Sintered high speed steel-base composites for wear and sliding applications

Leżański J., Konstanty J., Kazior J.

Kompozyty

2001

R. 1, nr 1

32-34

PM route has been chosen to fabricate M3/2 HSS-base wear resistant composite materials with WC and Cu additions of 0:30 wt.-% and 7.5:45 wt.-% respectively. The effects of the mixed powder composition on its cold compressibility and sintering behaviour have been investigated. The kinetics of sintering was monitored by means of dilatometry. The as-sintered specimens were subjected to density measurements, hardness and wear resistance tests, micro-structural examinations as well as X-ray diffraction analysis. It has been found that WC reinforced material shows superior resistance to wear while higher Cu content markedly improves sliding properties thus creating prospects of new applications.

Wykorzystując klasyczną metodę metalurgii proszków, wyprodukowano partie odpornych na ścieranie, kompozytowych spieków na osnowie stali szybkotnącej z gatunku M3/2, z dodatkiem do 30% węglika wolframu oraz od 7,5 do 45% miedzi. Badano wpływ wyjściowego składu mieszanek proszków na ich zgeszczalność oraz, stosując metodę dylatometryczną (rys. 1), na kinetykę procesu spiekania. Ponadto, spieki poddano pomiarom gęstości (rys. 2), twardości (rys. 3), odporności na zużycie ślizgowe (rys. 4), jakościowej analizie rentgenowskiej (rys. 5) oraz obserwacji struktury z użyciem mikroskopu skaningowego (rys. 6). W wyniku badań stwierdzono, że odporność spieków na zużycie ślizgowe rośnie wraz ze wzrostem zawartości węglika wolframu, podczas gdy zwiększanie zawartości miedzi do 45% wyraźnie poprawia własności ślizgowe materiału, co stwarza nowe możliwości zastosowania badanych materiałów w węzłach tarcia.