1
Content available The improvement in properties of polyester resin-based composites using a new type of silane coupling agent
Urbaniak Włodzimierz, Bednarek Wojciech Hubert, Paukszta Dominik, Szostak Marek, Szymańska Joanna
Polimery
|
2023
|
Vol. 68, nr 4
221--225
EN
Adhesion between the polymer matrix and fillers is an important factor influencing the properties of the obtained composites. One way to improve interactions at the interface is to modify the filler with coupling agents, e.g., silanes. The article presents the effect of modifying the surface of the mineral filler with a new type of silane [triethoxy(ketoimino)silane] on the mechanical properties of polyester resin based composites. Composites with triethoxy(ketoimino)silane-modified filler had similar mechanical properties to composites obtained with commercial silanes, with slightly lower water absorption.
PL
Adhezja między osnową polimerową i napełniaczami jest istotnym czynnikiem wpływającym na właściwości otrzymanych kompozytów. Jednym ze sposobów poprawy oddziaływań na granicy faz jest modyfikacja napełniacza środkami sprzęgającymi, np. silanami. W artykule przedstawiono wpływ modyfikacji powierzchni napełniacza mineralnego przy użyciu nowego typu silanu [triethoksy(ketoimino)silan] na właściwości mechaniczne kompozytów na bazie żywicy poliestrowej. Kompozyty z udziałem napełniacza modyfikowanego triethoksy(ketoimino)silanem miały podobne właściwości mechaniczne do kompozytów otrzymanych z udziałem silanów handlowych, przy nieco mniejszej chłonności wody.
2
Content available CO2 zamiast CO : katalityczna konwersja CO2 w syntezie związków karbonylowych
Wójcik Ewelina, Trzeciak Anna M.
Wiadomości Chemiczne
|
2021
|
[Z] 75, 3-4
395--422
EN
Modem industrial carbonylation processes, leading to functionalized carbonyl compounds, are based on the application of highly toxic and flammable carbon monoxide. Recently, carbon dioxide which is non-toxic and abundant, has attracted attention as a perfect C1 source to build new C-C and C-N bonds. From the standpoint of green and sustainable chemistry, it is appealing and challenging to combine the reduction of CO2 with subsequent carbonylation using in situ formed CO. Herein we present the application of CO2 as C1 building block for the carbonylation of different organic compounds in the presence of transition metal catalysts (e.g. Pd, Rh, Ru, Fe). Industrially important organic compounds has been obtained in hydroformylation, dehydrogenation, hydrogenation, aminocarbonylation and carboxylation reactions with CO2. On the other hand, rapid reduction of CO2 to CO could processed in the metal catalyst - free systems, using a catalytic amount of fluoride salt and stoichiometric amount of di- or hydrosilane. In these reactions silyl formate has been identified as an important intermediate formed from silane and carbon dioxide. Also hydrazine and sodium borohydrate have been used for CO2 reduction to formic acid or other products. Obviously, these reactions could be restricted because of their sensitivity to the applied conditions, high cost of reactants as well as the waste generated. The presented examples of catalytic carbonylation reactions with CO2 as a source of CO group illustrate a high technological potential of this strategy.
3
Content available remote Wytwarzanie powłok z użyciem organofunkcyjnych silanów
Martyła A., Osińska-Broniarz M., Kopczyk M., Sztorch B., Jarmołowicz A., Przekop R. E.
Przemysł Chemiczny
|
2017
|
T. 96, nr 6
1244--1248
PL
Zaprezentowano wyniki badań mających na celu ocenę powłok otrzymywanych z użyciem preparatów do hydrofobizacji. Podłożem bazowym, poddawanym modyfikacji był piaskowiec, granit oraz podłoże szklane. Badaniom poddano preparaty dostępne komercyjnie oraz ich modyfikacje dokonane z wykorzystaniem oleju silikonowego i organofunkcyjnego silanu. Ocenę właściwości hydrofobowych wykonano poprzez pomiar kątów zwilżania modyfikowanych materiałów.
EN
B-Si glass, sandstone and granite surface were modified by coating with com. hydrophobic formulations and their mixts. with silicone oil and organofunctional silanes and studied by measuring their wetting angles. A substantial increase in the sandstone and granite hydrophobicity was achieved. The glass surface showed low hydrophobizability.
