Degradation of welded joint made of T91 steel with different additional materials

Wojsyk Kwiryn, Klimaszewska Klaudia, Golański Grzegorz

Welding Technology Review

|

2019

|

R. 91, nr 7

55--60

EN

The aim of the research was to analyse the processes of degradation observed in a similar welded joint of T91 steel. The analysis was performed for welded joints after long-term annealing for up to 8000 hours at the temperature of 600 °C. Microstructural analysis and hardness testing were performed. The purpose of the tests was to evaluate the effect of annealing time at the temperature of ageing on formation and properties of the decarburized zone in the inter-bead area of the welded joint. The study presents the results of physical examinations of the joint welded using two different filler materials (similar welded joint) after long-term effect of high temperature.

PL

Celem badań była analiza procesów degradacji obserwowanych w złączu spawanym ze stali T91. Analizę wykonano dla połączeń spawanych po długotrwałym wyżarzaniu do 8000 godzin w temperaturze 600°C. Przeprowadzono analizę mikrostrukturalną i badania twardości. Celem badań była ocena wpływu czasu wyżarzania w temperaturze starzenia na powstawanie i właściwości strefy odwęglonej w obszarze międzyściegowym złącza spawanego.

2

Struktura i właściwości mechaniczne złącza ze stali T91 z niskostopową warstwą graniową

Wojsyk K., Merda A., Cieślak E., Golański G.

Przegląd Spawalnictwa

|

2018

|

R. 90, nr 6

29--33

PL

W pracy przedstawiono wyniki badań metalograficznych złącza stali T91 spawanego dwoma materiałami dodatkowymi. Ścieg przetopowy wykonany był materiałem dodatkowym o składzie chemicznym zbliżonym do stali 10H2M, ścieg wypełniający materiał o składzie stali T/P91. Badane złącze poddane było obróbce cieplnej – wyżarzaniu 760 °C/2h. Badania nieniszczące i niszczące wykazały, że analizowane złącze spawane spełniało wymagania jakościowe na poziomie B oraz charakteryzowało się wymaganymi lub dostatecznymi właściwościami mechanicznymi. Badania strukturalne wykazały występowanie pomiędzy ściegiem graniowym a wypełniającym pojedynczej, o szerokości i długości rzędu kilku ziaren, strefy odwęglonej.

EN

The paper presents the results of metal science research of the T91 steel joint welded with two additional materials. The root pass was made with the additional material with its chemical composition similar to that of the 10H2M steel, and the fill pass was made with the material of the chemical composition of T/P91 steel. The examined joint was subject to heat treatment annealing 760 °C/2h. The non-destructive and the destructive tests proved that the investigated welded joint fulfilled the quality requirements at the B level and was characterised by the required or satisfactory mechanical properties. The structural tests showed the occurrence of a single decarburised zone, its width and length being of the order of several grains, between the root pass and the fill pass.

3

Strukturalne aspekty długotrwałej eksploatacji stali T91

Golański G., Zielińska-Lipiec A., Zieliński A., Urbańczyk P.

Energetyka

|

2015

|

nr 10

659--661

PL

Przedstawiono wyniki badań mikrostruktury stali X10CrMoVNb9-1 (T91) po około 105 000 godzin eksploatacji w temperaturze 540°C. Próbki do badań pobrane zostały z wężownicy przegrzewacza pary. Po eksploatacji badaną stal charakteryzowała listwowa budowa odpuszczonego martenzytu z stosunkową dużą gęstością dyslokacji oraz licznymi wydzieleniami. Długotrwała eksploatacja przyczyniła się głównie do wydzielenia międzymetalicznej fazy Lavesa oraz fazy Z. W stali w stanie poeksploatacyjnym obserwowano również procesy zdrowienia i poligonizacji osnowy oraz koagulacji i sferoidyzacji węglików M23C6 i fazy Lavesa.

EN

The paper presents the results of research on the microstructure of X10CrMoVNb9-1 (T91) steel after around 105 000 hours of service at the temperature of 540°C. The test sample for research were taken from a coil of a boiler superheater. After service, the examined steel was characterized by a retained lath microstructure of tempered martensite with quite large density of dislocations and numerous precipitations: M23C6 and MX precipitates. The service has mostly contributed to the precipitation of the Laves phase and the Z phase precipitations. Moreover, the processes of recovery and polygonization of the matrix, as well as coagulation and spheroidization of M23C6 carbides and Laves phase were observed.

4

Spawanie złączy doczołowych jedno- i różnoimiennych ze stali Tempaloy A-3

Jachym R., Kwieciński K., Łomozik M., Urzynicok M.

Przegląd Spawalnictwa

|

2012

|

R. 84, nr 4

45-51

PL

Dynamiczny rozwój stali stosowanych w energetyce na elementy kotłów o parametrach nadkrytycznych wywołuje nowe wyzwania spawalnicze. Wprowadzanie nowych kombinacji dodatków stopowych w celu osiągnięcia jak najlepszych właściwości mechanicznych, w tym odporności na pełzanie, nie pozostaje bez wpływu na spawalność nowych stali. Każda z nich musi przejść wiele prób, szczególnie w zakresie gięcia i spawania, żeby można było opracować technologie umożliwiające wykonanie oraz montaż instalacji kotłowych. Stale martenzytyczne o zawartości 9% Cr, przeznaczone na przegrzewacze pary, odznaczają się dobrą wytrzymałością na pełzanie i niską odpornością na utlenianie w temperaturze powyżej 600oC. Natomiast stale o zawartości 12% Cr charakteryzują się zdecydowanie lepszą odpornością na utlenianie, lecz ich wytrzymałość w podwyższonej temperaturze spada – stosowanie ich na elementy kotłów pracujących przy najwyższych parametrach jest ograniczone. Lukę między tymi stalami bardzo dobrze uzupełniają stale austenityczne, których wytrzymałość na pełzanie i odporność na utlenianie są niekwestionowane. W artykule zaprezentowano doświadczenia zdobyte podczas spawania połączeń jednorodnych stali Tempaloy A-3 oraz połączeń mieszanych stali Tempaloy A-3 ze stalą T91 z wykorzystaniem EPRI87.

EN

The dynamic development of steels used in the power industry for boiler elements with supercritical parameters results with new challenges in welding. Introduction of ever new combinations of alloying elements to achieve the best mechanical properties, including creep resistance, does not remain without effect on the weldability of new steel. Each of them has to go through many tests, especially when it comes to bending and welding so as to be able to develop technologies to enable seamless execution and installation of boilers. Martensitic steels containing 9% Cr, designed for steam superheaters, exhibit good creep resistance, while a low resistance to oxidation at temperatures above 600°C. Steels with 12% Cr have a much better resistance to oxidation, but unfortunately, their strength at elevated temperatures drop and hence their use for boiler components operating at the highest performance is limited. The gap between the above steels complement very well austenitic steels where creep and oxidation resistance are unquestionable. This article presents the experience gained during the welding of similar joints made of Tempaloy A-3, and dissimilar joints made of Tempaloy A-3 with T91 steel using EPRI87 material.