Fatigue resistance of spring steel at high-frequency cyclic loading

Bokůvka O., Palček P., Mintách R., Nový F.

Zeszyty Naukowe Instytutu Pojazdów / Politechnika Warszawska

|

2011

|

z. 4/85

13--16

EN

High-frequency cyclic loading (f = 20 kHz, T = 20 ± 5 °C, R = -1) is used to determine near threshold crack growth rates, da/dN = f (Ka) and the threshold stress intensity factor amplitude Kath in two different leaf spring steels used in the transportation industry. The leaf springs are usually made of high-strength low-alloyed structural steels (with ultimate strength from Rm = 1300 MPa to 1650 MPa) produced according to different technologies; the trend is use steels with increasingly high tensile strength. The obtained results however confirm that an increase in tensile strength in leaf spring steels reduced values of Kath and increase the fatigue crack growth rates; hence the highest sensitivity to initial defects and lowest fatigue cracks resistance.

PL

Wysokoczęstotliwościowe obciążenie cykliczne (f = 20 kHz, T = 20 ± 5 °C, R = -1) jest wykorzystywane do określenia szybkości wzrostu progu pęknięcia, da / dN = f (Ka) oraz progu amplitudy współczynnika intensywności naprężeń Kath dla dwóch różnych stali wykorzystywanych do budowy resorów piórowych stosowanych w branży transportowej. Resory piórowe są zwykle wykonane z wysokiej wytrzymałości niskostopowych stali konstrukcyjnych (z wytrzymałością Rm = 1300 MPa do 1650 MPa) produkowanych według różnych technologii. Aktualnym trendem jest stosowanie stali z coraz większą wytrzymałością na rozciąganie. Uzyskane wyniki potwierdzają jednak, że wzrost wytrzymałości na rozciąganie w stalach wykorzystywanych na resory piórowe zmniejszenie wartość Kath i zwiększa szybkość wzrostu pęknięcia zmęczeniowego, stąd są one bardzo wrażliwe na wady początkowe i mają najniższą odporność na pękanie zmęczeniowe.

2

Wpływ metody wytwarzania naroży kształtowych na taśmach walcowanych na zimno ze stali konstrukcyjnej na ich jakość

Adamiec A., Radwański K., Wiedermann J., Stępień J.

Prace Instytutu Metalurgii Żelaza

|

2010

|

T. 62, nr 1

161-167

PL

W ramach pracy przedstawiono wpływ metod wytwarzania zaokrąglonych naroży kształtowych wykonanych na taśmach ze stali konstrukcyjnych w stanie po walcowaniu na zimno na ich jakość. Taśmy z narożami kształtowymi stosowane są między innymi jako noże do kosiarek i rozdrabniaczy, listwy nożowe do maszyn rolniczych czy elementy mocowań plandek samochodów ciężarowych. Naroża kształtowe wykonywano metodą skrawania oraz metodą walcowania. Skrawane naroża kształtowe mogą być wykonywane na taśmach po walcowaniu na gorąco i walcowaniu na zimno. W niniejszej pracy naroża kształtowe wykonano na taśmach po walcowaniu na zimno. W przypadku taśm z walcowanymi narożami kształtowymi materiałem wyjściowym jest drut. W pracy wykonano badania jakości naroży kształtowych taśm oraz wyznaczono rozkłady twardości po kolejnych etapach ich produkcji. W wyniku przeprowadzonych badań można stwierdzić, że metoda walcowania naroży kształtowych w porównaniu do metody z zastosowaniem obróbki skrawania brzegów pozwala na uzyskanie lepszej jakości zaokrąglonych naroży. Taśmy z walcowanymi narożami kształtowymi wykazują wysoką jakość w zakresie wymiarów, stanu powierzchni oraz symetrii.

EN

In this paper, the influence of production methods of cold rolled structural steel strip with trimmed edge on their quality was determined. Strips with trimmed edges can be applied inter alia as mower and shredder cutters, cutter-bars for agricultural machines or elements of truck tarpaulin fastenings. Trimmed edges were produced using both machining and rolling. Machined trimmed edges can be formed on strips after hot and cold rolling process. In the concerned work these were formed following cold rolling. The input material for production of strips with cold rolled trimmed edges is the wire. Examinations of quality of trimmed edges and distributions of hardness were carried out after different stages of their production. The main conclusion of a detailed study is that the method of rolling edges on the cold rolling constructional steel strip compared to the machining method allows for obtaining higher quality of trimmed edges. Steel strips with trimmed edges obtained by rolling are characterized by high quality including accuracy of dimensions, state of surface and symmetry.

3

Numerical verification of the rolls calibration for 200×6 mm flat bars rolling

Laber K., Sygut P., Mróz S., Dyja H.

