Wyniki wyszukiwania - BazTech

1

Effect of the addition of basalt fiber on life-cycle anti-cracking behavior of concrete

Li Yue, Shen Aiqin, Guo Yinchuan

Archives of Civil and Mechanical Engineering

|

2023

|

Vol. 23, no. 2

art. no. e92, 2023

EN

To evaluate the cracking resistance of basalt fiber reinforced concrete (BFRC) in different periods, including the curing period and the service period, restrained slab, restrained ring and three-point bending tests were conducted. In this investigation, various fiber lengths (i.e., 6 mm, 12 mm, and 18 mm) and fiber contents (ranging from 0.07% to 0.09%) were used to prepare BFRC. The plastic shrinkage behavior of BFRC was characterized by monitoring evaporation, bleeding, capillary pressure and plastic shrinkage strain, and the mechanism of the effect of the fibers in reducing plastic cracking was subsequently revealed. The restrained shrinkage strain in the steel ring was measured, and the cracking potential index (ΘCR) was assessed for all BFRC specimens. Furthermore, the fracture behavior, including the strain distribution and cracking process, was monitored by the digital image correlation (DIC) technique. The results showed that long basalt fibers (12 mm and 18 mm) effectively delayed the occurrence of the plastic settlement and reduced capillary pressure, resulting in a decreased crack width of concrete. The basalt fibers also led to a pronounced decrease in the ΘCR of the concrete, particularly at an early curing age (3 d). Moreover, the DIC test revealed that the crack occurrence was accompanied by a fuctuation in the strain field during the fracture process. Basalt fibers considerably slowed the formation and evolution of the strain stripes of the concrete under load, and consequently, the fracture energy and cracking resistance capacity of concrete can be improved by the addition of basalt fibers.

2

Rodzaje skurczu betonu, ich znaczenie i metody zapobiegania

Kurdowski Wiesław

Cement Wapno Beton

|

2021

|

R. 26, nr 2

109--117

PL

Jedną z niekorzystnych właściwości betonu stanowi skurcz, który jest spowodowany zmianami objętościowymi zaczynu cementowego. Wyróżniamy następujące rodzaje skurczu: skurcz chemiczny nazywany także kontrakcją lub skurczem Le Chatelier, skurcz plastyczny, skurcz autogeniczny, czasem zwany także skurczem auto-suszenia i skurcz suszenia. Opracowano szereg metod w celu usunięcia tego skurczu. Krystalizacja ettringitu jest jedną z metod i jest oparta na dodatku kompleksu Kleina do cementu. Są także stosowane domieszki organiczne, które opierają się na zmniejszeniu napięcia powierzchniowego wody w kapilarach. W pracy zbadano wpływ domieszki BASF Master Life SRA 815 samej i z dodatkiem CaO. W przeprowadzonych doświadczeniach wykazano, że CaO powoduje bardzo małe zmniejszenie skurczu, natomiast wymieniona domieszka daje duże zmniejszenie skurczu. Równoczesny dodatek CaO do Master Life SRA 815 powoduje zwiększenie wpływu tej ostatniej. Także dodatek samego kompleksu Kleina nie spowodował zmniejszenia skurczu, natomiast jego dodatek do Master Life SRA 815 zwiększył zmniejszenie skurczu.

EN

One of the unfavourable properties of concrete is shrinkage which is linked with the volume changes of cement paste. We distinguish the following kinds of shrinkage: – “chemical” shrinkage called also the contraction or Le Chatelier shrinkage, – plastic shrinkage, – autogenic shrinkage or spontaneous, sometimes called auto drying, – drying shrinkage. There are several methods to eliminate concrete shrinkage. The ettringite crystallization is one of the inorganic compounds methods and is based on Klein’s complex addition to cement. This complex is causing the rapid ettringite formation and the shrinkage is diminished. There are also organic admixtures which action is the reduction of the water surface tension. There are surface-active additions that are reducing this tension, in capillaries. The organic admixtures which are diminishing the shrinkage are based on neopentyl glycol or similar chemical compounds. In the study, the shrinkage-reducing admixture BASF Master Life SRA 815 alone and with CaO addition were examined. It was shown that CaO addition is giving very low diminishing of cement shrinkage, contrary to the fluid admixture Master Life SRA 815 which has a high diminishing influence on cement shrinkage. However, the simultaneous addition of CaO is increasing the diminishing influence of this fluid admixture. The addition of Klein’s complex does not influence of shrinkage but its simultaneous addition with Master Life SRA 815 gives higher shrinkage diminishing.

