Measurements of the mechanical Barkhausen noise in ferromagnetic steels

Maciakowski P., Augustyniak B., Piotrowski L., Chmielewski M.

Prace Instytutu Elektrotechniki

2012

Z. 258

221-228

This paper presents a new technique for measuring the mechanical Barkhausen noise in ferromagnetic steels. We study the effect of tempering time of P91 grade steels on: parameters of mechanical Barkhausen noise, mechanical hardness and magnetic coercivity. All of these quantities are compared. The variations in amplitude of root mean square of mechanical Barkhausen noise for different tempering times are revealed to be greater than those of hardness and coercivity.

W pracy została opisana metoda badania mechanicznego efektu Barkhausena z wygorzystaniem drgań giętnych belki. Badany był wpływ czasu wygrzewania hartowanej stali P91 na: właściwości mechanicznego efektu Barkhausena, twardość mechaniczną oraz pole koercji. Stwierdzono, że amplituda obwiedni sygnału napięciowego mechanicznego efektu Barkhausena wzrasta wraz z czasem wygrzewania, natomiast twardość mechaniczna oraz pole koercji maleją. Natężenie mechanicznego efektu Barkhausena wykazuje największą dynamikę względnych zmian, co pokazuje, że jest to najczulsze narzędzie do oceny stanu wygrzewania stali P91.

Correlation between magneto-acoustic effect, mechanical properties and microstructure of 2Cr - 1Mo steel in service.

Augustyniak B., Piotrowski L., Chmielewski M., Głowacka M., Ćwiek J., Łabanowski J.

Inżynieria Materiałowa

2001

R. XXII, nr 4

185-188

Results of magneto-acoustic emission (MAE) measurements for 10H2M steel after service at power plant and at as-received stage are presented. Creep damage stage was evaluated from microstructure and mechanical properties (hardness HV, yield strength R0,2 and ultimate tensile strength Rm). It was revealed that MAE intensity decreases monotonically with creep damage stage degree and that relative change of MAE intensity is much higher than change of any other mechanical parameter. Such result reveals that MAE is very useful for evaluation of quality of ferrous steel.

Przedstawiono wyniki badań efektu emisji magnetoakustycznej stali 10H2M o różnym stopniu degradacji i w stanie dostawy. Stopień degradacji stali oceniono na podstawie zmian mikrostruktury i własności mechanicznych R0,2, Rm oraz HV. Stwierdzono, iż natężenie emisji magneto-mechanicznej zmniejsza się w sposób monotoniczny ze wzrostem stopnia degradacji, przy czym względna zmiana natężenia tego efektu znacznie przewyższa zmianę twardości a także zmianę R0,2 i Rm. Ten wynik dowodzi, iż zjawisko emisji magneto-akustycznej jest szczególnie przydatne dla oceny jakości stali ferromagnetycznych.