Wyniki wyszukiwania - BazTech

1

The effect of particle size on the mechanical properties of Alkali Activated Steel Slag Mortar

Ing Doh Shu, Ho Chia Min, Xiaofeng Li, Jaya Ramadhansyah Putra, Abdullah Mohd Mustafa Al Bakri, Chin Siew Choo, Rahim Nur Liza, Nabiałek Marcin

Archives of Civil Engineering

|

2022

|

Vol. 68, nr 2

51--61

EN

With the rapid development of industry, abundant industrial waste has resulted in escalating environmental issue. Steel slag is the by-product of steel-making and can be used as cementitious materials in construction. However, the low activity of steel slag limits its utilization. Much investigation has been conducted on steel slag, while only a fraction of the investigation focuses on the effect of steel slag particle size on the properties of mortar. The aim of this study is to investigate the effect of steel slag particle size as cement replacement on properties of steel slag mortar activated by sodium sulphate (Na2SO4). In this study, two types of steel slag, classified as fine steel slag (FSS) with particle sizes of 0.075 mm and coarse steel slag (CSS) with particle sizes of 0.150 mm, were used for making alkali activated steel slag (AASS) mortar. Flow table test, compressive strength test, flexural strength test and UPV test were carried out by designing and producing AASS mortar cubes of (50x50x50) mm at 0,10%, 20% and 30% replacement ratio and at 0.85% addition of Na2SO4. The results show that the AASS mortar with FSS possess a relatively good strength in AASS mortar. AASS mortar with FSS which is relatively finer shows a higher compressive strength than CSS up to 38.0% with replacement ratio from 10% to 30%. This study provided the further investigation on the combined influence of replacement ratio and particle size of SS in the properties of fresh and hardened AASS.

2

Bezodpadowa metoda przerobu siarczanu(VI) sodu na kwas siarkowy(VI) i wodorotlenek sodu

Pisarska B., Mikołajczak W., Jaroszek H., Dylewski R., Kwiecień J., Nowak M.

Przemysł Chemiczny

|

2017

|

T. 96, nr 3

639--643

PL

Przedstawiono wyniki badań przerobu siarczanu(VI) sodu metodą elektro-elektrodializy (EED). Określono stopień przereagowania siarczanu(VI) sodu w procesie EED (obniżenie stężenia SO₄²⁻ do ok. 20 g/dm³), po przekroczeniu którego następuje znaczne pogorszenie wskaźników (napięcia zaciskowego, jednostkowego zużycia energii elektrycznej). Przedstawiono koncepcję kombinowanego procesu obejmującego zatężanie rozcieńczonych roztworów siarczanu(VI) sodu i ich przerób metodą EED. W tym kombinowanym procesie (NF + EED) otrzymuje się wartościowe produkty: roztwory wodorotlenku sodu i kwasu siarkowego(VI) oraz permeat o jakości wody przemysłowej, natomiast nie powstają w nim żadne odpady ciekłe.

EN

The waste aq. solns. of Na₂SO₄ were processed by electro-electrodialysis under constant current d. of 7.5 A/dm². The SO₄²⁻ ions concns. in chambers of the apparatus were detd. by conductometry on the samples. The decreasing of the SO₄²⁻ concn. in the dialyzate down to below 20 g/dm³ resulted in an adverse large increase of the cell voltage and unit power consumption. A nanofiltration of dialyzate and its recycling was redommended.

3

Wpływ zawartości soli na pozorną wartość współczynnika przewodzenia ciepła cegły ceramicznej

Bednarska D., Koniorczyk M.

