materiału. Wydzielenia są potwierdzone przez zmiany siły termoelektrycznej i pomiary twardości, wykazujące zwiększenie twardości w tej samej temperaturze, co maksimum na krzywej TEP. Widma ADIF, a także oddziaływania między dyslokacjami i wydzieleniami są interpretowane przez proponowany fenomenologiczny model oparty na teorii Granato-Lücke.

Influence of High Pressure and High Temperature Hydrogen on Fracture Toughness of Ni-Containing Steels and Alloys

Balitskii A., Ivaskevich L., Mochulskyi V., Eliasz J., Skolozdra O

Archive of Mechanical Engineering

2014

Vol. LXI, nr 1

129--138

The effect of hydrogen on short-term strength, low-cycle durability and planestress fracture toughness of 10Cr15Ni27 steel, 04Cr16Ni56 and 05Cr19Ni55 alloys at pressure up to 35 MPa and temperature 293. . . 773 K was investigated. The modes of hydrogen action for which the elongation , reduction of area , low-cycle durability N and crack resistance parameters Kc of alloys are minimal were established: hydrogen pressure above 10 MPa (non-hydrogenated specimens of 04Cr16Ni56 alloy) and above 15 MPa (hydrogenated specimens of 10Cr15Ni27 steel and 05Cr19Ni55 alloy, hydrogen concentration 15 and 19 wppm, respectively).

W ramach przeprowadzonych badan określono wpływ wodoru na krótkotrwałą wytrzymałość i płasko-naprężeniową ciągliwość stali 10Cr15Ni27 oraz stopów niklu 04Cr16Ni56, 05Cr19Ni55 przy wielkościach ciśnienia do 35 MPa i zakresie temperatury od 293 do 773 K. Wpływ wodoru wysokiego ciśnienia powoduje, że wydłużenie, plastyczność, wytrzymałość nisko cyklowa N i parametr odporności na pękanie Kc przyjmują minimalne wartości dla próbek stopu 04Cr16Ni56 przy ciśnieniu wynoszącym 10 MPa, natomiast dla nasyconych wodorem próbek stali 10Cr15Ni27 i stopu 05Cr19Ni55 minimum wartości tych parametrów występuje przy ciśnieniu 15 MPa, dla koncentracji wodoru wynoszącej odpowiednio 15 i 19 wppm.