Microstructural Changes in a High-Manganese Austenitic Fe-Mn-Al-C Steel

Witkowska M., Zielińska-Lipiec A., Kowalska J., Ratuszek W.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 3

971--975

EN

Microstructural changes in the age-hardenable Fe-28wt.%Mn-9wt.%Al-1wt.%C steel during ageing at 550°C for various times have been investigated by transmission electron microscopy (TEM) and X-ray diffraction (XRD). The steel was produced in an induction furnace and the ingot, after homogenization at 1150°C for 3 hours under a protective argon atmosphere, was hot-rolled and subsequently cold-rolled up to 23% reduction. The sheet was then aged at 550°C for various times in an argon atmosphere and cooled in air. XRD analysis and TEM observations revealed a modulated structure and superlattice reflections produced by spinodal decomposition, which occurred during ageing at 550°C. Theexistence of satellites suggests that either (Fe, Mn)3AlCx carbides were formed within the austenite matrix by spinodal decomposition during cooling or chemical fluctuactions occurred between the (Fe, Mn)3AlCx carbides and the austenitic matrix.

PL

W pracy analizowano zmiany mikrostruktury w stali Fe-28%wt. Mn-9%wt. Al-1%wt.C zachodzące podczas starzenia w temperaturze 550°C w różnych czasach. Stal Fe-28Mn-9Al-1C wytopiono w próżniowym piecu indukcyjnym. Po odlaniu wlewek homogenizowano w temperaturze 1150°C przez 3 godziny w atmosferze argonu. Wlewek walcowano na gorąco a następnie na zimno do 23 % odkształcenia. Próbki po odkształceniu starzono w temperaturze 550°C dla różnych czasów w atmosferze argonu i chłodzono na powietrzu. Obserwacje elektronomikroskopowe starzonej stali Fe-28Mn-9Al-1C ujawniły modulowaną strukturę i refleksy od nadstruktury, co było efektem rozpadu spinodalnego, który miał miejsce podczas procesu starzenia. Występowanie satelitów na zapisach dyfrakcyjnych sugeruje, że węgliki (Fe, Mn)3AlCx powstały w osnowie austenitycznej na skutek rozpadu spinodalnego zachodzącego podczas chłodzenia czy fluktuacji chemicznych występujących pomiędzy węglikami Fe, Mn)3AlCx i osnową austenityczną.

2

Struktura i właściwości spiekanych magnesów Alnico 8

Stanek A., Jezierska E., Wierzbicki Ł., Leonowicz M.

Inżynieria Materiałowa

|

2010

|

Vol. 31, nr 2

109-114

PL

Zbadano warunki wytwarzania spiekanych magnesów Alnico 8. Dla przyjętego składu chemicznego dobrano parametry prasowania i spiekania. Średnia gęstość po spiekaniu w temperaturze 1300°C wynosiła 6,83 g/cm3, a skurcz liniowy po średnicy i wysokości, wyniosły odpowiednio 9 i 11%. Stwierdzono, że magnesy wykazują strukturę modulowaną, złożoną z koherentnych faz o sieci RPC, o zróżnicowanych właściwościach ferromagnetycznych oraz z niewielkiej ilości fazy paramagnetycznej. Jedna z nich jest bogatsza w żelazo i kobalt, druga zaś w aluminium i nikiel. Mikrostruktura ma formę szachownicy, utworzonej przez cząstki o boku ok. 32 nm. Parametry magnetyczne są powtarzalne, a ich średnie wartości wynoszą: koercja H c = 131 kA/m, remanencja B r = 0,7 T, maksymalny iloczyn energii magnetycznej (BH)max = 35 kJ/m3, temperatura Curie Tc = 890°C.

EN

Effect of the processing variables on the structure, microstructure and properties of sintered Alnico 8 magnets was studied. Optimal sintering conditions were evaluated. It was found that the mean density after sintering at 1300°C was 6.83 g/cm3, and their transversal and longitudinal shrinkages were 9 and 11%, respectively. The magnets exhibited modulated structure, consisting of two coherent BCC phases having various magnetic properties and of small amount of the paramagnetic phase. One of the ferromagnetic phases was enriched in iron and cobalt, the second one in aluminum and nickel. Microstructure of the magnets had a chessboard form with a mean side length 32 nm. The magnetic properties were reproducible and their mean values were: coercivity H c = 131 kA/m, remanence B r = 0.7 T, maximum energy produkt (BH)max = 35 kJ/m3 and Curie temperature Tc = 890°C.