4
Content available Hydrophobicity and weathering resistance of wood treated with silane-modified protective systems
Hochmańska P., Mazela B., Krystofiak T.
Drewno : prace naukowe, doniesienia, komunikaty
|
2014
|
vol. 57, nr 191
99--110
EN
The study presents the hydrophobic effect of silane-modified protective systems on wood resistance to aging factors (water and UV radiation). This paper is focused on conventional and low VOC emulsion systems for exterior use, which were improved with silanes such as methyltrimethoxysilane (MTMOS), aminoethylaminopropyltrimethoxysilane (AEAPTMOS) and glycidoxypropyltrimethoxysilane (GPTMOS). The performance of the new protective systems, applied on pine wood by surface impregnation, was demonstrated through an accelerated weathering test and evaluated by contact angle, colour and gloss changes. The study showed improvement in the hydrophobicity and photostability of the protective systems modified with selected silanes. The highest protection from the accelerated weathering conditions was obtained using the treatment with a solvent-borne formulation with 5% AEAPTMOS and an alkyd emulsion with 5% MTMOS.
PL
Celem pracy było zbadanie wpływu związków krzemoorganicznych wprowadzonych do modelowych systemów impregnacyjno-ochronnych na hydrofobowość i odporność powierzchni drewna na abiotyczne czynniki niszczące. Badania przeprowadzono na drewnie bielu sosny zwyczajnej (Pinus sylvestris L.). Próbki drewna poddano impregnacji metodą powierzchniową wybranymi systemami impregnacyjno-ochronnymi bazującymi odpowiednio na żywicy alkidowej oraz mieszaninie olejów naturalnych z udziałem silanów w postaci metylotrimetoksysilanu (MTMOS), aminoetyloaminopropylotrimetoksysilanu (AEAPTMOS) oraz glicydoksypropylotrimetoksysilanu (GPTMOS). Zakres pracy obejmował ocenę właściwości fizykochemicznych opracowanych kompozycji, charakterystykę zwilżania oraz badania odporności na procesy starzeniowe zabezpieczonych powierzchni drewna. Do oceny jakości wyrobów i wymalowań zastosowano oznaczenie gęstości, lepkości i rozlewności. W celu określenia wpływu promieniowania UV i wody na badane systemy porównano takie właściwości jak zwilżalność, barwę oraz połysk przed i po ekspozycji na czynniki niszczące. Pomiarów dokonano odpowiednio po 5, 10, 15 i 20 cyklach starzeniowych. Na podstawie analizy wyników przeprowadzonych badań stwierdzono, że powierzchnia drewna sosny zabezpieczonego systemami impregnacyjno-ochronnymi z udziałem związków krzemoorganicznych (MTMOS, AEAPTMOS, GPTMOS) wykazała podwyższone właściwości hydrofobowe, a przez to zwiększoną odporność na promieniowanie UV i wodę. Powierzchnię drewna o najwyższej hydrofobowości oraz odporności na czynniki starzeniowe uzyskano poprzez impregnację systemem SB/olej z udziałem 5% AEAPTMOS oraz emulsją alkidową z udziałem 5% MTMOS. Opracowane systemy spełniały również wymagania kryterialne adsorpcyjnej teorii adhezji polimerów do drewna w odniesieniu do parametrów γS i Wa. Systemy pod względem aplikacyjnym wykazywały zwiększoną odporność na procesy fotodegradacji oraz stabilne walory estetyczno-dekoracyjne w warunkach starzenia.
5
Content available remote Krzemian magnezu modyfikowany silanowymi środkami proadhezyjnymi jako napełniacz polipropylenu : wytwarzanie i charakterystyka kompozytów
Bula K., Ciesielczyk F., Maciejewski H.
Przemysł Chemiczny
|
2013
|
T. 92, nr 11
1976-1980
PL
Przedstawiono wyniki badań procesu strącania i modyfikacji krzemianu magnezu z wykorzystaniem silanowych środków proadhezyjnych. Określono charakter dyspersyjny modyfikowanych krzemianów magnezu, wyznaczając polidyspersyjność i średnicę cząstek, oznaczono powierzchnię właściwą oraz wykonano zdjęcia mikroskopowe w celu określenia morfologii ziaren. Wykonano kompozyty zmodyfikowanych napełniaczy z polipropylenem z wykorzystaniem mieszalnika dynamicznego oraz poddano je próbie jednoosiowego rozciągania i udarności z karbem. Badania pozwoliły na określenie najbardziej korzystnego układu silan-krzemian magnezu w aspekcie właściwości kompozytów o osnowie z polipropylenu.
