The Prediction of Optimized Metalloid Content in Fe-Si-B-P Amorphous Alloys Using Artificial Intelligence Algorithm

Lee Min_Woo, Choi Young-Sin, Kwon Do-Hun, Cha Eun-Ji, Kang Hee-Bok, Jeong Jae-In, Lee Seok-Jae, Kim Hwi-Jun

Archives of Metallurgy and Materials

|

2022

|

Vol. 67, iss. 4

1539--1542

EN

Artificial intelligence operated with machine learning was performed to optimize the amount of metalloid elements (Si, B, and P) subjected to be added to a Fe-based amorphous alloy for enhancement of soft magnetic properties. The effect of metalloid elements on magnetic properties was investigated through correlation analysis. Si and P were investigated as elements that affect saturation magnetization while B was investigated as an element that affect coercivity. The coefficient of determination R2 (coefficient of determination) obtained from regression analysis by learning with the Random Forest Algorithm (RFR) was 0.95 In particular, the R2 value measured after including phase information of the Fe-Si-B-P ribbon increased to 0.98. The optimal range of metalloid addition was predicted through correlation analysis method and machine learning.

2

Effect of Fe-Ni substitution in FeNiSiB soft magnetic alloys produced by melt spinning

Kılıçaslan Muhammed Fatih, Yılmaz Yasin, Akgül Bekir, Karataş Hakan, Vurdu Can Doğan

Advances in Materials Science

|

2021

|

Vol. 21, nr 4(70)

79--89

EN

Alloys of FeNiSiB soft magnetic materials containing variable Fe and Ni contents (wt.%) have been produced by melt spinning method, a kind of rapid solidification technique. The magnetic and structural properties of FeNiSiB alloys with soft magnetic properties were investigated by increasing the Fe ratio. X-ray diffraction analysis and SEM images shows that the produced alloy ribbons generally have an amorphous structure, together with also partially nanocrystalline regions. It was observed that the structure became much more amorphous together with increasing Fe content in the composition. Among the alloy ribbons, the highest saturation magnetization was obtained as 0.6 emu/g in the specimen with 50 wt.% Fe. In addition, the highest Curie temperature was observed in the sample containing 46 wt.% Fe.

3

Characterization of magnetic biochar amended with silicon dioxide prepared at high temperature calcination

Baig S. A., Lou Z., Hayat M. T., Fu R., Liu Y., Xu X.

Materials Science Poland

|

2016

|

Vol. 34, No. 3

597--604

EN

Calcination is considered to increase the hardness of composite material and prevent its breakage for the effective applications in environmental remediation. In this study, magnetic biochar amended with silicon dioxide was calcined at high temperature under nitrogen environment and characterized using various techniques. X-ray diffraction (XRD) analysis revealed elimination of Fe3O4 peaks under nitrogen calcination and formation of Fe3Si and iron as major constituents of magnetic biochar-SiO2 composite, which demonstrated its superparamagnetic behavior (>80 Am2·kg-1·) comparable to magnetic biochar. Thermogravimetric analysis (TGA) revealed that both calcined samples generated higher residual mass (>96 %) and demonstrated better thermal stability. The presence of various bands in Fourier transform infrared spectroscopy (FT-IR) was more obvious and the elimination of H–O–H bonding was observed at high temperature calcination. In addition, scanning electron microscopy (SEM) images revealed certain morphological variation among the samples and the presence of more prominent internal and external pores, which then judged the surface area and pore volume of samples. Findings from this study suggests that the selective calcination process could cause useful changes in the material composites and can be effectively employed in environmental remediation measures.

4

Wpływ udziału żywicy epoksydowej epidian 100 na właściwości kompozytów magnetycznych z amorficznym wypełniaczem

Nabiałek M.

Inżynieria Materiałowa

|

2014

|

Vol. 35, nr 6

531--534

PL

W pracy przedstawiono wyniki badań otrzymane dla amorficznej próbki oraz kompozytów złożonych z amorficznego wypełniacza o gradacji cząstki 100÷200 μm połączonych żywicą epoksydową epidian 100, której udział masowy w odniesieniu do amorficznego wypełniacza wynosił 3%. Kompozyty magnetyczne ze względu na dobrą formowalność oraz możliwość projektowania ich parametrów w zależności od wypełniacza, jego wielkości oraz masowego udziału są materiałami, które mogą zastąpić obecnie stosowane rdzenie magnetyczne. Niezależnie od frakcji wypełniacza kompozytu jego mikrotwardość była zbliżona i wynosiła średnio 860 HV. Jak należało się spodziewać wzrost udziału procentowego żywicy Epidian 100 w kompozycie wpłynął na jego właściwości magnetyczne. Obserwowano gwałtowny skok wartości pola koercji i spadek magnetycznej polaryzacji dla kompozytów w porównaniu z litą płytką amorficzną. Wykazano również, że ze zwiększeniem udziału procentowego żywicy dochodzi do stopniowego pogarszania jego właściwości jako materiału magnetycznie miękkiego (zwiększeniet Hc i zmniejszenie μ0M). Należy stwierdzić jednak, że badania kompozytów o właściwościach magnetycznie miękkich są potrzebne dla dalszego rozwoju elektrotechniki, a umieszczone w pracy wyniki są konstruktywne i dają pogląd na badaną grupę kompozytów z amorficznym wypełniaczem i różnym udziałem procentowym lepiszcza.

