Wyniki wyszukiwania - BazTech

1

The influence of Cd-Zn coating and deformation velocity on mechanical properties of steel grade 45

Patejuk A., Gabrylewski M.

Archives of Metallurgy and Materials

|

2007

|

Vol. 52, iss. 1

93-96

EN

The work presents some researches about immediate strength in tensile test in a increasing temperature. It has been noticed that immediate strength of uncoated steel grade 45 is distinctly decreased after crossing the temperature 400°C. However, in case of steel grade 45 with two-ply Cd+Zn coating, clearly decrease of immediate strength is noticed just crossing the tensile temperature 320°C. Our investigations shows fundamental influence of latent crack on immediate strength of steel grade 45 in temperature range between 320–525 K. It was also noticed and ascertained that intensity of latent cracking process is a function of deformation velocity strain rate “ε” and this process is more intensified during diminution of deformation velocity (especially when ε< 2 10-3s-1). The results of our investigations on polycrystalline material (steel grade 45 with two-ply Cd+Zn coating) are the same as in literature where investigations were conducted on Zinc mono crystals. In both cases it was noticed that together with decrease of deformation velocity material is not plasticized. On the contrary, the fractography of testified steel samples by low deformation velocity, shows the symptoms of brittle scrap-metal. It can be noticed more than in other cases. The results of investigations conducted on polycrystalline samples with two-ply Cd+Zn coating did not confirm the expectations of latent cracking intensification connected with increasing of deformation velocity. This is also not confirmed that plastic properties of samples are decreasing. Whereas, during the investigations we got the coefficients of plasticity on constant level – A5 = 7–13%, Z = 2–8% in principle, and there are independent from deformation velocity.

PL

W artykule przedstawiono badania wytrzymałości doraźnej, w próbie rozciągania w podwyższonej temperaturze. Stwierdzono, że wytrzymałość doraźna stali 45 bez powłoki ochronnej obniża się wyraźnie po przekroczeniu temperatury rozciągania 400°C. Natomiast w wypadku stali 45 pokrytej dwuwarstwową powłoką Cd+Zn, istotny spadek wytrzymałości doraźnej odnotowuje się już przy temperaturach rozciągania przekraczających 320°C. W badaniach wykazano istotny wpływ utajonego pękania na wytrzymałość doraźną stali gat. 45 w zakresie temperatur 320–525 K. Stwierdzono również, że intensywność procesu utajonego pękania jest funkcją prędkości odkształcenia “ε”. Przy czym proces ten jest intensyfikowany w miarę spadku prędkości odkształcenia (szczególnie przy ε < 2 10-3s-1). Uzyskano pełną zbieżność wyników badań na polikrystalicznym materiale (stal gat. 45 z dwuwarstwowym pokryciem Cd+Zn) z wynikami badań przedstawianych w literaturze fachowej – prowadzonymi na monokryształach cynku. W obydwu przypadkach stwierdzono, że wraz ze spadkiem prędkości odkształcenia nie następowało uplastycznianie się materiału. Wręcz przeciwnie, fraktografia przełomu próbek stalowych testowanych przy niskich prędkościach odkształcania wykazywała nawet w większym stopniu przejawy złomu kruchego – w porównaniu z innymi. Wyniki badań na polikrystalicznych próbkach z dwuwarstwowym pokryciem Cd+Zn nie potwierdzają również tego, że należałoby oczekiwać nasilania się procesu utajonego pękania wraz ze wzrostem prędkości odkształcenia, a więc przede wszystkim spadku właściwości plastycznych. Natomiast podczas badań uzyskiwano wskaźniki plastyczności w zasadzie na stałym poziomie – A5 = 7–13%, Z = 2–8% niezależnym od prędkości odkształcenia.

2

Wpływ atmosfery i temperatury otoczenia węzła tarcia na zużycie stali 45

Witaszek M., Witaszek K.

Zeszyty Naukowe. Transport / Politechnika Śląska

|

2005

|

z. 57

443-449

PL

W artykule przedstawiono wyniki badań zużycia próbek wykonanych ze stali 45 nieobrobionej i obrobionej cieplnie. Badania przeprowadzono w układzie typu trzpień - tarcza, na stanowisku T-11. Umożliwia ono regulowanie temperatury otoczenia węzła tarcia i składu atmosfery tego otoczenia. Trzpienie wykonane ze stali 45 współpracowały z tarczami ze stali ŁH15. Nacisk i prędkość były stałe podczas badań. Zużycie trzpieni określano metodą wagową. Na podstawie wyników badań wyznaczono zależność intensywności zużycia próbek od temperatury otoczenia węzła tarcia przy tarciu w atmosferze powietrza i argonu.