EN
MgO·SiO2 was pptd. and surface-modified with alkoxysilanes, studied for particle size distribution, N2 adsorption and dispersive properties and then used as filler of polypropylene-matrix composites. The modified MgO·SiO2 particles improved slightly the tensile strength of polypropylene but significantly raised its Young modulus.
6
Content available remote Wpływ modyfikacji sadzy silanami i aminą na właściwości fizyczne wulkanizatów NBR
Potocki K., Zaborski M.
Przemysł Chemiczny
|
2012
|
T. 91, nr 8
1605-1607
PL
Przedstawiono wyniki badań nad wpływem modyfikacji sadzy na właściwości fizyczne wulkanizatów NBR. Do badań zastosowano sadzę kanałową, którą modyfikowano za pomocą N-2- aminoetylo-3-aminopropylotrimetoksysilanu, 3-metakryloksypropylotrimetoksysilanu oraz trietylenodiaminy. Zbadano takie właściwości fizyczne wulkanizatów, jak wytrzymałość na rozciąganie, naprężenie przy wydłużeniu 100%, 200% i 300%, wytrzymałość na rozdzieranie oraz wydłużenie przy zerwaniu. Okazało się, że modyfikacja sadzy za pomocą dietylenotriaminy poprawiła właściwości wytrzymałościowe wulkanizatów NBR.
EN
Nitrile rubbers was filled with channel C black samples modified with NH₂CH₂CH₂NH(CH₂)₃Si(OMe)₃, CH₂=CHCOO(CH₂)₃Si(OMe) and (NH₂CH₂CH₂)₂NH at 120°C and 60 hPa for 24 h and then studied for tensile strength, elongation under stress and tear strength. Only the modification of C black with (NH₂CH₂CH₂)₂NH resulted in an improvement of the mech. properties of the rubber vulcanizates.
7
Content available remote Modification of the Titanium Implants Surface by Silanes and Colloidal Silver
Zboromirska-Wnukiewicz B., Wnukiewicz J., Kogut K., Kasprzyk K., Wnukiewicz W.
Archives of Metallurgy and Materials
|
2009
|
Vol. 54, iss. 4
1005-1011
EN
Surface modification of an implants by colloidal silver and three kinds of silanes such as Z-6020, A - 187, TRIAMO were carried out. Contact angles of the implants covered colloidal silver with different properties were examined. The change of a hydrophobic character of the surface implants was defined. DSA 100 System which allow to contact angle measure of a solid bodies in wide bounds from 4° to 122° with accuracy of measurement to 0,1° were applied. The roughness of modified implants surface was examined by profilometer WYKO NT 9300 with high optical resolution.
PL
W pracy przedstawiono modyfikację powierzchni implantów srebrem koloidalnym oraz trzema rodzajami silanów: Z -6020, A - 187 oraz TRIAMO. Zmierzono kąt zwilżania na implantach pokrytych srebrem koloidalnym o różnych właściwościach. Określono charakter zmian hydrofobowości powierzchni implantów. Do pomiarów wykorzystano system DSA 100, który pozwala na pomiar kąta zwilżania płynów na powierzchniach ciał stałych w szerokich granicach od 40° do 120° z dokładnością pomiaru do 0,10°. Chropowatość powierzchni modyfikowanych implantów zmierzono przy pomocy profilometru optycznego Wyko NT 9300 o dużej rozdzielczości.
8
Content available remote Synteza organofunkcyjnych silanów z 3-chloropropylotrimetoksysilanu w skali półtechnicznej
Oczkowicz S., Maciejewski H., Dutkiewicz A., Dąbek I., Tyrka M., Minda D., Marciniec B.
Przemysł Chemiczny
|
2006
|
T. 85, nr 8-9
962-964
PL
Przedstawiono wyniki badań technologicznych, związanych z uruchomieniem produkcji 3-metakryloksypropylotrimetoksysilanu, 3-izocyjanianopropylotrimetoksysilanu oraz 3-(dietylenotriamino)propylotrimetoksysilanu, stosowanych jako promotory adhezji, czynniki sieciujące oraz modyfikujące polimery w wielu dziedzinach przemysłu. Silany te otrzymano w reakcji substytucji nukleofilowej chloru w 3-chloropropylotrimetoksysilanie.