3

Application of the Euler characteristic to the study of homopolymer blends and copolymer melts

Aksimentiev A., Hołyst R.

Polimery

|

2001

|

T. 46, nr 5

307-323

EN

The Euler characteristic is applied to study the phase separation/ordering phenomena occurring in polymer mixtures. Several methods used to compute Euler characteristics are described and discussed in terms of accuracy and efficiency. A novel, robust and exact algorithm based on simplex decomposition is presented. The simulated morphology of spinodal decomposition and the phase equilibrium diagram of gradient copolymers are analyzed in terms of Euler characteristics. Again, the Euler characteristics are applied to specify the connectivity of bicontinuous patterns, to distinguish the disperse and the bicontinuous morphologies, and to detect the percolation transition. During the spinodal decomposition, the dynamic transformation between the bicontinuous and the droplet patterns is shown to involve the formation of a transient "cylindrical" morphology.

PL

Opisano metody badania kinetyki przemian fazowych za pomocą charakterystyki Eulera. Metody te zastosowano do zbadania rozpadu spinodalnego (procesu separacji faz) w dwuskładnikowej mieszaninie homopolimerów oraz do omówienia diagramu fazowego kopolimerów gradientowych. Charakterystykę Eulera wykorzystano do opisania dwuciągłej morfologii i jej przejścia w morfologię kropelkową w procesie separacji faz oraz do określenia stopnia połączenia domen powstających w tym procesie. Stwierdzono, że w procesie separacji faz struktura dwuciągła może rozpaść się na cylindryczne domeny, które w dalszej ewolucji przybierają kształt sferyczny. Omówiono także kilka metod numerycznego obliczania charakterystyki Eulera oraz przedstawiono nowy ścisły algorytm jej obliczania.

4

Thermo-mechanical processing of the CuNi30Cr3Mn alloy with spinodal decomposition.

Ciura L.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 4

263-266

EN

The study of structural transformations taking place during ageing of the CuNi30Cr3 alloy was carried out showing a close relationship between precipitation morphology in the successive stages of the solid solution decomposition and the mechanical properties. The highest growth of the mechanical properties and hardness has been achieved by spinodal decomposition resulting in the formation of a modulated structure. Based on the laboratory tests, a flowsheet for an alternate use of cold working and heat treatment in order to obtain materials of a lamellar structure has been developed. This alternate use of cold working and heat treatment makes that the material gets high strength and hardness at good plasticity, whereas the accompanying structural changes lead to the gradual creation of a lamellar structure. It has been proved that the primary segregation, location of the deformation in the shear bands, privileged nucleation and growth of the particles of the second phase within the shear bands play a decisive role in the process of the creation of the lamellar structure.

PL

Przeprowadzone badania strukturalne przemian zachodzących podczas starzenia stopu CuNi30Cr3 wykazały ścisłą zależność pomiędzy morfologią wydzielania w kolejnych stadiach rozpadu roztworu stałego, a własnościami mechanicznymi. Najwyższy wzrost zespołu własności wytrzymałościowych i trwałości uzyskano w wyniku rozpadu spinodalnego powodującego powstanie struktury modulowanej. Na podstawie przeprowadzonych badań i prób laboratoryjnych opracowano schemat przemiennego stosowania przeróbki plastycznej na zimno i obróbki cieplnej dla uzyskania materiałów o strukturze warstwowej. Przemienne zastosowanie przeróbki plastycznej na zimno i obróbki cieplnej zgodnie z opracowanym schematem prowadzi do uzyskania przez materiał wysokiego poziomu własności wytrzymałościowych i twardości przy dobrej plastyczności, zaś zmiany struktury stopu towarzyszące przemiennemu stosowaniu tych operacji prowadzą do stopniowego tworzenia struktury warstwowej. Wykazano, że decydujący udział w powstawaniu struktury warstwowej ma pierwotna segregacja, lokalizacja odkształcenia w pasmach ścinania, uprzywilejowane zarodkowanie i wzrost cząstek drugiej fazy w obszarze pasm ścinania.