Effect of Soft Annealing Treatment on Impact Strength and Hardness of the EN AC-AlSi11 Alloy

Jarko A.

Archives of Foundry Engineering

|

2017

|

Vol. 17, iss. 3

55--58

EN

The paper presents research on the effects of soft annealing parameters on a change of the impact strength KC and Brinell hardness (HB) of the EN AC-AlSi11 alloy. The research has been performed according to the trivalent testing plan for two input parameters – temperature in the range between 280°C and 370°C and time in the range between 2 and 8 hours. The application of such heat treatment improves the plasticity of the investigated alloy. The improvement of the impact strength KC by 71% and the decrease of the hardness HB by 20% was achieved for the soft annealing treatment conducted at a temperature 370°C for 8 hours, compared to the alloy without the heat treatment. A change of the form of eutectic silicon precipitations which underwent refinement, coagulation and partial rounding, had a direct effect on the hardness HB and impact strength KC. The results obtained were used to prepare space plots enabling the temperature and time for soft annealing treatment to be selected with reference to the obtained impact strength KC and hardness HB of the alloy with the heat treatment.

2

Poprawa plastyczności stopu AlSi11 przez zastosowanie wyżarzania zmiękczającego

Jarco A.

Prace Instytutu Odlewnictwa

|

2016

|

Vol. 56, no. 3

261--266

PL

W artykule przedstawiono badania dotyczące możliwości zwiększenia plastyczności okołoeutektycznego stopu AlSi11 przez zastosowanie wyżarzania zmiękczającego. Dla dwóch przyjętych wielkości wejściowych, tj. temperatury i czasu wygrzewania, w oparciu o trójwartościowy plan przeprowadzono badania pozwalające na przedstawienie zmian wytrzymałości na rozciąganie (Rm) oraz wydłużenia (A5) w zależności od parametrów wyżarzania zmiękczającego (temperatury z przedziału 280°C do 370°C i czasu od 2 godzin do 8 godzin). Dla średnich wartości z przyjętych zakresów temperatury i czasu uzyskano wzrost wydłużenia A5 o około 40% w odniesieniu do wartości wyjściowej. Największy wzrost A5 wyniósł 96%, w porównaniu do stopu wyjściowego, dla wygrzewania w temperaturze 370°C przez 8 godzin, równocześnie nieznacznie spadła wytrzymałość Rm, w granicach 15%.

EN

The paper presents research on the possibility of improving the plasticity of near-eutectic AlSi11 alloy by the use of soft annealing treatment. For two assumed input quantities, i.e. temperature and duration of the soaking treatment, based on the trivalent testing plan, have enabled the presentation of changing tensile strength (Rm) and elongation (A5) in function of the soft annealing parameters (temperature in the range from 280°C to 370°C and time from 2 hours to 8 hours). For average values of assumed range of temperature and time there was an increase in elongation (A5) of about 40% compared to the starting value. The highest increase in elongation (A5) amounted to 96%, compared to the initial alloy, which was obtained in the case of the soaking treatment at temperature 370°C for 8 hours, the tensile strength (Rm) decreased simultaneously within limits of 15%.

3

Wpływ rozciągania z jednoczesnym skręcaniem na otrzymanie struktury kulistego perlitu

Kulakovska G., Gwoździk M., Nitkiewicz Z., Pashynska O.

Hutnik, Wiadomości Hutnicze

|

2014

|

Vol. 81, nr 5

314--317

PL

W artykule przedstawiono wyniki obserwacji mikroskopowych prętów ze stali podeutektoidalnej. Pręty zostały przygotowane według następujących wariantów: I stan wyjściowy; II stan wyjściowy + wyżarzanie zupełne; III stan wyjściowy + odkształcenie plastyczne (skręcanie z jednoczesnym rozciąganiem); IV stan wyjściowy + wyżarzanie zupełne, odkształcenie plastyczne (skręcanie z jednoczesnym rozciąganiem); V stan wyjściowy + wyżarzanie sferoidyzujące; VI stan wyjściowy + odkształcenie plastyczne + wyżarzanie sferoidyzujące; VII stan wyjściowy + wyżarzanie zupełne, odkształcenie plastyczne (skręcanie z jednoczesnym rozciąganiem) + wyżarzanie sferoidyzujące. Celem badań było określenie wpływu rozciągania z jednoczesnym skręcaniem z następnym wyżarzaniem zmiękczającym na stan struktury.

EN

This article presents the results of the microscopic observation of wire made from carbon steel. Wires were prepared according to the following variants: I the initial state; II the initial state + annealing; III the initial state + stretching deformation (turning with stretching deformation); IV the initial state + annealing + stretching deformation (turning with stretching deformation); V the initial state + soft annealing; VI the initial state + plastic deformation + soft annealing; VII the initial state + annealing + stretching deformation (turning with stretching deformation) + soft annealing. The goal of the research was to determine the effect of turning with stretching deformation with next soft annealing for structure of steel.

4

Analysis of the High Chromium Cast Iron Microstructure after the Heat Treatment

Kopyciński D., Guzik E., Siekaniec D., Szczęsny A.