EN

In this paper wear tests results of steel grade 45 have been presented. Some of the specimens were heat treated whereas other ones weren't. Tests were carried out on pin -on - disk wear testing machine type T -11, which enabled ambient temperature and atmosphere controlling. Pins, machined from steel grade 45 were run against disks from steel ŁH15. Load and velocity during tests were constant. Mass loss of pins was measured after each run. On the basis of test results, the influence of ambient temperature and atmosphere on wear rate of specimens has been determined.

3

Zużycie elementów ze stali 45 w warunkach tarcia suchego

Witaszek M., Witaszek K., Witaszek S.

Zeszyty Naukowe. Transport / Politechnika Śląska

|

2003

|

z. 50

35-42

PL

W pracy przedstawiono wyniki badań zużycia stali 45. Badania przeprowadzono na stanowisku trzpień - tarcza, przy suchym tarciu ślizgowym. Zużycie próbek określono dwiema metodami: za pomocą czujnika przemieszczenia i metodą wagową. W celu wyjaśnienia zagadnień związanych z mechanizmami zużycia przeprowadzono badania metalograficzne zużytych powierzchni ściernych elementów.

EN

This paper presents results of wear of 45 grade steel. These tests have been carried out on pin-on-disc machine in dry, sliding conditions. Two methods of wear determining have been used: with the aid of displacement and analytical balance. To highlight problems connected with wear mechanisms metallographic researches of worn surfaces have been carried out.

4

Zużycie tarciowe natlenionego i azotowanego powierzchniowo stopu TiA16V4 w parze trącej ze stalą 45

Zalisz Z., Hepner M., Król S.

Zeszyty Naukowe. Mechanika / Politechnika Opolska

|

2003

|

z. 76

311-316

5

Influence of loading program sequence on the course of the 45 steel stabilization process.

Mroziński S.

Archive of Mechanical Engineering

|

2003

|

Vol. L, nr 4

387-401

EN

Results and low-cycle fatigue tests analysis of 45 steel in conditions of block programmed loading with a different sequence of levels were presented in the paper. During tests four types of programs were applied: gradually increasing, gradually decreasing, gradually increasing and decreasing, and irregular. The sequence of levels in the block loading program was the parameter, which diversified the applied programs. The results of tests were analysed in the aspect of influence of loading program character on the course of the stabilization process. The analysis of the stabilization process was performed by comparing the stress loading amplitude for the chosen levels of the program in the following blocks. The hardening index was proposed as a description of the stabilization process. The comparative analysis showed similarity of the stabilization process both under the programmed and the constant-amplitude loading.

PL

W pracy zamieszczono wyniki oraz analizę niskocyklowych badań zmęczeniowych stali 45 w warunkach obciążeń programowanych blokowych o różnej sekwencji stopni. Podczas badań stosowano cztery typy programów: stopniowo narastające, stopniowo malejące, stopniowo rosnące a następnie malejące oraz obciążenia o nieregularnej kolejności stopni. Wyniki badań analizowano w aspekcie wpływu prostaci programu obciążenia na przebieg procesu stabilizacji. Analizę procesu stabilizacji prowadzono porównując amplitudę naprężenia dla wybranych stopni programu w kolejnych blokach. Do opisu procesu stabilizacji zaproponowano w pracy wskaźnik umocnienia. Analiza porównawcza wskaźnika uwidoczniła podobieństwo przebiegu procesu stabilizacji podczas obciążeń programowanych oraz stałoamplitudowych.

6

Investigations into the cutting properties of ceramic tools type TA-Z in face milling of steel 45.

Lubecka Elżbieta, Lubecki Paweł

Advances in Manufacturing Science and Technology

|

2001

|

Vol. 25, nr 3

51-59

EN

The paper presents results of the research on the cutting properties of ceramic tools (TA-Z) in face milling of steel 45. Roughness of the machined surface Ra and periodical cutting speed Vc15 were assumed to be the machinability rating for the tested tools. It was shown that ceramic tools type TA-Z have good cutting properties, which results in low surface roughness and high periodical cutting speed Vc15. The tools demonstrate good cutting properties also in the conditions of interrupted machining (face milling). No case of catastrophic failure was observed. The predominant mechanism of tool wear is the one of abrasive wear.