Materiały Budowlane

|

2017

|

nr 5

112--114

PL

W artykule przedstawiono wyniki badań zależności pozornej wartości współczynnika przewodzenia ciepła λ cegły pełnej od stopnia nasycenia wodą oraz roztworem siarczanu sodu. Badania przeprowadzono metodą stacjonarnego przepływu ciepła w przypadku następujących stopni nasycenia: 25, 50, 75, 100%. Wyniki eksperymentu potwierdzają negatywny wpływ wilgoci na przewodność cieplną materiału. Wartość współczynnika przewodzenia ciepła λ rośnie wraz ze wzrostem stopnia nasycenia materiału wodą lub roztworem soli. Zaobserwowano, iż obecność roztworu Na2SO4 oraz kryształów dziesięciowodnego siarczanu sodu ma mniej negatywny wpływ na przewodność cieplną badanych próbek niż obecność czystej wody.

EN

This paper presents the experimental results concerning the relation between the apparent thermal conductivity coefficient of brick and its water or Na2SO4 solution content. The research is conducted using stationary technique for the dry specimens, as well as the ones containing 25%, 50%, 75% and 100% water or sodium sulphate solution. The experimental results confirm the negative influence of water or sodium sulphate solution on the thermal properties of material. The study shows that the presence of Na2SO4 solution mitigate the negative influence on brick’s thermal conductivity coefficient.

4

Wpływ siarczanu sodu i magnezu na trwałość betonów z kruszywem węglanowym

Dębska D.

Przegląd Budowlany

|

2014

|

R. 85, nr 5

14--17

PL

Spośród kruszyw węglanowych, jedynie kruszywa dolomitowe poddane działaniu środowiska ciekłego mogą ulegać rozkładowi z wytworzeniem pęczniejących wodorotlenków wapnia i magnezu. Na przebieg procesów rozkładu kruszyw dolomitowych może znacząco wpływać obecność jonów Na+, Mg2+ i SO4 2– w środowisku agresywnym.W artykule zaprezentowano wyniki badań dotyczących określenia wpływu jonów Na+, Mg2+ i SO4 2– na trwałość betonów cementowych wykonanych z różnych rodzajów kruszywa węglanowego, eksponowanych na ciągłe działanie każdego z siarczanów w temperaturze 20±2ºC.

EN

Among carbonate aggregates, dolomite aggregates the only exposed to the liquid medium may decompose and produce swelling form of calcium and magnesium hydroxides. The decomposition processes of dolomite aggregates can be significantly affected with presence of Na+, Mg2+ cations and SO4 2– anions in aggressive environment. The results of studies on impact of exposure to a wet environment containing Na+, Mg2+ and SO4 2– ions on the durability of cement concrete made with different types of carbonate aggregates at temperature conditions 20±2ºC, are presented in the article.

5

Zmiany wytrzymałości w warunkach krystalizacji soli oraz oddziaływania dwutlenku siarki w wybranych makroporowatych skałach węglanowych

Bobrowska A.

Przegląd Geologiczny

|

2013

|

Vol. 61, nr 5

311--314

EN

The article presents the changes in long-term endurance of macroporous carbonate rocks by modelling the process of crystallization of salt (sodium sulphate) from the solution and the impact of sulphur dioxide in the presence of humidity. The characteristics of travertine endurance were determined based on the uniaxial compression test of endurance. Tests were conducted in laboratory conditions on monoliths from Poland and Turkey. Rock material from Poland was the so-called "Polish travertine" collected from an active quarry in Raciszyn (RA) and represented by Upper Jurassic limestones. The material from Turkey was a reed-type travertine rock, one of the leading lithotypes from the Denizli region, taken from an active quarry in Hierapolis (HO), and weathered material collected from the ancient opening in Hierapolis (HA). Research shows that the rock materials, regardless of the degree of weathering and location, have an increased susceptibility to lower endurance to uniaxial compression as a result of the impact of SO2 in the presence of humidity, rather than as a result of the crystallization of salt from the solution. This observation demonstrates that the travertine is characterised by relatively high resistance to salt solutions. Within porous material, the salt crystals can freely crystallize in the gaps without damaging the structure.

6

Kinetyka krystalizacji bezwodnego siarczanu sodu i przenoszenie skali procesu

Warmuziński K., Jaschik J., Jaschik M.