Archives of Foundry Engineering

|

2014

|

Vol. 14, iss. 3

43--46

EN

The article presents results of heat treatment on the high chromium cast iron. The study was carrying out on samples cut from the casting made from chromium cast iron. Those were hardened at different temperatures, then tempered and soft annealed. The heat treatment was performed in a laboratory chamber furnace in the Department of Engineering Alloys and Composites at Faculty of Foundry Engineering AGH. At each stage of the heat treatment the hardness was measured by Vickers and Rockwell methods, and the microscope images were done. Additionally based on images from the optical microscope the microstructure was assessed. Based on these results, the effect of hardening, tempering and soft annealing on the microstructure and hardness of high chromium cast iron was studied. Next the effects of different hardening temperatures on the properties of high chromium cast iron were compared. The study led to systemize the literature data of the parameters of heat treatment of high chromium cast iron, and optimal conditions for heat treatment was proposed for casts of similar properties and parameters.

5

Modelling of casting, hot-charge rolling and cold-strip production from high-carbon steel

Schindler I., Kozelsky P, Kulveitova H., Cizek L., Rusz S., Marek M., Kubina T., Sojka J., Svinc V., Cerny L.

Archives of Civil and Mechanical Engineering

|

2004

|

Vol. 4, no 3

103-113

EN

Structure development of steel with 0.62 wt. % C during its laboratory casting, conventional as well as hot-charge rolling, cold-strip rolling and soft annealing in controlled atmosphere was studied. Effect of changes of processing parameters on final mechanical properties of a strip was determined. It was confirmed that microstructure and properties of strip produced by the effective and energy-saving hotcharge rolling could be more beneficial than after conventional rolling. Grain size seems to be more intensively effected by cooling rate and heating time of the casting than by phase transformations occurred before conventional rolling. As to final mechanical properties of thin strip from the steel applied, the ferrite fraction in the hot-rolled microstructure plays a key role. Due to higher ferrite content resulting from the finer austenite grain size, samples obtained after laboratory remelting and casting are characterized by lower yield stress and strength, together with higher ductility, which should be advantageous for subsequent processing of real strips in question.

PL

Badano rozwój struktury stali z zawartością węgla 0.62% podczas laboratoryjnego odlewania, walcowania konwencjonalnego i walcowania z jednoczesnym nagrzewaniem, walcowania taśmy na zimno oraz wyżarzania w atmosferze definiowanej. Ustalono, jak zmiany parametrów obróbki wpływają na końcowe właściwości mechaniczne. Stwierdzono, że mikrostruktura oraz właściwości taśmy produkowanej metodą efektywnego oraz energooszczędnego walcowania z jednoczesnym nagrzewaniem mogą być korzystniejsze niż po walcowaniu konwencjonalnym. Na wielkość ziarna prawdopodobnie znacznie silniej wpływa szybkość ochładzania podczas odlewania i czas nagrzewania niż transformacje fazowe poprzedzające walcowanie konwencjonalne. Zasadniczy wpływ na mechaniczne właściwości końcowe cienkiej taśmy z badanej stali ma frakcja ferrytyczna zawarta w mikrostrukturze walcowanej na gorąco. Z powodu większej zawartości ferrytu, wynikającej z drobnoziarnistej struktury austenitycznej, próbki uzyskane w trakcie laboratoryjnego przetapiania i odlewania charakteryzuje niższa granica sprężystości i wytrzymałości oraz większa sprężystość, co powinno być zaletą w obróbce wspominanych taśm.

6

Wpływ mechanicznej aktywacji powierzchni stali 4H13 na chropowatość po azotowaniu jonowym i gazowym

Jasiński J., Wojtal A., Jeziorski L., Radecki A., Ucieklak S.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 6

501-504

PL

W pracy przedstawiono problem aktywacji cieplnej i mechanicznej powierzchni stali 4H13 na stan warstwy wierzchniej azotowanej jonowo i gazowo. W celu określenia wpływu azotowania i dokonania analizy wyników stal poddano wyżarzaniu zmiękczającemu oraz hartowaniu z odpuszczaniem w T=550 stopni Celsjusza, a także aktywacji mechanicznej powierzchni, polegającej na szlifowaniu obwodowym na papierach ściernych o numerach uziarnienia: 60, 360, 1000 i polerowaniu mechanicznym. Głównym celem poznawczym pracy było ustalenie wpływu różnej struktury geometrycznej powierzchni w zależności od struktury stali 4H13 na profil chropowatości po azotowaniu jonowym i gazowym. W związku z tym przeprowadzono badania podstawowych parametrów chropowatości przed i po procesach cieplno-chemicznych oraz analizę utylitarnej przydatności zastosowanych aktywacji.

EN

The article describes the problem of the thermal and mechanical activation of the surface of the X40Cr13 steel on the state of the ion and gas nitriding. In order to determine the nitriding influence and make the analysis of results, the steel was subjected to: soft annealing, hardening with subsequent tempering at T=550 degrees centigrade and also mechanical activation of the surface consisting in peripheral grinding with abrasive papers of the grain-size numbers: 60, 360, 1000 and mechanical polishing. The main aim of this work was to establish the influence of different surface geometrical structure, depending on X40Cr13 steel structure, on the roughness profile after ion and gas nitriding. With regard to the above, the examinations of basic roughness parameters prior to and after thermochemical processes and the analysis of utilitarian usefulness of activations applied were carried out.