PL

W pracy przedstawiono wyniki badań właściwości skrawnych ostrzy ceramicznych gatunku TA-Z podczas frezowania czołowego stali 45. Za wskaźniki skrawalności badanych ostrzy przyjęto chropowatość powierzchni obrobionej, określonej parametrem Ra oraz okresową prędkość skrawania Vc15. Wykazano, że ostrza ceramiczne gatunku TA-Z mają dobre właściwości skrawne, umożliwiające osiąganie małej chropowatości powierzchni obrobionej i dużej wartości okresowej prędkości skrawania Vc15. Ostrza te mają dobre właściwości skrawne w warunkach obróbki przerywanej (frezowanie czołowe). W przeprowadzonych badaniach nie stwierdzono, żadnego przypadku katastroficznego zużycia ostrza. Dominującym mechanizmem zużycia ostrzy jest mechanizm zużycia ściernego.

7

Comparison analysis of low-cycle properties of 45 steel under uniaxial loading and bending.

Mroziński Stanisław

Archive of Mechanical Engineering

|

2000

|

Vol. XLVII, nr 2

105-117

EN

The paper presents comparative analysis of the results of low-cycle fatigue experiments on specimens made of 45 steel under uniaxial loading and bending. The analysis involves, among other things, the cyclic properties and the fatigue life of the specimens in a wide range of loading conditions. The experimental techniques used during bending enabled us to estimate the influence of strain distribution on fatigue life. The materials data obtained under the loading conditions mentioned above were employed to estimate the fatigue life of the structural elements. The results of experiments and calculations are presented in the form of fatigue curves. They also show the influence of axial loading and bending on the accuracy of the calculation.

PL

W pracy przedstawiono analizę porównawczą wyników niskocyklowych badań zmęczeniowych stali 45 w warunkach obciążenia osiowego i zginania. Przeprowadzona analiza obejmuje między innymi własności cykliczne oraz trwałość zmęczeniową w rozpatrywanych warunkach obciążenia. Metodyka badań przyjęta podczas zginania umożliwiła ponadto ocenę wpływu rozkładu odkształcenia na trwałość. Wyznaczone w rozpatrywanych warunkach obciążenia dane materiałowe wykorzystano do obliczeń trwałości zmęczeniowej elementów konstrukcyjnych. Wyniki badań i obliczeń przedstawiono w formie wykresów zmęczeniowych. Uzyskane rezultaty wskazują na wpływ źródła danych (obciążenie osiowe lub zginanie) na zgodność wyników obliczeń z wynikami badań.

8

On cavitation erosion resistance of the 45 and 2H13 steels remelted by laser beam and optical discharge plasma - a treatise on problems

Gireń B.G.

Metallurgy and Foundry Engineering

|

1998

|

T. 24, no. 2

115--125

EN

To make the first step towards resolving the problem of residual stresses influence on the cavitation resistance of materials, the samples of 0.45% carbon steel (steel 45) and 13% chromium steel (steel 2Cr13) were superficially processed by a cw CO2 laser beam and continuous optical discharge (COD) plasma. Afterwards, the workpieces were subjected to the process of cavitation erosion in a rotating disk facility. The tests were carried out on metals treated by COD plasma and/or laser beam featured by the same metallurgical structures but different distribution of residual stresses. The determination of the performance differences of fusion and heat affected zones, as well as the matrix region in laser beam treated and COD plasma treated samples during the incubation period of cavitation erosion, established a base for analysing the materials cavitation resistance as a function of its mechanical state. It was found for most cases that samples processed with the plasma gained better resistance against cavitation than the samples treated by a laser beam only.

PL

Próbki ze stali węglowej 45 i chromowej 2H13 poddano obróbce powierzchniowej za pomocą wiązki lasera cw CO2 i plazmy ciągłego wyładowania optycznego. Następnie próbki poddano procesowi kawitacji na stanowisku z wirującą tarczą. Celem pracy było rozpoznanie wpływu naprężeń wewnętrznych, powstających w wyniku przemian fazowych i zmian objętości materiału na odporność kawitacyjną badanych stali. W testowanych materiałach uzyskiwano - w wyniku obróbki plazmą i wiązką laserową - jednakową strukturę, lecz różny rozkład naprężeń wewnętrznych. Analizę zależności odporności kawitacyjnej badanych metali od ich stanu mechanicznego przeprowadzono na podstawie określenia rozwoju erozji w obszarze przetopionym, rdzeniu i strefie wpływu ciepła. Stwierdzono, że w większości przypadków próbki przetopione plazmą wyładowania optycznego uzyskują lepszą odporność na działanie kawitacji niż próbki obrobione samą wiązką laserową.