EN

The paper presents the results obtained for full metal amorphous sample and composite. The composite were consisting of amorphous filler particles of grit 100÷200 μm and epoxy resin Epidian 100. The proportion by weight relative to the amorphous filler was 3%. Magnetic composites due to their good formability. opportunity to design their parameters depending on the filler are materials that can replace currently used magnetic cores. Microhardness of composites studied were similar and averaged 860 HV. The increase in the percentage of resin in the composite Epidian 100 affected its magnetic properties. There was a sharp rise in the value of coercive field and decrease the magnetic polarity of the composites compared to the amorphous solid plate. It was also shown that the increase in the percentage of resin, a gradual deterioration of its properties as a soft magnetic material (increase in Hc and decrease μ0M). It should be noted, however, that the study of composites of soft magnetic properties are needed for the further development of electrical engineering, and placed in the work results are constructive and give a view of the study group composites with amorphous filler based on Fe and different percentage of binder.

5

The influence of resin content on the mechanical and soft magnetic properties of composite prepared on the basis of the bulk amorphous materials

Błoch K., Nabiałek M., Szota M.

Inżynieria Materiałowa

|

2014

|

Vol. 35, nr 2

82--85

EN

The paper presents studies of microstructure, magnetic and mechanical properties of composite prepared on the basis of the bulk amorphous materials. The results presented in this work indicate, that it is possible to generate electrotechnical composite material having a rather high microhardness, which are built in more than 95 wt % of amorphous ferromagnetic metal powder, and the remaining part is Epidian 100 resin. Examined composites were fully amorphous and homogeneous. The homogeneity of the material from which ferromagnetic particles are prepared for composites is an important parameter, which ensures the same properties throughout the entire volume of the composite. Combination of amorphous particles of fraction 100÷200 microns, with the polymeric binder, resulted in a microhardness reduction in relative to the bulk amorphous plate. With increasing weight content of the resin, in the composite, the saturation magnetization significantly decreased, while the coercivity field increased over twentyfold.

PL

W pracy przedstawiono wyniki badań struktury, właściwości magnetycznych i mechanicznych przeprowadzonych dla kompozytów wytworzonych z amorficznych cząstek połączonych żywicą epoksydową. Otrzymane wyniki wskazują, że jest możliwość wytworzenia elektrotechnicznego materiału kompozytowego o dość dużej mikrotwardości zbudowanego w ponad 95% z ferromagnetycznego metalicznego amorficznego proszku, resztę stanowi żywica epidian 100. Badane materiały kompozytowe były w pełni amorficzne i homogeniczne, co oznacza, że rozdrobniony materiał uzyskany z amorficznych płytek miał dobrą jednorodność. Jednorodność materiału, z którego wytwarza się cząstki ferromagnetyczne dla kompozytów jest istotnym parametrem, zapewniającym zachowanie takich samych właściwości w całej objętości kompozytu. Zespolenie amorficznych cząstek o frakcji 100÷200 μm polimerowym lepiszczem wpłynęło na obniżenie mikrotwardości w porównaniu z próbką w postaci płytki. Wraz ze wzrostem zawartości żywicy w kompozycie znacznie zmniejszyła się magnetyzacja nasycenia, natomiast pole koercji wzrosło ponad dwudziestokrotnie.

6

Kompozyty magnetyczne zbudowane na bazie amorficznego wypełniacza o różnych gradacjach połączone lepiszczem epoksydowym

Błoch K.

Inżynieria Materiałowa

|

2014

|

Vol. 35, nr 6

455--458

PL

W pracy przedstawiono wyniki badań struktury oraz właściwości magnetycznych przeprowadzonych dla kompozytów wytworzonych z amorficznych cząstek połączonych żywicą epoksydową. Badane materiały kompozytowe były w pełni amorficzne. Zespolenie amorficznych cząstek ferromagnetycznych z polimerowym lepiszczem wpłynęło na pogorszenie właściwości magnetycznych w porównaniu z próbki w postaci płytki. Dodatkowo zmniejszenie gradacji cząstek ferromagnetycznych powoduje zmniejszenie magnetyzacji nasycenia oraz zwiększenie pola koercji przy takim samym udziale masowym żywicy epidian 100 dla każdej gradacji.

EN

The paper presents studies of microstructure and magnetic properties of composites made of amorphous particles and epoxy resin. Examined composites were fully amorphous. Combination of ferromagnetic particles with the polymeric binder, contributed to the deterioration of the magnetic properties in relative to the bulk amorphous full metal samples. In addition, reducing the gradation of ferromagnetic particles causes decrease of the saturation magnetization and increase of coercivity, with the same wt content of the Epidian 100 resin for each gradation.