2 Fibres & Textiles in Eastern Europe

Znaleziono wyników: 2

Liczba wyników na stronie

Wyniki wyszukiwania

Wyszukiwano:
w słowach kluczowych: stosunek mieszanki

Sortuj według:

Ogranicz wyniki do:

Influence of the Bamboo/Cotton Fibre Blend Proportion on the Thermal Comfort Properties of Single Jersey Knitted Fabrics

Kadapalayam Chinnasamy K., Chidambaram P.

Fibres & Textiles in Eastern Europe

2017

Vol. 25, no. 6 (126)

53--57

The main aim was to find out the influence of the blend ratio and linear density on the thermal comfort properties of regenerated bamboo cotton blended single jersey knitted fabrics. An increase in the regenerated bamboo fibre ratio in the fabric influences the thermal comfort properties. Knitted fabrics prepared from regenerated bamboo blended yarns have lesser thickness and inferior mass per square meter than cotton fabrics. The proportion of regenerated bamboo fibre increases in the yarn as the value of thermal conductivity decreases in knitted fabrics. Water vapour permeability and air permeability confirm a similar increase as the proportion of regenerated bamboo fibre increases. 100% regenerated bamboo fabrics have superior air permeability values compared with regenerated bamboo/cotton blended fabrics. The statistical investigation also showed that the results are significant for the thermal comfort properties of regenerated bamboo cotton knitted fabrics.

Głównym celem pracy było poznanie wpływu współczynnika mieszania i gęstości liniowej przędz składowych na komfort cieplny dzianin bambusowo-bawełnianych. Zbadano właściwości komfortu cieplnego dzianin wykonanych w 100% z bawełny, w 100% z regenerowanego bambusa i dzianin mieszanych bambus/bawełna. Stwierdzono, że dzianina bambusowa ma najwyższą przepuszczalność powietrza i względną przepuszczalność pary wodnej. Powyższe wskaźniki są za to najniższe w przypadku wyrobów wykonanych z bawełny. Dzianiny bambusowe mają za to niższe od dzianin bawełnianych przewodnictwo cieplne. Zwiększenie stosunku zregenerowanego włókna bambusowego w wyrobie wpływa na jego komfort termiczny. Dzianiny bambusowe mają lepszą przepuszczalność powietrza w porównaniu z wyrobami mieszanymi bambus/bawełna.

Effect of the Acrylic Fibre Blend Ratio on Carpet Pile Yarn Compression Behaviour

Sheikhi H., Shaikhzadeh N. S., Etrati S. M., Dayiary Bidgoly M.

Fibres & Textiles in Eastern Europe

2012

Vol. 20, no. 4 (93)

77--81

The aim of this research was to investigate the compression properties of acrylic cut-pile carpet consisting of pile yarn with different fibre blend ratios. Acrylic fibres with finenesses of 7.69, 10.99 and 16.48 dtex were selected and then blended at 10 different percentages of blend ratios using the semi-worsted spinning system, and finally 10 two-fold pile yarn samples were produced. In addition typical cut-pile carpet samples with a constant pile density level of 15 pile/cm2 and pile height of 13 mm were produced by the face to face method. Then the compression behaviour of the carpet samples was evaluated under a constant compression stress of 40.89 kPa using an Instron tensile tester. The cut-pile carpet compression properties were evaluated using different compression parameters including the energy of compression WC, the decompression energy W?ŚC, the resilience of carpet compression RC and relative compressibility EMC. The experimental results were then statistically analysed using ANOVA and Duncan test methods. The results showed that with an increase in the coarse acrylic fibre component ratio (16.48 dtex fibre) the yarn specific volume first decreases and then increases. The results of this research revealed that acrylic cut-pile carpet produced from pile yarn with 16.48, 10.99 and 7.69 denier fibre at a 15%, 67% and 18% blend ratio, respectively, exhibit the highest WC, W?ŚC, EMC and RC values compared with other samples and commercially produced yarn. The statistical regression analysis suggested that the compression behaviour of acrylic cut-pile carpet is extremely close to the two parameter model proposed for woven fabrics.

Wytypowano do badań przędze nylonowe o masie liniowej 7.69 dtex, 10.99 dtex, 16.48 dtex, które łączono w różnych proporcjach dla wyprodukowania tkanin dywanowych. Zachowanie się dywanów przy ściskaniu badano przy stałym naprężeniu ściskającym 40.89 kPa, stosując aparat firmy Instron. Przy analizie ściskania uwzględniano: energię ściskania, energię dekompresji, odprężalność dywanów oraz względną ściśliwość. Wyniki analizowano statystycznie za pomocą programu ANOVA i testu Duncana. Określono parametry produkcji, dla których uzyskano najkorzystniejsze parametry ściskania.