Hutnik, Wiadomości Hutnicze

|

2010

|

Vol. 77, nr 5

214-216

EN

Numerical verification of the rolls calibration for 200×6 mm flat bars rolling was carried out within this work for the technological conditions of a Bar Rolling Mill. The purpose of the performed theoretical analysis was to verify the correctness of the developed roll pass design scheme for the ability to assure the proper shape and dimensions of finished product. The scope of studies carried out within the work covered the verification of the stability and symmetricalness of band during the rolling process in edging passes. For the theoretical studies, the Forge2008Ž software application was used.

PL

W pracy przeprowadzono numeryczną weryfikację kalibrowania walców do walcowania prętów płaskich o wymiarach 200×6 mm, dla warunków technologicznych jednej z walcowni prętów. Celem przeprowadzonej analizy teoretycznej było sprawdzenie poprawności opracowanego schematu kalibrowania walców pod kątem zapewnienia właściwego kształtu oraz wymiarów wyrobu gotowego. Zakres przeprowadzonych w pracy badań obejmował również sprawdzenie stabilności i symetryczności pasma podczas procesu walcowania w wykrojach osadczych. Do badań teoretycznych wykorzystano program komputerowy Forge2008Ž.

4

Badania elementów ze stali sprężynowej C67S

Pocica A., Nowak A.

Zeszyty Naukowe. Mechanika / Politechnika Opolska

|

2009

|

z. 95

55-56

5

Influence of heat treatment and corrosion atmosphere on surface layer properties of selected spring steels

Drozd K., Weroński A.

Inżynieria Materiałowa

|

2004

|

R. XXV, nr 3

713-716

EN

In this paper there are presented results of specimen tests made of spring steels. The specimens were subjected to heat treatment using different parameters and to salt spray chamber medium. Photographs of surface layer characteristic structures and hardness diagrams at a variable distance from surface have been showed. The steel of 50HS grade has been assented for the most resistant to a destructive action of a furnace atmosphere and corroding medium. The greatest changes of a microhardness were visible in the specimens of 60SiCr7 steel grade.

PL

W pracy przedstawiono wyniki badań próbek wykonanych ze stali sprężynowych. Próbki poddawano obróbce cieplnej przy zastosowaniu różnych parametrów oraz oddziaływaniu środowiska komory solnej. Zamieszczono fotografie charakterystycznych struktur warstw wierzchnich (ww) oraz wykresy twardości w zmiennej odległości od powierzchni. Jako najbardziej odporną na destrukcyjne działanie atmosfery pieca i środowiska korozyjnego oceniono stal 50HS. Największe zmiany mikrotwardości wystąpiły dla próbek ze stali 60SiCr7.

6

Wpływ temperatury na zmianę własności termofizycznych dla stali 60S2A

Laber K., Dyja H.

Hutnik, Wiadomości Hutnicze

|

2003

|

Vol. 70, nr 11

431--434

PL

W pracy podjęto próbę scharakteryzowania podstawowych własności termofizycznych stali 60S2A w zależności od temperatury. W celu określenia rozkładu współczynnika przewodzenia ciepła X dla omawianej stali w zależności od temperatury sporządzono wykres, wykorzystując równanie drugiego stopnia. Współczynniki tego równania wyznaczono stosując zasady korelacji i regresji. Po analizie wpływu składu chemicznego na wartości ciepła właściwego CP stwierdzono, że do wyznaczenia wartości Cp dla stali 60S2A w zależności od temperatury można stosować omówione w pracy wzory lub korzystać z danych zamieszczonych w pracach [1, 8], W celu wyznaczenia gęstości p stali 60S2A w zależności od temperatury można wykorzystać omówioną w pracy zależność (12). Znajomość tych parametrów termofizycznych oraz ich rozkładu w materiale, w zależności od temperatury, ma szczególnie duże znaczenie przy analizowaniu wszelkiego rodzaju procesów przepływu ciepła.

EN

An attempt was made in this study to characterize the basic thermophysical properties of60S2A steel depending on temperature. In order to determine the distribution of the thermal conductivity, X, of the steel as a function of temperature, a diagram was made with the use of a quadratic equation. The coefficients of this equation were determined by using correlation and regression principles. Based on the analysis of the effect of chemical composition on the values of specific heat, Cp, it was concluded that in order to determine the values ofCp for 60S2A steel depending on temperature, either the formulas discussed in this paper, or data reported in works [1, 8] can be used. To determine the density, p, of60S2A steel as a function of temperature, relationship (12) discussed in the paper can be used. The knowledge of these thermophysical parameters and their distribution in the material, depending on temperature, is of particular importance in the analysis of any types of heat flow processes.