3

Rodzaje skurczu betonu jego znaczenie i metody zapobiegania

Pawluk J.

Cement Wapno Beton

|

2018

|

R. 21/83, nr 4

290--297

PL

W pracy omówiono rodzaje skurczu betonu i ich przyczyny oraz metody zapobiegawcze. Następnie przeprowadzono badania skurczu cementu CEM I 42,5R z dodatkiem CaO, uzyskanego w wyniku prażenia wapna hydratyzowanego w 1450°C oraz domieszek handlowych. Były to domieszki BASF MasterLife SRA 150 i BASF MasterLife SRA 815, pierwsza, która opiera się na powstawaniu ettringitu, druga wpływająca na napięcie powierzchniowe wody. Dodatek CaO miał bardzo mały wpływ na skurcz cementu, podobnie jak pierwsza domieszka, natomiast ich równoczesny dodatek powodował znaczne zmniejszenie skurczu. Natomiast druga domieszka spowodowała znaczne zmniejszenie skurczu, a równoczesny dodatek wapna praktycznie nie zmieniał wpływu tej domieszki. Ten różniący się znacznie wpływ dwóch domieszek na skurcz cementu jest spowodowany ich różną zgodnością z zastosowanym cementem.

EN

In the paper the kind of shrinkage and the preventing methods were presented. Then the cement CEM I 42.5R shrinkage with the addition of CaO and two admixtures BASF MasterLite SRA 150 and BASF MasterLite SRA 815, was tested. CaO was obtained from lime hydrate burned at 1450°C and the admixtures SRA 150 was based on ettringite formation, but the SRA 815 on the decreasing of water surface tension. CaO addition had a very low influence on shrinkage, analogously as the first admixture. However, their simultaneous addition to cement the significant shrinkage reducing was causing. The second admixture the significant shrinkage reduction was causing. The simultaneous addition of CaO had no influence on the admixture reduction effect. These quite different influence of the two admixtures on shrinkage is caused by their quite different compatibility with the used cement.

4

Ocena wielkości odkształceń skurczowych zapraw i betonów cementowych z dodatkiem polimerów

Gruszczyński M.

Cement Wapno Beton

|

2007

|

R. 12/74, nr 3

139-144

PL

Przedstawiono wpływ różnych dodatków polimerowych na wielkość skurczu i wytrzymałość kompozytów cementowych. Wpływ ten porównano z działaniem klasycznej domieszki zmniejszającej skurcz opartej na wielkocząsteczkowym alkoholu. W oparciu o przeprowadzone badania stwierdzono znaczne zmniejszenie skurczu i wzrost wytrzymałości na zginanie, spowodowany 5% dodatkiem dyspersji polimerowej, w stosunku do masy cementu. Zmniejszenie skurczu i poprawa właściwości użytkowych przesądza o atrakcyjności materiałów polimerowo-cementowych w przypadku napraw konstrukcji betonowych i wykonywania bezspoinowych podkładów i posadzek przemysłowych.

EN

The influence of different polymers addition on shrinkage and mechanical properties of mortars and concretes was investigated. This influence was compared with the effect of trade shrinkage reducing admixture widely applied in concrete industry. The experiments have shown significant reduction of shrinkage and increase of bending strength of mortars and concretes with the addition of polymer dispersion in the amount of at least 5% of cement mass. Shrinkage reduction and improvement of properties of mortars and concretes properties make these materials interesting for concrete structures repairs and for construction of industrial primers and floors without joints.