PL
 |
EN
Preferencje help
Polish version English version Język
Widoczny [Schowaj] Abstrakt
Liczba wyników
Powiadomienia systemowe
  • Sesja wygasła!
  • Sesja wygasła!
  • Sesja wygasła!
  • Sesja wygasła!

Znaleziono wyników: 5

Liczba wyników na stronie
first rewind previous Strona / 1 next fast forward last
Wyniki wyszukiwania
Wyszukiwano:
w słowach kluczowych:  selective leaching
help Sortuj według:

help Ogranicz wyniki do:
first rewind previous Strona / 1 next fast forward last
1
Content available remote Characterization of nanoporous nickel-based films on electrode materials for hydrogen evolution, fabricated by dealloying technique
Bakr A., El-Aziz Ahmed M., Abdel-Karim R.
Ochrona przed Korozją
|
2021
|
nr 5
134--139
EN
Nanoporous nickel-based films, with a thickness of several μm have been fabricated on Ni substrate by electrodeposition of zinc, heat treatment of modified Zn-rich layer and by selective leaching of the active zinc metal from the electrode material substrate. The fabrication process involved three steps: (i) cathodic deposition of zinc on Ni substrate, (ii) heat treatment process of the surface layer and (iii) dealloying of zinc in alkaline solution on the electrochemical route. SEM and EDS analyses were carried out after each step of the fabrication process. The dealloyed film displays a porous structure with an average pore size of the order of 0.94μm. The electrocatalytic activity of the fabricated surface towards hydrogen evolution reaction (HER) was evaluated by cathodic polarization measurements and the results have been compared to these of pure nickel and commercial porous nickel foam surface. It has been concluded that the nanoporous nickel films fabricated by electrochemical dealloying revealed considerably higher electrocatalytic activity for HER process.
PL
Nanoporowate, warstwy na baize niklu, o grubościach kilku μm wytwarzano na podłożach niklowych poprzez elektroosadzanie cynku, obróbkę cieplną zmodyfikowanych warstw wzbogaconych cynkiem i przez selektywne ługowanie cynku z wytworzonych warstw powierzchniowych. Proces wytwarzania składał się z trzech etapów: (i) katodowego osadzania cynku na podlożu niklowym, (ii) obróbki cieplnej warstwy powierzchniowej i (iii) selektywnego wytrawiania cynku w roztworze alkalicznym na drodze elektrochemicznej. Po każdym etapie procesu wytwarzania przeprowadzano analize SEM i EDS zmodyfikowanej powierzchni. Wyługowane warstwy wykazują porowatą structure z średnimi rozmiarami porów na poziomie 0.94μm. Elektroaktywność katalityczną zmodyfikowanej powierzchni w odniesieniu do reakcji wydzielania wodoru oceniano w pomiarach katodowej polaryzacji a wyniki porównano dla podłoży czystego niklu i komercyjnego, porowatego niklu gąbczastego. Stwierdzono, że nanoporowate warstwy niklowe wytwarzane poprzez selektywne ługowanie wykazywały znacząco wyższą elektroaktywność katalityczną w odniesieniu do reakcji wydzielania wodoru.
2
Content available Removal of calcium from magnesite flotation concentrate by selective leaching and kinetics analysis
Hu Xiaoxing, Zhu Yangge
Physicochemical Problems of Mineral Processing
|
2020
|
Vol. 56, iss. 5
939--948
EN
Dolomite is the main impurity mineral in magnesite ore, affecting the quality of magnesite products. This study proposed a selective leaching process to reduce the calcium content from the magnesite flotation concentrate using hydrochloride acid (HCl). Laboratory scale tests were conducted to explore the influence of operation factors including HCl concentration, leaching temperature and time, stirring speed on the leaching recovery. The results showed that leaching recovery of CaO and MgO increased with increasing HCl concentration, temperature and time. The CaO leaching recovery is always significantly higher than that of MgO, indicating a good selectivity of HCl to leach dolomite from magnesite. The leaching kinetics of both dolomite and magnesite follow the Avrami model and are diffusion controlled, with an activation energy of 43±}1 kJ×mol-1 and 25±}4 kJ×mol-1, respectively.
