Effect of Temperature on the Structure and Mechanical Properties of Mechanically Alloyed Al-NiO Composite

Zygmunt-Kiper M., Blaz L, Sugamata M.

Archives of Metallurgy and Materials

2014

Vol. 59, iss. 1

121--126

Mechanical alloying of high-purity aluminum and 10 wt.% NiO powders combined with powder vacuum compression and following hot extrusion method was used to produce an Al-NiO composite. Mechanical properties of as-extruded materials as well as the samples annealed at 823 K /6 h, were tested by compression at 293 K - 770 K. High mechanical properties of the material were attributed to the highly refined structure of the samples. It was found that the structure morphology was practically not changed during hot-compression tests. Therefore, the effect of deformation temperature on the hardness of as-deformed samples was very limited. The annealing of samples at 823 K/6 h induced a chemical reaction between NiO-particles and surrounding aluminum matrix. As a result, the development of very fine aluminum oxide and Al3Ni grains was observed.

Kompozyt na osnowie aluminium zawierający dodatek 10% mas. NiO wytworzono metodą mechanicznej syntezy stosując mielenie proszków aluminium i tlenku niklu oraz mechaniczną konsolidację uzyskanego proszku metodą prasowania próżnio- wego i wyciskania w temperaturze 673 K Własności mechaniczne uzyskanego kompozytu, jak również próbek wyżarzonych w 773 K/6 godz., badano w zakresie 293 K-770 K w próbie ściskania. Badania strukturalne wykazały silne rozdrobnienie skład- ników strukturalnych zarówno w materiale wyciskanym, jak również w próbkach wyżarzonych, co jest przyczyną wysokich własności mechanicznych uzyskanego kompojrytu. W przypadku próbek odkształcanych „na gorąco” praktycznie nie obserwuje się istotnych zmian morfologii struktury. Jednakże wyżarzanie w 823 K/6 godz. spowodowało zmiany strukturalne wywołane reakcją chemiczną między cząstkami NiO a osnową, której skutkiem było utworzenie silnie dyspersyjnych wydzieleń tlenku aluminium i ziam fezy międzymetalicznej typu AI3Ni.

Effect of Magnesium Addition on Properties of Al-Based Composite Reinforced with Fine NiO Particles

Zygmunt-Kiper M., Błaż L., Sugamata M.

Archives of Metallurgy and Materials

2014

Vol. 59, iss. 2

431--435

An Al(Mg)-NiO composite was manufactured using combined mechanical alloying (MA) and powder consolidation methods that yielded well-consolidated and very-fine grained bulk material. Compression tests at 293 K – 773 K revealed high mechanical properties of the material. Preliminary annealing at 823 K/6 h was found to result in the flow stress reduction at 573 K – 773 K. However, the effect of preliminary annealing on the flow stress value was relatively low for Al(Mg)-NiO if comparing to similar tests performed for the Al-NiO composite. Structural observations revealed very-fine grained structure of both as-extruded and annealed Al(Mg)-NiO composites. The chemical reaction between the composite matrix and reinforcements (NiO) at sufficiently high temperatures resulted in fine grains and spinel-type particles’ development. With respect to the similarly produced Al-NiO composite, a magnesium addition was found to intensify chemical reaction between Al(Mg)-based matrix and NiO particles. As result, fine Al3Ni particles were observed in both hot-extruded material and Al(Mg)-NiO samples annealed at 823 K/6 h.

Kompozyt Al(Mg)-NiO wytworzono metodą mechanicznej syntezy stosując mielenie składników proszkowych i mechaniczną konsolidację uzyskanego proszku kompozytowego w procesie prasowania próżniowego i wyciskania „na gorąco”. Uzyskano jednorodny materiał charakteryzujący się dużym rozdrobnieniem składników strukturalnych. Próby ściskania w temperaturze 293 K – 773 K wykazały wysokie własności mechaniczne kompozytu. Wyżarzanie próbek w 823 K / 6 godz. spowodowało nieznaczne obniżenie wartości naprężenia uplastyczniającego w zakresie 573 K – 773 K, jednakże w znacznie mniejszym stopniu niż w porównywanym przypadku kompozytu nie zawierającego dodatku magnezu (Al-NiO), który opisano we wcześniejszej pracy. Obserwacje struktury wyjściowych próbek kompozytowych i próbek wyżarzonych w 823 K / 6 godz. wykazały zmiany strukturalne wywołane reakcją chemiczną między osnową kompozytu (Al-Mg) a dyspersyjnymi cząstkami zbrojenia (NiO), której skutkiem jest utworzenie silnie dyspersyjnych wydzieleń tlenków typu spinelu, oraz submikronowych ziarn typu Al3Ni. W porównaniu z kompozytem Al-NiO, dodatek magnezu powoduje zwiększenie szybkości reakcji chemicznej, która przejawia się utworzeniem ziarn fazy międzymetalicznej Al3Ni zarówno w materiale wyjściowym – wyciskanym „na gorąco” – jak również w próbkach wyżarzonych w 823 K / 6 godz.