Calculations of oxide inclusions composition in the steel deoxidized with Mn, Si and Ti

Podorska D., Drożdż P., Falkus J., Wypartowicz J.

Archives of Metallurgy and Materials

2006

Vol. 51, iss. 4

581-586

The work deals with the determination of the composition of liquid oxide solution MnO-SiO2-TiO2-Al2O3, present as an inclusion in liquid steel during its solidification. The region of compositions at which oxide solution remains entirely liquid at the temperatures 1523 K and 1673 was calculated by means of FACT program. The evolution of oxide phase chemical composition in thermodynamic equilibrium with liquid steel during its equilibrium solidification was calculated. The procedure of calculations may be applied in the determination of the conditions for acicular ferrite formation, which nucleates at oxide inclusions.

Praca zajmuje się określeniem zmian składu ciekłego roztworu tlenkowego MnO-SiO2-TiO2-Al2O3 znajdującego się w postaci wtracenia w ciekłej stali w trakcie jej krzepnięcia. Obliczono przy pomocy programu FACT zakres składów roztworu tlenkowego, przy jakim pozostaje on całkowicie ciekły przy temperaturach 1523 i 1673 K. Wyznaczono ewolucje składu chemicznego fazy tlenkowej pozostającej w równowadze termodynamicznej z ciekłą stalą w trakcie jej równowagowego krzepnięcia. Procedura obliczeniowa może być zastosowana do określania warunków tworzenia ferrytu iglastego zarodkującego na wydzieleniach tlenkowych.

The solubility of sulphur in oxide inlusions in Si and Mn deoxidised steel

Kalicka Z., Kawecka-Cebula E., Wypartowicz J.

Archives of Metallurgy and Materials

2004

Vol. 49, iss. 3

585-593

The solubility of MnS in liquid oxide melts: MnO-SiO2, MnO-SiO2-Al2O3 MnO-SiO2-FeO and MnO-SiO2-TiO2 have been calculated from the values of MnO activity and sulphide capacity of these melts. The MnO activity in MnO-SiO 2 melt was based on the experimental data of Rao and Gaskell. The Ban-ya regular solution model was checked on the base of experimental data and it appeared inadequate to the MnO-SiO2 liquid solution. The sulphide capacity of oxide solutions was calculated from the model of Nzotta, Sichen and Seetharaman, with exception of MnO-SiO2-TiO2 melt, for which model parameters are incomplete. It appeared that replacement of SiO 2 with Al2O3 and FeO decreases MnS solubility, while introduction of TiO2 increases this solubility. The highest solubility, up to 80 mass % was obtained in binary MnO-SiO2 solutions.

Obliczono rozpuszczalność MnS w ciekłym roztworze tlenków: MnO-SiO2, MnO-SiO2-Al2O3, Mno-SiO2-FeO i MnO-SiO2-TiO2 na podstawie wartości aktywności MnO w tych roztworach i ich pojemnościsiarczkowej. Aktywności MnO w ciekłym roztworze MnO-SiO2 zostały wyznaczone z danych doswiadczalnych Rao i Gaskella. Na podstawie dostępnych danych doświadczalnych zweryfikowano również stosowalność modelu roztworu regularnego Ban-ya. Model ten okazał się nieodpowiedni dla opisu roztworu MnO-SiO2. Pojemność siarczkowa roztworów tlenkowych została obliczona na podstawie modelu Nzotta, Sichen, Seetharaman, za wyjątkiem roztworu MnO-SiO2-TiO2, dla którego niekompletne są parametry modelu. Stwierdzono, że zastąpienie SiO2 przez Al2O3 i FeO obniża rozpuszczalnośc MnS, podczas gdy wprowadzenie TiO2 podnosi rozpuszczalność MnS. Najwyższe wartości rozpuszczalności, do 80% masowych, występują w przypadku roztworu dwuskładnikowego MnO-SiO2.