1
Content available Geometry of remeltings and efficiency of the surface remelting process applied to cobalt alloy castings
Mróz M., Orłowicz W., Tupaj M.
Archives of Foundry Engineering
|
2013
|
Vol. 13, iss. 2
95--98
EN
The paper summarises results of measurements of remelting area geometry, thermal efficiency and melting efficiency characterising the surface remelting process applied to castings of MAR-M-509 cobalt alloy. The remelting process was carried out with the use of GTAW (Gas Tungsten Arc Welding) method in protective atmosphere of helium, at the electric current intensity in the range from 100 A to 300 A, and the electric arc scanning velocity vs in the range from 200 mm/min to 800 mm/min. The effect of current intensity and electric arc scanning velocity on geometrical parameters of remeltings, thermal efficiency, and melting efficiency characterising the remelting process has been determined.
2
Content available Stress rupture test of MAR-M509 alloy with structure refined by rapid resolidification
Mróz M., Orłowicz W., Tupaj M., Trytek A.
Archives of Foundry Engineering
|
2012
|
Vol. 12, iss. 4
117-120
EN
This study presents results of stress rupture test of MAR-M-509 cobalt alloy samples, as-cast and after surface refining with a concentrated stream of heat. Tests were conducted on samples of MAR-M-509 alloy castings, obtained using the lost-wax method. Casting structure refining was performed with the GTAW method in argon atmosphere, using the current I = 200 A and electrical arc scanning velocity vs = 100, 150, 200 and 250 mm/min. The effect of rapid resolidification of the MAR-M-509 alloy on the microstructure was examined and significant improvement in stress rupture test was observed.
3
Content available remote Fatigue strength of MAR-M509 alloy with structure refined by rapid crystallization
Mróz M., Orłowicz W., Tupaj M., Trytek A.
Archives of Foundry Engineering
|
2010
|
Vol. 10, iss. 3
119--122
EN
This study presents test results of high-cycle (N>2⋅107) fatigue bending strength of MAR-M-509 cobalt alloy samples, as cast and after surface refining with a concentrated stream of heat. Tests were conducted on samples of MAR-M59 alloy casts, obtained using the lostwax method. Cast structure refining was performed with the GTAW method in argon atmosphere, using the current I = 200 A and electrical arc scanning velocity vs = 250 mm/min. The effect of rapid crystallization occurring after the fusion process is refinement of the MAR-M509 alloy cast microstructure and significant improvement in bending fatigue strength.
4
Content available remote Evaluation of fractures in MAR-M509 alloy samples after fatigue strength tests
Mróz M., Orłowicz W., Tupaj M.
Archives of Foundry Engineering
|
2010
|
Vol. 10, iss. 3
115--118
EN
The paper presents the result of fracture analysis in MAR-M509 samples after high-cycle bending fatigue strength tests. Microstructural tests were carried out with a scanning electron microscope. To identify carbide phases a quantitative analysis of the chemical composition was made. The fracture surface and the surface in a plane perpendicular to the fracture surface were observed. It was discovered that the crack initiation and propagation occurs on carbide separations.
5
Statistical analysis of evaluation reproducibility of the area of MC phase's plane section in the MAR M509 cobalt superalloy
Skupień P., Maliński M.
Inżynieria Materiałowa
|
2008
|
Vol. 29, nr 4
355-357
EN
As a part of the research concerning evaluation of reproducibility of the size of selected structure elements of metallic materials (plane section area), a methodology was developed based on an analysis of data obtained through computer simulation with the use of normal, log-normal and uniform distributions. Next, the developed methodology was verified in relation to the measurements of MN carbide phase plane section area in MAR M509 alloy. The results obtained allow the determination of the number of measuring fields necessary for determining correctly the area of carbide phase plane section in this alloy.
PL
W ramach badań nad oceną odtwarzalności wielkości wybranych elementów struktury tworzyw metalicznych (powierzchni płaskiego przekroju) opracowano metodykę na podstawie analizy danych uzyskanych drogą symulacji komputerowej z wykorzystaniem rozkładu normalnego, logarytmo-normalnego oraz równomiernego. W dalszej kolejności dokonano weryfikacji opracowanej metodyki w odniesieniu do pomiarów powierzchni płaskiego przekroju fazy węglikowej MN w stopie MAR M509. Otrzymane wyniki pozwoliły określić niezbędną liczbę pól pomiarowych do poprawnego określenia pola powierzchni płaskiego przekroju fazy węglikowej w tym stopie.
6
Influence of solution heat treatment parameters on the quantity and morphology of M23C6 carbides in MAR M509 cobalt superalloy
Skupień P., Szala J.
