Wpływ mikrododatków V, Nb, Ti, Al i azotu na hartowność stali 40Cr8

Adrian H., Staśko R.

Stal, Metale & Nowe Technologie

|

2015

|

nr 9-10

124--128

PL

W pracy przedstawiono wyniki badań hartowności stali niskostopowej 40Cr8 zawierającej zróżnicowaną zawartość azotu oraz mikrododatki V, Nb, Ti i Al. Stwierdzono spadek hartowności stali ze wzrostem ilości azotu, przy braku mikrododatków. Obecność mikrododatków powodowała wzrost hartowności stali i rozdrobnienie wielkości ziarna austenitu. Idealna średnica krytyczna określona na podstawie próby hartowania od czoła mieściła się w zakresie od 140 do 199 mm.

EN

In the paper results of investigations of hardenability of low alloy steel 40Cr8 with different contents of nitrogen and microalloying elements V, Nb, Ti and Al are presented. In investigated steel without microalloying elements the hardenability decreased with nitrogen content, whilst in microalloyed steel significant increase of hardenability was observed. Additionally microalloying elements decreased the austenite grain size. The ideal critical diameter of investigated melts estimated using Jominy test was in the range 140-199 mm.

2

Wysokowytrzymałe stale konstrukcyjne ulepszane cieplnie

Węglowski M.S.

Stal, Metale & Nowe Technologie

|

2014

|

nr 9-10

142--146

PL

Nowoczesne konstrukcje stalowe są coraz bardziej skomplikowane, a jednocześnie muszą spełniać coraz wyższe wymagania eksploatacyjne. Konstruktorzy i wykonawcy z jednej strony zmierzają do obniżenia masy konstrukcji, redukcji kosztów jej wytworzenia, a z drugiej jednocześnie wymiary samych konstrukcji są coraz większe. Jednym z materiałów, który może sprostać tym sprzecznym wymaganiom, są stale o wysokiej wytrzymałości i niskiej temperaturze przejścia w stan kruchy.

EN

Modern steel structures are becoming more complex, and simultaneously have to meet increasingly higher performance requirements. Designers and manufacturers tend to decrease the weight of structures, reduce their production costs but at the same time the dimensions of these structures increase. One of the materials that can meet these conflicting demands are high-strength steels of low-temperature brittle transition.

3

Microstructure and mechanical properties of ultra-high strength steel Weldox 1300

Węglowski M. S., Osucha W., Michta G.

Inżynieria Materiałowa

|

2013

|

Vol. 34, nr 3

205--208

EN

Toughened (quenched and tempered) steels are ﬁne-grained alloy steels. By selecting a proper chemical composition as well as the conditions of rolling and heat treatment, one obtains steels having different levels of yield point ranging from 460 to 1300 MPa. These steels contain chromium and molybdenum which decrease critical cooling rate and increase hardenability. The presence of niobium or vanadium in these steels guarantees obtaining ﬁne grains of austenite during rolling and thus very tiny lamellas of supersaturated ferrite (martensite) after cooling. In the present study, the characteristics of Weldox 1300 steel, in respect to microstructures and mechanical properties were investigated. The mechanical properties were evaluated based on the tensile, impact and hardness tests. The microstructure of steel was examined by the light, scanning (SEM) and transmission electron microscopy (TEM). The mechanical investigation revealed that the Weldox 1300 steel characterized by high values of impact strength both at room temperature and lower temperatures. The microstructure examination have shown that the microstructure of the Weldox 1300 steel is composed of the tempered martensite with a hardness of about 501 HV10. The TEM investigation revealed that inside the laths of martensite, the minor precipitations mainly V(CN) were observed.

PL

Stale ulepszone cieplnie są drobnoziamistymi stalami stopowymi (niskostopowymi). Dobierając odpowiedni skład chemiczny, warunki walcowania i obróbki cieplnej, uzyskuje się stale o różnym poziomie granicy plastyczności w zakresie od 460 do 1300 MPa. Chrom i molibden, znajdujący się W tych stalach, obniżają krytyczną prędkość chłodzenia i zwiększają hartowność. Obecność niobu lub wanadu w tych stalach gwarantuje otrzymanie drobnych ziaren austenitu podczas walcowania, a tym samym bardzo drobnych płytek przesyconego ferrytu (martenzytu) po ochłodzeniu. W pracy przedstawiono wyniki badań własności mechanicznych i badań mikrostrukturalnych stali Weldox 1300. Własności mechaniczne zostały ocenione na podstawie próby rozciągania, badań udamości oraz pomiarów twardości. Mikrostruktura stali została zbadana za pomocą mikroskopu świetlnego, SEM i TEM. Wyniki badań własności mechanicznych wskazują, iż stal charakteryzuje się dużą udamością zarówno w temperaturze pokojowej, jak i obniżonej. Badania wykazały, że mikrostruktura stali składa się z martenzytu odpuszczonego o twardości około 501 HVl0. Badania TEM ujawniły, iż wewnątrz listew martenzytu są obecne wydzielenia głównie V(CN).