X-Ray Phase Analysis of Nitrided Layers of X2CrNiMo17-12-2 Austenitic Steel

Frączek T., Olejnik M., Pilarska M.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 3A

2005--2012

This work presents the results of diffraction analyses carried out using X-ray phase analyses (XRD and GIXRD) of nitrided layers of X2CrNiMo17-12-2 austenitic steel. Plasma nitriding process was c arried out in the temperature range of 325 ÷ 400 °C and time of 2 ÷ 4 h. Hydrogen-nitrogen plasma was used as reactive atmosphere (H2 75% + N2 25%) with pressure of 150 Pa. On the basis of the X-ray analyses it was stated that the obtained nitrided layers consisted of a subsurface layer of chromium nitrides and a zone of nitrogen saturated austenite.

W pracy zaprezentowano wyniki badań strukturalnych metodą rentgenowskiej analizy fazowej (XRD i GIXRD) warstw azotowanych na podłożu stali austenitycznej X2CrNiMo17-12-2. Proces azotowania jarzeniowego przeprowadzono w zakresie temperatur 325 ÷ 400 °C i czasu 2 ÷ 4 h. Atmosferę reaktywną stanowiła plazma wodorowo-azotowa (H2 75% + N2 25%) o ciśnieniu 150 Pa. Na podstawie badań rentgenowskich stwierdzono, że otrzymane warstwy azotowane składają się z przypowierzchniowej warstwy azotków chromu oraz strefy austenitu przesyconego azotem. Zastosowanie ekranu aktywnego spowodowało wzrost głębokości dyfuzji azotu w głąb azotowanej powierzchni oraz zwiększyło jego koncentrację w fazie austenitu przesyconego azotem.