Effect of selected parameters of the melt-spinning process on the thickness and magnetic properties of Nd-Fe-Al ribbons

Kaszuwara W., Michalski B., Latuch J., Rębiś J.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

306-308

Magnetically hard Nd-Fe-Al alloys, cast by the melt-spinning method, could be used for the manufacture of miniature magnets by cutting them from ribbons, provided that we are able to produce wide Nd-Fe-Al ribbons of a thickness of the order of tenths of millimeter, with smooth plane-parallel surfaces and good magnetic properties. The present study concerns the effect of the basic parameters of the melt- spinning process on the magnetic properties (Fig. 1, 2 and 3) and surface topography (Fig. 5) of such ribbons. It has been found that the best properties of the ribbons are achieved when the melt-spinning process parameters are selected so that the quenching rate is low (wheel speed of 5 m/s, pressure of 0.1 MPa). Our examinations have also shown that with decreasing wheel speed and increasing pressure, the free surface (opposite to the wheel) loses its flatness. The best magnetic properties are shown by the ribbons whose surface is most developed (more irregular).

Magnetycznie twarde stopy Nd-Fe-Al, odlewane metodą melt-spinning mogłyby być stosowane na miniaturowe magnesy wytwarzane przez wykrawanie z taśm. Warunkiem tego jest otrzymanie szerokich taśm o grubości rzędu dziesiątych części milimetra o gładkich płasko równoległych powierzchniach i dobrych właściwościach magnetycznych. W pracy zbadano wpływ podstawowych parametrów procesu melt-spinning na właściwości magnetyczne uzyskanych taśm (rys.1, 2 i 3) i topografię ich powierzchni (rys. 5). Stwierdzono, że dla uzyskania najlepszych właściwości należy tak dobrać parametry procesu melt-spinning, aby szybkość chłodzenia była mała (prędkość bębna 5 m/s, ciśnienie wypychające 0,1 MPa). Badania wykazały również, że powierzchnia swobodna taśm (przeciwległa do bębna) nie jest płaska, a jej nierówności zwiększają się przy zmniejszaniu szybkości bębna i zwiększaniu ciśnienia wypychającego. Taśmy o najlepszych właściwościach magnetycznych mają najbardziej rozwiniętą powierzchnię.

Hard magnetic properties of bulk Nd-Fe-Al glasses

Kaszuwara W., Michalski B., Latuch J., Witkowski A., Leonowicz M.

Inżynieria Materiałowa

2007

Vol. 28, nr 3-4

275-278

Rapidly cooled Nd-Fe-Al alloys of, containing about 60at.% of Nd and about 10at.% of Al, are hard magnetic materials. They can be produced in the form of massive large-size samples. When examined by the X-ray methods they seem to be amorphous, but in fact, their phase structure contains both amorphous and ordered regions. The present study is concerned with the effect of the Nd content (from 56 to 64at.%) on the magnetic properties of these materials at room temperature and at low temperatures. It has been shown that their magnetic saturation increases with decreasing Nd content, whereas the coercivity reaches its maximum at the Nd content of 60at.%. As the Nd content increases, Nd appears in the form of crystalline precipitates, whose presence can be observed by X-ray methods. At smaller Nd contents, the diffractograms contain peaks of unidentified phases. The dominant mechanism of coercivity involves pinning of the domain walls.

Szybko chłodzone stopy z układu Nd-Fe-Al, zawierające około 60% at Nd i około 10% at. Al, są materiałami magnetycznie twardymi. Stosując metody rentgenowskie można stwierdzić, że są to materiały amorficzne. Możliwe jest ich otrzymywanie w postaci masywnych próbek o dużych rozmiarach. W rzeczywistości w strukturze fazowej szybko chłodzonych stopów Nd-Fe-Al występują fazy amorficzne oraz obszary wykazujące uporządkowanie. W niniejszej pracy określono wpływ zawartości Nd (w przedziale od 56 do 64% at.) na właściwości magnetyczne mierzone w temperaturze pokojowej oraz w obniżonych temperaturach. Wykazano, że namagnesowanie nasycenia materiału rośnie wraz ze zmniejszeniem zawartości Nd i osiąga maksimum dla 58% at., natomiast koercja osiąga wartości maksymalne przy zawartości 60% at. Nd. Większa zawartość Nd sprawia, że występuje on w postaci krystalicznych wydzieleń, których obecność można zarejestrować metodami rentgenowskimi. Przy mniejszych zawartościach Nd na dyfraktogramach pojawiają się piki od niezidentyfikowanych faz. Dominującym mechanizmem koercji jest kotwiczenie ścian domenowych.