The kinetics of high temperature degradation of thin chromium protective layers on valve steels

Drożdż M., Pawlak W., Grzesik Z.

Ochrona przed Korozją

2015

nr 7

254--257

The oxidation kinetics of four valve steels (X33CrNiMn23-8, X50CrMnNiNbN21-9, X53CrMnNiN20-8 and X55CrMnNiN20-8) covered by a sputter-deposited chromium layer with the thickness of 1 micrometer have been studied at 1173 K in air, using the microthermogravimetric technique. It has been found that coated steels show better oxidation resistance than uncoated ones. This phenomenon is a result of the formation of highly protective Cr2O3 scales on surfaces of coated materials. It has been also demonstrated that the better oxidation resistance of coated steels is observed during a much longer period of time than the lifetime of the chromium layers.

W pracy badano kinetykę izotermicznego utleniania w powietrzu czterech stali zaworowych (X33CrNiMn23-8, X50CrMnNiNbN21- 9, X53CrMnNiN20-8 i X55CrMnNiN20-8), pokrytych w procesie rozpylania jonowego warstwą chromu o grubości 1 mikrometra. Badania prowadzono metodą termograwimetryczną w temperaturze 1173 K. Stwierdzono, że stale z naniesioną warstwą chromu charakteryzują się większą odpornością na utlenianie niż stale nie poddane modyfikacji powierzchni. Rezultat ten jest wynikiem powstawania na modyfikowanych powierzchniowo stalach podczas procesu utleniania ochronnych warstw tlenku Cr2O3. Wykazano również, iż większa odporność na utlenianie modyfikowanych powierzchniowo stali trwa znacznie dłużej od okresu stabilności naniesionych warstw chromu.

Design of multi-layer sputter-deposited anode to reduce catalyst loading for liquid DMFC

Saito H., Nakashima T., Nakase K., Sudoh M.

Journal of Automation Mobile Robotics and Intelligent Systems

2009

Vol. 3, No. 4

175-178

Superior catalyst utilization of direct methanol fuel cells (DMFCs) may be obtained by localized catalyst loading on reaction sites. The objective of this work is to improve the catalyst utilization by multi-layer structure and reduction of loading catalyst. Multi-layer anode consisted of sputter-deposited Pt-Ru catalyst layer and the support layer of Nafion-carbon-Isopropanol ink (NCI). Single layer anode consisted of sputter-deposited Pt-Ru catalyst layer and the layer of carbon-glycerin ink (CG). Multi-layer (1~4 layers) and single-layer (0.04, 0.10 and 0.24 mg cm-2) were evaluated by using electrochemical measurement and SEM images. Three-layer anode provided 50.9 W g-1, 3.4 times as mass activity of conventional paste method anode. Methanol residues stripping voltammetry revealed that electrochemical surface area (ECSA) was increased with the number of layers. Additionally, single-layer anode (0.04 mg cm-2) provided over 150 W g-1. These results suggested that reduction of loading catalyst per unit layer and multilayer structure enhanced catalyst utilization.