3
Content available Beneficiation of Ga from alunite concentrates by selective acid leaching and alkaline precipitation
Zhu Mao-Lan, Chen Hang, Zhong Shui-Ping, Huang Zhong-Sheng, Chen Xi, Hu Zhi-Biao
Physicochemical Problems of Mineral Processing
|
2019
|
Vol. 55, iss. 4
1028--1038
EN
In this study beneficiation of Ga from alunite ore was investigated. The effects of the calcination temperature, H2SO4 concentration, leaching temperature and liquid-solid ratio on the dissolution characteristic of Ga, K and Al were studied. The results showed that increasing the calcination temperature, H2SO4 concentration and leaching temperature can improve the solubility of K and Al. However, higher H2SO4 concentration and lower leaching temperature can improve the dissolution of Ga, which was beneficial to recovery of Ga. On the basis of the solubility difference in H2SO4, a two-stage process of selective acid leaching and alkali precipitation of Ga was proposed. The concentration of Ga was increased significantly from 54 g/t in alunite ore to 4100 g/t in alkali precipitation product. The major elements of Al and K in alunite were recovered as the alum crystal with a purity of 99.62%.
4
Content available remote Alkaline leaching of amphoteric elements from powdered, overstoichiometric hydride material
Gęga J., Dymek M., Drulis H., Hackemer A., Indyka P., Bala H.
Ochrona przed Korozją
|
2015
|
nr 11
378--380
EN
The alkaline preferential dissolution of amphoteric elements from overstoichiometric, powdered hydrogen absorbing material of LaNi4.5Co0.5(AlZnSn)0.35 composition has been studied using ICP AES method. The observations of structure changes of the as received and leached material particles have been studied by XRD and TEM techniques. It has been shown that during 50 h exposure of the powder in 6 M KOH (38oC) over 50% of amphoteric elements are selectively etched from the tested material. At the same time, as a result of etching, the surface layers of powder particles undergo strong development.
PL
Metodą ICP AES analizowano preferencyjne wytrawianie pierwiastków amfoterycznych z nadstechiometrycznego materiału wodorochłonnego o składzie LaNi4.5Co0.5(AlZnSn)0.35. Zmiany strukturalne wyjściowych i trawionych cząstek materiału obserwowano za pomocą technik XRD i TEM. Pokazano, że 50-godzinna ekspozycja badanego proszku w 6 M KOH (38oC) prowadzi do selektywnego roztworzenia ponad 50% pierwiastków amfoterycznych obecnych w wyjściowym materiale. Jednocześnie, w wyniku wytrawiania proszku, powierzchnia zewnętrznych warstw cząstek ulega silnemu rozwinięciu.
5
Mechanism of enrichment of trace metals on fine sludges collected from filtration plants
Janukowicz H.
Zeszyty Naukowe. Marine Sciences / Uniwersytet Szczeciński
|
1998
|
Nr 5
135-147
PL
Osady filtracyjne pobrano z pięciu stacji filtracyjnych, określono w nich podział ilościowy dziesięciu metali (Ag, Cd, Mn, Zn, Pb, Cu, SN, Co, Ni oraz Fe) za pomocą selektywnego ługowana. Stwierdzono, że: ˇ ilości dostępne, które pokazują całkowitą ilość każdego z metali wypłukanego pomiędzy 1M CH3COONH4 i 30-procentowym H2O2 dla Ag, Cd i Mn wynosiły od 34 do 96% w pięciu osadach; ˇ dostępne ilości dla Zn, Pb, Cu i Sn wynosiły od 38 do 95% na pięć osadów; ˇ najważniejszą frakcją dla Co, Ni i Fe, z wyjątkiem osadu z Goleniowa, znacznie zanieczyszczonego przez materię organiczną, była frakcja krystaliczna. Dlatego uważa się, że powyższe metale, z wyjątkiem Co, Ni i Fe są wzbogacone w miejscach wymiany jonowej przez materię organiczną, uwodnione tlenki Fe/Mn oraz siarczki w osadach filtracyjnych.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.