Gas nitrided layers on precipitation hardened stainless steel

Kochmański P., Baranowska J.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

324-327

This article presents results of research of nitrided layers on Sandvik NanoflexTM precipitation hardened stainless steel. Nitriding was conducted with gaseous method at temperature from range 450÷475°C. The layers were investigated with following methods: light microscopy, SEM, X-ray microanalysis WDS, XRD and GXRD, optical spectrometry GDOES, hardness measurements, corrosion potentiometric tests. Structure of the layers consists of S-phase, expanded martensite, presence of nitrides is possible as well. Results of corrosion tests performed in 3% NaCl water solution indicated, that corrosion resistance of nitrided layers and the untreated steel is comparable.

W artykule opisano wyniki badań warstw azotowanych na odpornej na korozję stali utwardzanej wydzieleniowo typu Sandvik NanoflexTM. Azotowanie gazowe prowadzono w temperaturze 450÷475°C. Otrzymane warstwy poddano badaniom metodami: mikroskopii świetlnej i elektronowej skaningowej, mikroanalizy rentgenowskiej WDS, rentgenografii strukturalnej, spektrometrii optycznej GDOES. Przeprowadzono również pomiary twardości i badania odporności korozyjnej metodą potencjometryczną. Struktura warstw złożona była z fazy S, expanded martensite, a także z azotków. Badania korozyjne prowadzone w wodnym 3% roztworze NaCl wskazują, że azotowanie nie pogarsza tej odporności w stosunku do materiału rdzenia.