Evaluation of Casting Shrinkage and Liquid Metal Fluidity of IN-713C Alloy

Binczyk F., Cieśla M., Gradoń P., Findziński A.

Archives of Foundry Engineering

|

2014

|

Vol. 14, iss. 1

9--12

EN

This paper presents the results of measurements of liquid metal fluidity and linear shrinkage of nickel alloy IN-713C in vacuum induction melting furnace Balzers VSG-2. Because of limited volume of the furnace chamber special models for technological trials were fluidity of hypoeutectic silumin, however in case of nickel superalloy the mould cavity was completely filled in each test because of high required pouring temperature. Positive results were obtained from the modified spiral test for all alloys used in the research. Relationship between the linear shrinkage for the test rod and a specific indicator of contraction defined on a spiral was observed.

2

Analiza wybranych właściwości technologicznych siluminu AlSi17Cu2NiMg.

Pucka G., Piątkowski J., Podolski P.

Inżynieria Materiałowa

|

2002

|

R. XXIII, nr 1

29-34

PL

W pracy przedstawiono wyniki badań swobodnego skurczu liniowego oraz lejności nowo opracowanego siluminu AlSi17 z dodatkiem Cu, Ni i Mg. Metodą ATSD (analizy różniczkowej równocześnie rejestrowanych krzywych stygnięcia i swobodnego skurczu liniowego) uzyskano jakościowe i ilościowe wartości temperatury i skurczu w zależności od średnicy próbki. Wykazano, iż zmniejszenie intensywności stygnięcia powoduje zwiększenie całkowitego skurczu liniowego oraz rozszerzenia przedskurczowego. Temperatura maksymalnego rozszerzenia przedskurczowego (równoznaczna z temperaturą początku skurczu liniowego) zawsze mieści się w zakresie krzepnięcia stopu. Przejściu od temperatury początku skurczu liniowego do temperatury Tsol towarzyszy największy przyrost prędkości skurczu liniowego. Lejność siluminu AlSi17Cu2NiMg określono na podstawie długości zalanego kanału w próbie spiralnej. Wykazano związek pomiędzy temperaturą odlewania a lejnością oraz prędkością przepływu czoła strugi w tym kanale dla badanego siluminu. Ponadto określono zakres temperatury, dla którego lejność jest największa. Stwierdzono, że przegrzanie stopu nie zawsze prowadzi do polepszenia lejności.

EN

The work presents the results of free linear contraction and pourability measurements of the newly developed AlSi117 silumin with the addition of Cu, Ni and Mg. Using of ATSD method (a differential analysis of simultaneously recorded cool-down curves and free linear contraction) qualitative and quantitative values of temperature and contraction depending on the sample diameter have been obtained. It has been proved that a decrease of cool-dawn intensity causes an increase of the total linear contraction and pre-contraction expansion. The temperature of the maximum pre-contraction expansion (tantamount to the linear contraction starting points) was always kept within the range of solidification of the alloy. The transition from linear contraction initial point to the Tsol temperature is accompanied by the greatest increase of linear contraction rate. The pourability of AlSi17Cu2NiMg silumin has been determined on the basis of length of the filled passage of a spiral test piece. Relationships between the pouring temperature and pourability and velocity of the stream flow in the passage were found. Besides, the temperature range for with the pourability reaches the greatest value has been determined. It has been found out that the overheating of alloy does not always lead to improvement of pourability.

3

Wpływ temperatury odlewania na intensywność przepływu stopów Al-Si w kanale próby spiralnej

Binczyk F., Piątkowski J., Smoliński A.

Krzepnięcie Metali i Stopów

|

1999

|

R. 1, nr 40

269--273

PL

Lejność jest jedną z podstawowych własności technologicznych istotnie wpływających na uzyskanie odlewów bez wad. Dla siluminów duże znaczenie ma temperatura przegrzania ciekłego metalu. Badania wstępne wskazują iż istnieje związek pomiędzy temperaturą odlewania a przebiegiem procesu przepływu stopu w kanale próby spiralnej. W pracy przedstawiono wyniki badań nad wpływem temperatury odlewania siluminów: AK11 i AK 20 na szybkość przepływu czołówki strugi metalu w kanale próby spiralnej. W określonych odcinkach spirali dokonano pomiaru temperatury metodą jednoczesnej analizy termicznej krzywych ATD i DTA, z których obliczono czasy przepływu czoła strugi stopu oraz charakterystyczne temperatury krzepnięcia i przechłodzenia.