Effects of SiC Coating of Carbon Fiber on Mechanical Properties in Short Carbon Fiber Reinforced Al Matrix Composite

Jang Jin Man, Ko Se-Hyun, Lee Wonsik

Archives of Metallurgy and Materials

2021

Vol. 66, iss. 4

941--946

A356 Al composites reinforced by short carbon fiber were prepared through the 2-step process: fabrication of a composite precursor and ultrasonication of the precursor melt. The short carbon fibers were coated with 0.15~1.5 μm thick SiC layer by a car-bothermal reaction, and an amount of the carbon fiber reinforcement was determined to be 1.5 vol.% and 4.0 vol.%, respectively. The addition of the carbon fiber increased the hardness of A356 alloy. However, tensile strength did not increase in the as-cast composites regardless of the SiC coating and volume fraction of the carbon fiber, due to the debonding which reduced load transfer efficiency from matrix to fiber at the interface. After T6-treatment of the composites, a significant increase in strength occurred only in the composite reinforced by the SiC-coated short carbon fiber, which was considered to result from the formation of a precipitate improving the Al/SiC interfacial strength.

Polyurethane composites with mixture of carbon fibers and glass frit

Mizera K., Auguścik M., Woronka D., Lipert K., Kalarus W., Ryszkowska J.

Polimery

2016

T. 61, nr 5

307--315

Polyurethane elastomer (EPU) and polyureaurethane (PUUR) products are used in many stages of the mining process, such as extraction, transport, processing and storage. In these stages wheels with tires from polyurethane elastomers are used. Tire materials, especially in suspended transport, are exposed to particularly high loads, which results in their destruction and consequently short exploitation period. To solve this problem it was proposed to use for the production of tires polyurethane composites manufactured using fillers in the form of chopped carbon fiber and glass frit. The effect of the mixture of glass frit and carbon fibers on the properties of polyurethane elastomers was measured. The resulting composites were characterized using the techniques of thermal analysis (DSC, TGA and DMTA) and the structure was described using SEM. The results of tribological research and the evaluation of antistatic traits of the obtained polyureaurethanes were presented.

Wyroby z elastomerów uretanowych (EPU), w tym uretanomoczników (PUUR), są wykorzystywane w kopalniach (np. jako opony kół transportu podwieszanego) na wielu etapach procesu pozyskiwania kopalin, zarówno na etapie wydobywania, transportowania, przetwarzania, jak i magazynowania. Opony w transporcie podwieszanym są narażone na szczególnie duże obciążenia, powodujące szybkie zniszczenie i w konsekwencji skrócenie czasu eksploatacji. W związku z tym do produkcji opon zaproponowano wykorzystanie kompozytów poliuretanowych zawierających cięte włókna węglowe i frytę szklaną. Oceniono wpływ mieszaniny fryty szklanej i włókien węglowych na właściwości elastomerów uretanowych. Wytworzone kompozyty scharakteryzowano metodami analizy termicznej (DSC, TGA i DMTA), a ich strukturę – metodą SEM. Przedstawiono wyniki badań trybologicznych oraz dokonano oceny cech antystatycznych otrzymanych uretanomoczników.