Influence of Soaking Parameters on the Segregation and Corrosion Resistance of GJS-X350NiMnCu7-3-2 Ductile Iron

Medyński D., Janus A., Stachowicz M.

Archives of Foundry Engineering

|

2017

|

Vol. 17, iss. 2

69--74

EN

In this paper, the effect of changes the parameters of heat treatment on the structure and the degree of elements segregation was determined, in the context of corrosion resistance of ductile iron Ni-Mn-Cu, containing 7.2% Ni, 2.6% Mn and 2.4% Cu. In the condition after casting, castings of austenitic matrix and 160HBW hardness were obtained. The achieved castings were soaked at 450, 550 and 650°C for 4, 8 and 12 hours, then cooled down at the ambient air. In most cases, the heat treatment resulted in a change in the castings matrix, had the consequence of increasing their hardness in comparison to raw castings. Increasing the temperature and prolonging soaking time resulted in increasing the degree of transformation of austenite, while reducing the degree of elements segregation. This led to the formation of slightly bigger number of pitting due to corrosion, but not so deep and more evenly distributed in comparison to raw castings. Wherein the results of corrosion tests show that heat treatment of castings did not significantly change their corrosion resistance in comparison to raw castings, in contrast to the significant increase in mechanical properties.

2

Poprawa jakości wewnętrznej wlewka konwencjonalnego metodą obróbki akustycznej

Kania H., Nowacki K.

Prace Instytutu Metalurgii Żelaza

|

2015

|

T. 67, nr 2

38--43

PL

Bezpośrednim efektem oddziaływania energii akustycznej podczas krzepnięcia wlewka we wlewnicy jest zmiana struktury metalu. Dotychczasowe badania i eksperymenty przeprowadzone w ramach współpracy naukowej pomiędzy Politechnikę Śląską w Katowicach i Instytutem Metalurgii Żelaza w Gliwicach nad zastosowaniem technologii obróbki akustycznej do poprawy jakości wewnętrznej wlewków ze stali wysokowęglowej dały pozytywne wyniki. W strefie oddziaływania fali akustycznej we wlewku, uzyskano rozdrobnienie struktury stali i równomierny rozkład pierwiastków, a także wzrost twardości, która może być postrzegana jako wskaźnik obrabialności akustycznej stali. W celu określenia przydatności opracowanej technologii w warunkach przemysłowych, zawiązano konsorcjum składające się z partnerów polskich i niemieckich. Liderem konsorcjum jest grupa przemysłowa Alchemia S.A. (Huta Batory), ponadto w jego składzie znajdują się następujący partnerzy: Politechnika Śląska Katowice, Instytut Metalurgii Żelaza z Gliwic, TU Bergakademie Freiberg, BGH Edelstahl Freital GmbH oraz wrocławska firma PBP OPTEL S.A. Założonym efektem prowadzonych badań jest redukcja segregacji pierwiastków w objętości wlewka konwencjonalnego oraz zwiększenie udziału strefy kryształów równoosiowych za pomocą fali akustycznej dostarczonej bezpośrednio do objętości ciekłego, krzepnącego wlewka, a poprzez to poprawa właściwości fizycznych przerobionego plastycznie materiału.

EN

The direct effect of exposure to acoustic energy during the solidification of ingot in a mould is the change in metal structure. The research and experiments carried out so far as a part of scientific cooperation on application of the acoustic treatment technology for improving the internal homogeneity of high-carbon steel ingots between the Silesian University of Technology in Katowice and the Institute for Ferrous Metallurgy in Gliwice yielded positive results. Within the acoustic wave influence area in the ingot, the refinement of steel structure and uniform distribution of elements as well as increase in hardness, which can be perceived as the steel acoustic treatability index, were obtained. To determine the applicability of the developed technology under industrial conditions, the consortium consisting of Polish and German partners has been set up. The leader of the consortium is the industrial group Alchemia S.A. (Huta Batory). In addition, it comprises the following partners: Silesian University of Technology in Katowice, Institute for Ferrous Metallurgy in Gliwice, TU Bergakademie Freiberg, BGH Edelstahl Freital GmbH and PBP OPTEL S.A. in Wroclaw. The assumed effect of conducted research is the reduction in segregation of elements within the volume of conventional ingot and increase in the share of the area of equiaxed crystals by means of the acoustic wave supplied directly to the volume of solidifying liquid ingot, and thus the improvement in physical properties of plastically worked material.

3

Segregation of elements in corrosion resistant castings of diversified wall thickness

Malatyńska P.

Archives of Metallurgy and Materials

|

2013

|

Vol. 58, iss. 3

775--778

EN

The segregation of elements in two corrosion resistant cast steel grades Cr18-Ni9-Mo, in castings of wall thickness: 7, 15 and 30 mm were performed. The results indicate the analogous path of curves of the content of Fe, Cr, Ni, Mo and C, in walls of various thickness. Decrease in the content observed in the delta ferrite Fe (2 to 3 wt. %), Ni (from 3.5 to 5 wt. %) and C (about 1 wt. %), where the Mo and Cr increased their content of 2% wt. %, and about 6% wt. respectively in the case of the two test cast. For the test steel Q2 with a carbon content 0.054 wt. % were found carbides in the form of white precipitates on the grain boundary of delta ferrite. This resulted in the occurrence of the peaks in the lines of the element distribution analysis especially for molybdenum, iron and carbon, as shown in the diagrams for various segregation of wall thickness.

PL

Zbadano segregację pierwiastków w dwóch gatunkach staliwa kwasoodpornego Cr18-Ni9-Mo, bezpośrednio w odlewach o grubościach ścianek 7, 15 i 30 mm. Wyniki wskazują, analogiczny przebieg krzywych zawartości Fe, Cr, Ni, Mo i C, zebranych w różnych grubościach ścianek. Spadek zawartości odnotowano w ferrycie delta dla Fe (od 2 do 3% wag.), Ni (od 3,5 do 5% wag.) oraz C (około 1%), natomiast w przypadku Mo oraz Cr stwierdzono wzrost zawartości o odpowiednio 2% wag. i około 6% wag., w przypadku dwóch badanych staliw. Dla badanego staliwa Q1 o zawartości węgla 0,054% wag. stwierdzono występowanie węglików w postaci białych wydzieleń na granicy ferrytu delta. Spowodowało to występowanie pików na linii analizy rozkładu pierwiastków zwłaszcza dla molibdenu, zelaża oraz węgla, co zostało uwidocznione na wykresach segregacji dla różnych grubości ścianek.