EN
Three organofunctional silanes (3-methacryloxypropyltrimethoxysilane, 3-isocyanatopropyltrimethoxysilane and 3-(diethylenetriamino)propyltrimethoxysilane) were implemented to the pilot plant prodution. The production process was based on nucleophillic substitution of chlorine in 3-chloropropyltrimethoxysilane. The products were recommended as adhesion promoters, crosslinking agents and polymer modifiers for many branches of industry.
9
Content available remote Corrosion protection of a silver laser on glass
Zahradnik L., Tynova E.
Ochrona przed Korozją
|
2006
|
nr 2
46-48
EN
An overview of the protective methods used for silver layers on glass surface has been made. A new method based on the reaction of silver and mercaptosilane has been presented. A new technique for fi xing a protective silane layer through copolymerization with a suitable aminosilane has been succefully applied. The optimal composition of a solution of silanes in isopropanol to protect the silver layer has been discovered. The protective function of the created layers on the silver layer on glass was tested by two standardised tests; a test in an atmosphere of sulphur substances and a test in an atmosphere of neutral salt spraying. This solution protects the glass with a silver laser successfully; no blackening and no milkiness had occurred during the performed tests.
PL
Przedstawiono przegląd metod zabezpieczania warstwy srebra na powierzchni szkła. Omówiono nową metodę opartą na reakcji srebra z merkaptosilanem. Metoda ta, przedstawiająca nowe możliwości utwierdzeniu ochronnej warstwy silanu poprzez kopolimeryzację z odpowiednim aminosilanem została z powodzeniem zastosowana. Znaleziono optymalny skład roztworu silanów w isopropanolu do ochrony warstwy srebra. Właściwości ochronne utworzonych powłok na warstwie srebra pokrywającego szkło została zbadana za pomocą dwóch standardowych testów: w atmosferze zawierającej związki siarki oraz w rozpylonej mgle solnej. Roztwór ten z powodzeniem chroni szkło pokryte warstwą srebra; nie wystąpiło czernienie ani też zmatowienie powłoki srebra podczas wykonywanych testów.
10
Content available remote Modyfikacja włókien aramidowych jako napełniacza w tworzywach akrylowych
Domka L.
Czasopismo Techniczne. Mechanika
|
2006
|
R. 103, z. 6-M
149-154
PL
W pracy przedstawiono wyniki badań nad zastosowaniem modyfikowanych włókien kevlarowych jako napełniacza w tworzywach akrylowych. Włókna aramidowe poddano procesowi modyfikacji za pomocą fal ultradźwiękowych, a następnie stosując wybrane związki powierzchniowo-czynne z grupy silanów. Zaistniałe zmiany struktury modyfikowanych włókien w próbkach akrylowych obserwowano w skaningowym mikroskopie elektronowym (SEM). Przeprowadzono badania fizykomechaniczne na trójpunktowe zginanie za pomocą aparatu Hounsfield H5 KS.
EN
The paper presents results of a study on modification of kevlar fibres to be used as fillers in acrylic resins. The aramid fibres were modified first by ultrasound treatment and then by selected surfactants from the group of silanes. The structural changes in the fibres occurring as a result of the modification were observed under a scanning electron microscope (SEM). Moreover, the mechanical properties of the modified fibres were characterized on a universal testing machine Hounsfield H5 KS.
11
Content available remote Badania silanowych promotorów adhezji w wodorozcieńczalnych farbach epoksydowych
Kuczyńska H.
Ochrona przed Korozją
|
2005
|
nr 5
156-159
PL
Przyczepność powłok lakierowych do podłoża decyduje w dużej mierze o trwałości wymalowań ochronno-dekoracyjnych. W celu zwiększenia adhezji powłok organicznych do metali i innych podłoży coraz częściej są stosowane organosilany. Przedstawiono wyniki badań wpływu sześciu silanowych promotorów adhezji na właściwości, zwłaszcza na przyczepność powłok wodorozcieńczalnych farb epoksydowych do malowania stali. Określano przyczepność początkową oraz jej zmiany po długotrwałej ekspozycji w wodzie. Najlepsze właściwości ochronne wykazał silan g - glicydyloksypropylotrimetoksylowy oraz jeden z silanów z grupą aminową.
