Wyniki wyszukiwania - BazTech

1

Evaluation of tensile properties of 5052 type aluminum-magnesium alloy at warm temperatures

Ozturk F., Toros S., Kilic S.

Archives of Materials Science and Engineering

|

2008

|

Vol. 34, nr 2

95-98

EN

Purpose: The purpose of the paper is to evaluate the tensile properties of 5052 type aluminum-manganese alloy in warm temperatures. Design/methodology/approach: In this research, uniaxial tensile deformation behavior of 5052-H32 type aluminum magnesium alloy was studied range between room to 300°C and in the strain rate range of 0.0083-0.16 s-1. Findings: It was observed that the uniaxial tensile elongation of the material increases with increasing temperatures and decreases with increasing strain rates. The formability of this material at warm temperatures is better than the room temperature and the most suitable forming conditions were obtained at 300°C and 0.0083 s-1. Practical implications: Results indicate that strain rate sensitivity plays an important role in the formability of this material at warm temperatures. Originality/value: The evaluation of the tensile properties of 5052 type aluminum-manganese alloy in warm temperatures.

2

Badania fraktograficzne spajanych stopów Al-Mg

Czechowski M.

Przegląd Spawalnictwa

|

2006

|

R. 78, nr 5-6

32-34

PL

Przedstawiono charakterystyczne dla spajanych stopów AI-Mg powierzchnie pęknięcia próbek z badań odporności na korozję naprężeniową przy małej prędkości odkształcania oraz z badań niskocyklowego zmęczenia. Badano stopy AI-Mg spajane metodami MIG oraz zgrzewane tarciowo z przemieszaniem materiału (FSW). Główny nacisk położono na określenie czynników wpływających na rozwój pęknięć w aspekcie mikrostrukturalnym. Ocena mikrostruktur oraz powierzchni dróg pękania wykonana została za pomocą mikroskopu skaningowego elektronowego o dużej rozdzielczości Philips XL30 i przystawki EDAX do mikroanalizy składu chemicznego za pomocą dyfraktometru rentgenowskiego EDS. Zaobserwowano, że zarodkowanie pęknięć powstaje na granicach międzyfazowych osnowy z wydzieleniami, a rozwój pęknięcia głównego zachodzi poprzez łączenie mikropustek.

EN

One introduced characteristic for welded AI-Mg alloys surfaces of the crack of samples from research of the stress corrosion cracking at the slow strain rate tests and from Iow-cycle fatigue tests. The AI-Mg alloy welded by MIG and by friction stir welding (FSW) were investigated. The main pressure was put on the qualification of influent factors on the development of cracks in the microstructure aspect. The metallographic tests was carried out by the scanning electron microscope (SEM) with the chemical composition analysis (energy dispersive spectroscopy, EDS). One observed that the initiated of cracks came into being on interphasic borders of the matrix with particles. The development of the main crack happens through the joining microvoids.

3

Incubation period in cavitation erosion of the aluminium-magnesium alloy PA2.

Krella A., Zieliński A., Jezierska E.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 4

490-493

EN

The cavitation erosion can cause different damage of material, depending on cavitation intensity. Here the relationships between cavitation intensity and changes in microstructure of aluminium-magnesium alloy are presented.

PL

Erozja kawitacyjna powoduje różne uszkodzenia materiału w zależności od intensywności kawitacji. W artykule przedstawiono zależności między intensywnością kawitacji a zmianami mikrostruktury badanego materiału.