Fracture Statistics Using Three-Parameter and Two-Parameter Weibull Distributions for Fe-0.4C-1.5Cr-1.5Ni-0.8Mn-0.2Mo Structural Sintered Steel

Fiał C., Ciaś A., Czarski A., Sułowski M.

Archives of Metallurgy and Materials

|

2016

|

Vol. 61, iss. 3

1547--1554

EN

A statistical analysis is presented of tensile and bending strengths of a porous sintered structural steel which exhibits non-linear, quasi-brittle, behaviour. It is the result of existing natural flaws (pores and oxide inclusions) and of the formation of fresh flaws when stress is applied. The analysis is by two- and three-parameter Weibull statistics. Weibull modulus, a measure of reliability, was estimated by the maximum likelihood method for specimen populations < 30. Probability distributions were compared on the basis of goodness to fit using the Anderson-Darling tests. The use of the two-parameter Weibull distribution for strength data of quasi-brittle sintered steels is questioned, because there is sufficient evidence that the 3-parameter distribution fits the data better.

2

Wyznaczanie temperatur początku przemian zachodzących podczas spiekania konstrukcyjnych stali manganowo-chromowo-molibdenowych

Sułowski M.

Rudy i Metale Nieżelazne

|

2009

|

R. 54, nr 7

422-435

PL

Celem badań było określenie temperatur początku przemian zachodzących podczas spiekania konstrukcyjnych stali zawierających 3 % Mn, 1,5 % lub 3 % Cr, 0,5 % lub 0,2 % Mo oraz 0,3 % C. Do badań wykorzystano komercyjne proszki stopowe Astaloy CrL i Astaloy CrM, proszek niskowęglowego żelazomanganu oraz proszek grafitu C-UF. Z proszków wyjściowych w mieszalniku Turbula w czasie 30 minut sporządzono mieszanki proszków, a następnie, metodą prasowania w sztywnej matrycy, sprasowano kształtki prostopadłościenne, o wymiarach 5 × 5 × 15 mm, przeznaczone do badań dylatometrycznych w dylatometrze poziomym Netzsch 402E. Wykonane badania dylatometryczne pozwoliły na określenie temperatur początku przemian perlitycznej, bainitycznej oraz martenzytycznej, mieszczących się odpowiednio w zakresie temperatur 600-650 stopni Celsjusza, 450-500 stopni Celsjusza oraz 200-300 stopni Celsjusza. Przeprowadzone badania metalograficzne spiekanych stali wykazały istnienie niejednorodnej i porowatej mikrostruktury spieków. Zaobserwowano również znaczne odwęglenie stali przy powierzchni badanych spieków.

EN

The present work was focused on the determination of transformation temperatures during sintering Mn-Cr-Mo PM structural steels based on pre-alloyed Astaloy CrL and Astaloy CrM powders. Manganese (3 %) and carbon (0.3 %) were added in the form of low-carbon ferromanganese and graphite C-UF powders, respectively. Mixtures of powders were prepared in Turbula mixer for 30 minutes. Following pressing in rigid die, rectangular test bars (5 × 5 × 15 mm) were sintered in Netzsch 402E dilatometer under different conditions. During dilatometric investigations of Fe-3%Mn-(Cr)-(Mo)-0.3%C the Ps, Bs and Ms temperatures were in the range of 600-650 degrees of Celsius, 450-500 degrees of Celsius and 200-300 degrees of Celsius respectively. Metallography of sintered steels showed inhomogeneous and porous microstructure; also decarburisation effect was observed.

3

Badania procesu wytwarzania bezniklowych spiekanych stali konstrukcyjnych przeznaczonych do hartowania bezpośredniego techniką „sinter-hardening”

Ciaś A., Sułowski M.

Hutnik, Wiadomości Hutnicze

|

2009

|

Vol. 76, nr 4

283-289

PL

Badania nad procesem wytwarzania i własnościami nowoczesnych stali spiekanych są prowadzone w Katedrze Metaloznawstwa i Metalurgii Proszków WIM i IP AGH od wielu lat. W ostatnim czasie, podążając za aktualnymi tendencjami światowymi, podjęto badania nad wytwarzaniem samohartujących się, spiekanych, bezniklowych stali konstrukcyjnych, o ograniczonej do minimum zawartości molibdenu. Przyjęto założenie, że proponowane stale muszą być możliwe do wytworzenia przy wykorzystaniu istniejących, tradycyjnych pieców przemysłowych i bezpiecznych atmosfer; powinny przy tym nadawać do produkcji średnio i mocno obciążonych, odpowiedzialnych części maszyn, włącznie z częściami dla motoryzacji. Prezentowana praca ma na celu podsumowanie dokonań Katedry w zakresie wytwarzania spiekanych stali konstrukcyjnych Fe-Cr-Mn-Mo-C. Przedstawiono rezultaty badań nad zastosowaniem spiekania standardowego (1120 °C) oraz wysokotemperaturowego (1250 °C), w atmosferze wodoru i azotu, jak również w atmosferze stanowiącej mieszaninę tych gazów.

EN

The investigations of processing and properties of modern sintered steels have been continued in Department of Physical Metallurgy and Powder Metallurgy, Faculty of Metal Engineering and Industrial Computer Science of AGH-UST, for many years. Recently, following the global trends, investigations of self-hardening, Ni-free, low Mo-content structural steels have been carried out. The idea was to produce medium-to-high loaded sintered steel structural parts, involving automotive parts, using the existing conventional furnaces and safe low-hydrogen atmospheres. This paper summarises the results of the investigations in the Department and describes a new process that utilises materials and methods that strive to reduce the cost of PM steel parts. It concerns the effect of processing conditions on the resultant properties of Fe-Mn-C and Fe-Mn-Cr-Mo-C steels, sintered both at 1120 °C and 1250 °C in nitrogen, hydrogen and mixtures thereof.