Przemysł Chemiczny

|

2012

|

T. 91, nr 7

1445-1448

PL

Przedstawiono wyniki badań doświadczalnych kinetyki krystalizacji wyparnej bezwodnego siarczanu sodu. Badania prowadzono z zastosowaniem trzech geometrycznie podobnych krystalizatorów o pojemności: 0,2, 1 i 5 dm³. Wyznaczano liniową szybkość wzrostu kryształów i efektywną szybkość zarodkowania. Opracowano korelacje potęgowe określające zależność parametrów kinetycznych krystalizacji od przesycenia, gęstości zawiesiny i intensywności mieszania. Określono wpływ wielkości krystalizatora na rozmiar otrzymywanych kryształów.

EN

Anhyd. Na₂SO₄ was crystd. from its aq. soln. in mixed reactors (0.2–5 L) under vacuum evapn. (430 hPa, 80°C) at varying residence time (1135–4012 s), evapn. rate (0.980– 35.433 g/min), suspension d. (22.13–129.63 kg/m³) and stirrer speed (450–1950 rpm) to study the process kinetics and to det. the linear crystal growth and effective nucleation rates. The correlations between kinetic parameters of the crystn. and supersatn., magma d. and mixing intensity were derived from the expt. data. The detd. order of crystal growth rate was about 1.4 for all crystallizers. The exponents in the equations describing the effect of the growth rate, magma d. and stirrer speed on the nucleation rate were 0.85, 1 and 2.5, resp. The scale-up principles to achieve the same median crystal size were developed. Over the range studied, a modest increase in median crystal size with increasing vol. of the crystallizer was obsd. for a const. sp. power input.

7

Characterization of the metastable zone width in the water solutions of sodium sulphate Na2SO4ź10H2O

Piotrowski J., Skiba P., Piotrowski K.

Polish Journal of Chemical Technology

|

2006

|

Vol. 8, nr 4

74-76

EN

Sodium sulphate Na2SO4ź10H2O is produced on industrial scale in the process of mass crystallization from the water solutions of sodium sulphate. In order to produce the crystal population of the required size distribution, it is necessary to know the optimum technological parameters of the continuous process, mainly the metastable zone width under various hydrodynamic conditions. The performed measurements with the application of a natural cooling method covered: concentration range c(r) = 138 - 409 gźdm3 temperature T = 13 - 31°C, mixer's location in 1/3, 1/2, 2/3 of the liquid high, mixer's revolution number: 800, 1000 i 1600 revźmin-1. The values of the maximal relative supersaturation are within (S)= 1.05 - 1.46 range, which corresponds to deltac(max) =13-64 gźdm3 and deltaT(max) = 0.7 - 5.3°C.

8

Kinetyka krystalizacji siarczynu sodu

Jaschik J., Warmuziński K., Jaschik M.

Inżynieria Chemiczna i Procesowa

|

2004

|

T. 25, z. 3/2

1023-1028

PL

Przedstawiono wyniki badań doświadczalnych kinetyki krystalizacji siarczynu sodu. Badania przeprowadzono w pracującej w sposób ciągły laboratoryjnej instalacji wyparnej, zawierającej krystalizator o pojemności ok. 0,2 dm3. Wykorzystując model krystalizatora MSMPR wyznaczano szybkość zarodko-wania i liniową szybkość wzrostu kryształów. Opracowano równania określające zależność liniowej szybkości wzrostu kryształów od przesycenia oraz szybkości zarodkowania od przesycenia i gęstości zawiesiny.

EN

Results are presented of experimental investigations on the kinetics of the crystallization of sodium sulphite. The measurements were made in a laboratory scale evaporative installation, containing an 0.2 dm3 continuously operated crystallizer. The Iinear crystal growth and nucleation rates are estimated from the population density plot using the MSMPR model. The correlations between rates of growth and nucleation, supersaturation and magma density are derived from the experimental data.