Inżynieria Materiałowa
|
2008
|
Vol. 29, nr 4
358-361
EN
The influence of solution heat treatment parameters on the morphology and number of M23C6 carbide precipitations in MAR M509 superalloy was analysed. It was found that M23C6 carbides in this alloy create together with ay solid solution two morphologically different eutectics. The dissolution process of the first of them, characterized by a high compactness of the phases which create it, stops at temperature below 1260°C. The second, quantitatively dominant eutectic, which is dissolved only after 4 hours of annealing at a temperature of 1260°C, is more stable.
PL
W pracy analizowano wpływ parametrów przesycania na morfologię i ilość wydzieleń węglików M23C6 w nadstopie MAR M509. Stwierdzono, że węgliki M23C6 w tym stopie tworzą z roztworem stałym y dwie odmienne morfologicznie eutektyki. Proces rozpuszczania pierwszej z nich charakteryzującej się dużą zwartością tworzących ją faz kończy w temperaturze niższej niż 1260°C. Bardziej stabilna jest druga, dominująca ilościowo eutektyka, która zostaje rozpuszczona dopiero po 4 godzinach wyżarzania w temperaturze 1260°C.
7
Wielkość ziarna pierwotnego jako strukturalne kryterium powtarzalności procesu technologicznego elementu wykonanego ze stopu MAR-M509
Markusik M., Adamiec J., Cwajna J., Borla K.
Inżynieria Materiałowa
|
2006
|
Vol. 27, nr 3
201-204
PL
W pracy przedstawiono wyniki ilościowej oceny makrostruktury odlewanych precyzyjnie segmentów osłonowych barier cieplnych (BOAS) z nadstopu kobaltu MAR-M509. Badania przeprowadzono na segmentach doświadczalnych otrzymanych w początkowej fazie realizacji projektu badawczego oraz na segmentach odlanych z zastosowaniem zoptymalizowanej technologii formy, przetapiania stopu wyjściowego master-heat oraz odlewania segmentów. Uzyskane wyniki ilustrują postęp osiągnięty w zakresie ujedno-rodnienia wielkości i kształtu ziaren pierwotnych ujawnianych na powierzchni roboczej segmentów i na ich przekrojach poprzecznych. Wskazują one również na możliwość zastosowania wyników ilościowej oceny wielkości i kształtu ziaren pierwotnych jako strukturalnych kryteriów oceny powtarzalności technologii precyzyjnego odlewania segmentów osłonowych barier cieplnych z nadstopu MAR-M509.
EN
The paper presents the results of the quantitative macrostructure evaluation of the precisely cast segments of the blade outer air seals (BOAS) made of the MAR-M509 cobalt alloy. The research was conducted on the experimental segments which were received in initial phase of the research project. The research was conducted also on segments which were cast with application of the optimum form technology, initial master-heat alloy remelting and segments casting. Acquired results illustrate progress achieved in homogenizing of the size and shape of primary grains revealing on the working surface of segments and on its transverse cross section. They also indicate possibility of applying the results of quantitative evaluation of the primary grains size and shape as a structural criterion of the casting of the blade outer air seals made of the MAR-M509 super alloy technological process reproducibility.
8
Ilościowa ocena wielkości i kształtu ziaren pierwotnych w odlewanych precyzyjnie elementach z nadstopu kobaltu MAR-M509
Adamiec J., Szczotok A., Cwajna J.
Inżynieria Materiałowa
|
2006
|
Vol. 27, nr 3
108-111
PL
W artykule przedstawiono rezultaty prac badawczych nad makrostrukturą powierzchni roboczej (rys. 1, 3a, 4a) oraz makrostrukturą przekroju poprzecznego (rys. 2, 3b, 4b) żaroodpornego komponentu wykonanego ze stopu MAR-M509. Opisano kolejne etapy postępowania mającego na celu wyznaczenie parametrów charakteryzujących ziarno w przypadku obu rodzajów badanych powierzchni. Efektem tych działań jest opracowanie kompleksowej i powtarzalnej procedury oceny ilościowej ziaren pierwotnych badanego komponentu. Ponadto procedura ta może stać sie punktem wyjścia przy próbach stworzenia podobnych procedur w odniesieniu do innych materiałów i innych komponentów.
EN
The paper has presented results of researches on work surface macrostructure (Fig. 1, 3a, 4a) and transverse cross section macrostructure (Fig. 2, 3b, 4b) of a heat-resistant component made of MAR-M509 alloy. Consecutive stages of procedure being aimed at determination of parameters characterizing grain in the case of both kinds of the analyzed surfaces were described. An effect of these activities was elaboration of a complex and repeatable procedure of quantitative description of the analyzed component’s primary grains. Moreover, the procedure could become a point of reference for trials of creating similar procedures for other materials and components.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.