EN
The adhesion of coatings to substrate is a crucial factor determining the durability of protective-decorative coatings. Organosilanes are applied increasingly more often in order to strengthen the adhesion of organic coatings to metal or other substrates. The results of research conducted to determine the influence of six silane adhesion promotors on the properties, and especially on the adhesion of waterborne epoxy coatings to steel were presented in this article. Initial adhesion and its changes after long-time exposure in water were determined. The best protective properties were achieved for g - glycidoxypropyltrimethoxy silane and one of the silanes containing an amino group.
12
Influence of silanes with different functional groups for zeta potential ceramic - high aluminium material
Zboromirska-Wnukiewicz B., Gryzło K., Sokołowski A.
Prace Naukowe Instytutu Podstaw Elektrotechniki i Elektrotechnologii Politechniki Wrocławskiej. Konferencje
|
2004
|
Vol. 40, nr 15
282-285
EN
This article describes influence of silanes with different functional group for zeta potential ceramic-high alumnium material. For modification of ceramic material's surfaces we have used five different siliconorganic compounds-silanes: Z-6020, MTMO, TRIAMO, VTMO and A-187. The zeta potential changes under action of silane modifiers of material surfaces were related to pH.
13
Content available remote Zastosowanie silanów jako promotorów adhezji gumy do włókien
Zaborski M., Marasek T., Lipińska M.
Elastomery
|
2003
|
T. 7, nr 6
17-25
PL
Zbadano wpływ związków krzemoorganicznych zawierających różne grupy funkcyjne na adhezję kordów i żyłek poliestrowych i poliamidowych do gumy. Silanowe substancje proadhezyjne stosowano do impregnacji włókien, a także dodawano bezpośrednio do mieszanek gumowych w celu ich modyfikacji. Dla porównania kordy impregnowano również kąpielą RFL. Stwierdzono korzystny wpływ impregnacji silanami z roztworu, a zwłaszcza silanem zawierającym grupy aminowe (DAMS), na adhezję włókien do gumy. Modyfikacja składu mieszanek dodatkiem silanów powodowała wzrost siły adhezji, jednakże silany jako promotory adhezji okazały się w tym przypadku mniej skuteczne niż układ proadhezyjny RFS (rezorcyna, krzemionka, donor formaldehydu).
EN
The influence of silanes with different funcional groups on the adhesion between rubber and fibers was investigated. Silane coupling agents were using as impregnation agents of the fibers as well as were added directly as modifying agents to the rubber mixes. For comparison the RFL impregnation was used. The advantageous influence of the impregnation from solution, especially with using DAMS silane on the adhesion between rubber and fibers was observed.
14
Content available remote Wpłw środków do preparacji powierzchni napełniaczy na właściwości wytrzymałościowei tribologiczne kompozytów metalożywicznych
Dasiewicz J., Janecki J., Pawelec Z.
Tribologia
|
2001
|
nr 3
265-274
PL
W artykule przedstawiono wpływ modyfikatorów własności powierzchniowych napełniaczy na cechy użytkowe regeneracyjnych kompozytów metalożywicznych. Jako modyfikatory zastosowano dwa rodzaje związków krzemoorganicznych z reaktywną grupą epoksydową i aminową. Zaprezentowano niektóre wyniki badań własności wytrzymałościowych i cieplnych. Za pomocą testera tribologicznego typu rolka-klocek wyznaczono charakterystyki tarciowo zużyciowe wybranych kompozytów regeneracyjnych.
EN
The article presents the influence of modifiers of superficial properties of fillers on useful features of regeneration metal-resinous composites. Two kinds of silicon-organic compounds with a reactive epoxidation and amine group were used as modifiers. The article shows some results of research on resistance and thermal properties. Friction-wear characteristics of selected regeneration composites were determined with the use of a tribological tester of the block-on-ring type.
15
Modyfikacja CACO3 i jej wpływ na właściwości elastomeru
Lipińska M., Zaborski M.
Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej. Konferencje
|
2001
|
Vol. 50, nr 23
500-503
PL
Powierzchnię strącanego węglanu wapnia zmodyfikowaliśmy hydroksykwasami, kwasami nienasyconymi i ich pochodnymi oraz silanami. W wyniku modyfikacji zmniejszyły się: składowa dyspersyjna energii powierzchniowej ü(ypsilon)Df. Modyfikacja węglanu wapnia w większości przypadków zwiększa adsorpcję ftalanu dibutylu. Została zbadana aktywność napełniaczy w kopolimerze butadienowo-akrylonitrylowym i etylenowo-propylenowym. Zmodyfikowane napełniacze wykazują tendencję do tworzenia „własnej struktury" w ośrodku elastomerowym.
EN
The surface area of precipitated calcium carbonate was modified by hydroxyacids, unsaturated acids and their derivatives and silanes. As a result of the modification a dispersive component of surface energy ü(ypsilon)Ds and specific interaction parameter Sf decreased. The modification of calcium carbonate leads to increase dibutyl phthalate adsorption . The activity of modified fillers in butadiene-acrylonitrile copolymer (NBR) and ethylene-propylene copolymer (EPM) was studied. The modified fillers show tendency to create "own structure" in elastomers matrix.
16
Content available remote Silanowe środki wiążące. Cz. VIII. Ureidofunkcyjne silany
Maciejewski H., Guliński J., Marciniec B.
Polimery
|
1998
|
T. 43, nr 4
219-225
PL
Ureidofunkcyjne silany stanowią kolejną grupę silanowych środków wiążących, które dzięki swojej budowie, a tym samym właściwościom (połączenie reaktywności grupy aminowej i karbonylowej) znajdują zastosowanie jako czynnik sieciujący, promotor adhezji oraz środek poprawiający charakterystykę napełniaczy w kompozytach. Przedstawiono metody syntezy, właściwości i charakterystykę typowych ureidosilanów. Opracowana przez autorów technologia produkcji tych związków na podstawie wytwarzanych w kraju produktów stanowi podstawę do produkcji w Polsce omawianej grupy silanów.
EN
Ureido-functional silanes represent another group of silane coupling agents that combine the alkoxy, the amine and the carbonyl group reactivities and may serve as adhesion promoters and curing agents. Syntheses, properties and application of the silanes are described. A basic process design package was prepared, based on the domestic-made starting materials.
17
Content available remote Silanowe środki wiążące. Cz. VII. Alkilotrójpodstawione silany
Urbaniak W., Marciniec B.
Polimery
|
1998
|
T. 43, nr 3
148-155
PL
Przedstawiono przegląd literaturowy dotyczący metod syntezy alkilotrichlorosilanów i alkilotrialkoksysilanów oraz ich zastosowania, głównie w roli środków sprzęgających. W szczególności omówiono metody syntezy trójpodstawionych alkilosilanów metodą katalitycznego hydrosililowania aikenów chloro- i alkoksysilanami. Oparte na tej reakcji technologie opracowane w Uniwersytecie im. A. Mickiewicza w Pozna-niu są obecnie sukcesywnie wdrażane w skali przemysłowej przez Przedsiębiorstwo Innowacyjno-Wdrożeniowe "Unisil" Sp. z o.o. w Tarnowie. Omówiono także wpływ alkilosilanów na adhezję oraz możliwości wykorzystania alkilosilanów zawierających w łańcuchu alkilowym od 2 do 20 atomów węgla jako środków sprzęgających w układach napełniaczpolimer oraz do modyfikacji polimerów. Wskazano inne dziedziny zastosowań alkilotrójpodstawionych silanów, takie jak modyfikacja katalizatorów Zieglera- Natty i wypełnień kolumn w chromatografii cieczowej (HPLC) oraz środki hydrofobujące w budownictwie.
EN
Syntheses and coupling-agent applications of alkyltrichloro- and alkyltriethoxy silanes are reviewed with particular reference to catalyzed hydrosilylation of alkenes with chloro- and alkoxy silanes. The process developed by the team of the A. Mickiewicz University, Poznan, is being commercialized at the UNISIL Innovation Applications Co., Ltd., Tarnów, Poland. The role of alkylsilanes in adhesion and the use of C2 -C20 alkylsilanes as adhesion promoters and coupling agents in filler-polymer and metal- polymer systems are described. Possible application areas are indicated, including polymer modifiers, Ziegler-Natta catalyst modifiers, HPLC column packing modifiers, and hydrophobizers for the building industry.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.