Effect of the type of abrasive agent on the properties of cast Co-Cr alloys used in prosthetics

Augustyn-Pieniążek J., Kurtyka P.

Rudy i Metale Nieżelazne Recykling

|

2015

|

R. 60, nr 6

262--268

EN

The study presents the results of abrasion resistance tests carried out on alloys from the cobalt-based family, including Remanium 2001 (CoCrMoW) and Wironit LA (CoCrMo). Tests were performed on the Miller apparatus. The abrasive agent was slurry composed of water and silicon carbide particles of different granulations (SiC > 500 μm and SiC ~45 μm). The study included metallographic examinations, measurements of hardness and weight loss recorded in the tested materials after different times of abrasion amounting to 2, 4, 6, 8, 12 and 16 hours. The surfaces of samples subjected to abrasion were additionally examined by SEM. Alloys were characterized by a dendritic structure typical of cast materials. The results have proved the effect of abrasive particle size on the relative weight loss in Remanium 2001 and Wironit LA alloys. They have also proved that, regardless of the size of abrasive particles, the Wironit LA alloy offers better resistance to abrasion than Remanium 2001. This is due to, among others, the geometric features of the dendrite arms.

PL

W artykule przestawiono wyniki badań odporności na ścieranie stopów z grupy na osnowie kobaltu Remanium 2001 (CoCrMoW) i Wironit LA (CoCrMo), które wykonano na aparacie Millera. Ośrodek ścierający stanowiła zawiesina złożona z wody i węglika krzemu o różniej granulacji (SiC > 500 μm i SiC ~45 μm). W ramach badań wykonano obserwacje metalograficzne, pomiary twardości oraz zarejestrowano ubytki mas badanych materiałów po poszczególnych czasach ścierania tj. 2, 4, 6, 8, 12 i 16 h. Dodatkowo powierzchnie próbek po ścieraniu poddano obserwacji przy wykorzystaniu SEM. Wykazano, że stopy charakteryzowały się strukturą dendrytyczną typową dla materiałów odlewanych. Stwierdzono również istotną rolę wielkości elementów trących na wartości względnych ubytków mas stopu Remanium 2001 oraz Wironit LA. Pokazano również, że stop Wironit, cechuje się większa odpornością na ścieranie od stopu Remanium 2001, niezależnie od wielkości cząstek ścierających. Efekt ten jest związany między innymi z właściwościami geometrycznymi ramion dendrytów.

2

The gas corrosion of the cobalt base clad layer at elevated temperature

Smolenska H.

Journal of Achievements in Materials and Manufacturing Engineering

|

2006

|

Vol. 18, nr 1-2

235--238

EN

Purpose: Purpose of this paper is to evaluate the microstructural and mechanical properties evolution of the laser and PTA clad layers made of the powder containing cobalt after oxidation in air (750°C, 200 hours) and corrosion in exhaust gases (700°C, two month). Design/methodology/approach: The layers were made by cladding technique. Cladding was conducted with a high power diode laser HDPL ROFIN SINAR DL 020 and Plasma Transformed Arc method. The subsequent tracks were overlapped by 30÷40%. The performance of the hardfaced materials were evaluated by microstructure (optical and scanning electron microscope SEM), chemical analysis and micro hardness measurements. Findings: After heat treatment the microstructure of the clad layers did not change much, neither on the top part nor in the clad/steel interface. However the oxide layer on the surface is observed. The EDS analyze revile the composition of this scale which consisted generally of chromium and iron oxides. The semi-quantitative chemical analysis (EDS) of the dendritic regions and micro regions confirms changes in chemical contents before and after oxidation and after corrosion in exhaust gases. The oxidation at temperature 750°C for 200 hours in air and for two month in exhaust gases did not influence on the morphology of the clad layers neither on the top part nor in the clad/steel interface. However changes in chemical composition were observed. On the surface of both sort of clads the oxide layers were observed. These sorts of layers are resistant for the hot exhausted gases. Research limitations/implications: During the future research kinetic analyze of high temperature corrosion should be done also for different temperature and times of the process. Practical implications: The layers were designed as a method to prolong service time for the ship engine exhausted valve. Originality/value: The chemical composition of the powder was new one. Also using the laser cladding technique for ship engine parts is a subject of interest.

3

Azotowanie kobaltu i jego stopów

Jamrozek J., Konstanty J., Przybyłowicz K.

Rudy i Metale Nieżelazne

|

2004

|

R. 49, nr 1

29-31

PL

Przedstawiono wyniki badań dyfuzyjnych warstw uzyskanych podczas azotowania kobaltu oraz wieloskładnikowego stopu na osnowie kobaltu, w warunkach wyładowania jarzeniowego. Obróbkę prowadzono przez 4 godziny, w temperaturze 520 stopni Celsjusza, w atmosferze N2-33% obj. H2 pod ciśnieniem 3 hPa. Próbki do badań wykonano metodą metalurgii proszków, na drodze prasowania na gorąco proszku Co Extrafine oraz mieszanki proszków Co Extrafine i stopu niklu HMSP 1660-02 (po 50% mas.) Określono wpływ rodzaju materiału poddanego obróbce na strukturę warstwy dyfuzyjnej, jej grubość i mikrotwardość. W pracy wykorzystano stereoskopowy mikroskop Olympus SZ-STU2, z aparatem cyfrowym Camedia C-3030, mikrotwardościomierz Hanemanna oraz dyfraktometr rentgenowski TUR-M62.

EN

Results of the examination of difussive layers obtained by nitriding cobalt and multicomponent cobalt-based alloy in the conditions of glow discharge have been presented. The treatment was conducted for 4 hours at the temperature of 520 degrees centigrade, in the atmosphere of N2-33% vol. H2 under the pressure of 3 hPa. Samples for the examination were made by powder metallurgy methods, by hot pressing of the Co Extrafine powder and of a mixture of powders of Co Extrafine and HSMP 1660-02 nickel alloy (by 50 mass % each). An effect of a type of material subjected to such treatment on a structure of the diffusive layer has been determined as well as its thickness and microhardness. In the examination, Olympus SZ-STU2 stereo microscope fitted with Camedia C-3030 digital camera, Hanemann's microhardness meter, and the TUR-M62 type X-ray difractometer, were used.

4

Stop amorficzny Co68Fe4Mo1,5Si13,5B13 - materiał ekranujący pola elektromagnetyczne.

Ziębowicz A., Nowosielski R., Marciniak J.

Inżynieria Materiałowa

|

1999

|

R. XX, nr 1

19-22

PL

W artykule przedstawiono wyniki badań wpływu obróbki cieplnej na własności elektryczne i magnetyczne szkła metalicznego typu AEM (Co68Fe4Mo1,5Si13,5B13). Omówiono zmiany rezystywności, natężenia koercji, pozostałości magnetycznej i przenikalności magnetycznej maksymalnej stopu w stanie bezpośrednio po odlaniu i po wygrzewaniu w zakresie temperatury od 100 do 400 stopni Celsjusza w czasie 1-64 godzin.

EN

The paper presents the results of investigations concerning the effect of heat treatment on the electric and magnetic properties of metallic glass of the AEM type (Co68Fe4Mo1,5Si13,5B13). The paper also deals with changes of the resistivity, intensity of the coersive force, residual flux density and maximum magnetic permeability of the alloy immediately after casting and soaking 1-64 hours within the temperature range from 100 to 400 degrees centigrade.