Effect of carburization and thermal shocks on structure of Al-Si casting coatings

Kubicki J., Kochmańska A.

Archiwum Odlewnictwa

2001

R. 1, nr 2

212--219

The purpose of this paper is to describe the changes of the structure of Al-Si coatings after carburization and thermal fatigue. The coatings were produced on GX25NiCrSi3617 cast steel directly in a casting mould. The carburization changes essentially the structure of coatings (especially the ferritic ones), what results in an increase in fractions of carbides (M7C3) and solution &gamma(Fe,Ni), which is accompanied by a simultaneous decrease in the fraction of &alpha(Ni, Cr, Fe) and &betaAlNi. However, for both coatings of the ferritic and austenitic structure, the depth of carburization was reduced by 75% and 55% respectively, in comparison with the material unprotected by a coating.

W pracy opisano strukturę powłok Al-Si wytwarzanych na staliwie L25H17N36S bezpośrednio w formie odlewniczej, koncentrując się na zmianach wywołanych nawęglaniem i zmęczeniem cieplnym. Nawęglanie powoduje istotne zmiany w strukturze powłok (zwłaszcza ferrytycznych) polegające głównie na wzroście udziału węglików M7C3 i roztworu &gamma(Fe,Ni) przy jednoczesnym spadku zawartości α(Ni,Cr,Fe) oraz &betaAlNi. Niezależnie od tych zmian badane powłoki zależnie od struktury wyjściowej wykazały: o 75% (ferrytyczne) i o 55% (austenityczne) mniejszą głębokość nawęglania niż materiał odlewu nie zabezpieczony powłoką.

Structure and properties of casting coatings Al-Si.

Kubicki Jerzy

Advances in Manufacturing Science and Technology

2000

Vol. 24, nr 4

145-156

In this paper the structure and the ability to protect the castings made from GX25NiCrSi36-17 cast steel against carburization with the use of the coatings produced directly in a casting mould have been described. To analyse the structure the following methods of testing were used: an optical and electron microscopy, X-ray microanalysis, X-ray diffraction and quantative image analysis. It can be stated that depending on a silicon carrier used in the investigation (FeSi or Si) the coatings having either the austenitic structure (main constituent gamma(Cr, Fe, Ni)) or ferritic structure (main constituated alpha(Ni, Cr, Fe)) can be obtained. Moreover, in the coatings are also presented: betaAlNi. gamma(Fe, Ni), M23C6, and additionally in the ferritic coatings - (Cr, Si)3Ni2Si. The carburization and thermal fatigue cause the formation of a brittle scale on the surface of the coatings, so the investigated coatings provide only temporary protection of the casting material. Moreover, the carburization changes essentially the structure of the coatings which, after this process (independently of the primary structure), consist of the solution gamma(Fe, Ni) mixture beta'AlNi + alpha(Ni, Cr, Fe) + gamma(Cr, Fe, Ni) and the carbides M23C6 and M7C3. However, for both coatings of the ferritic and austenitic structure the depth of carburization was reduced by 75% and 55% respectively, in comparison with the casting material unprotected by the coating.

W pracy opisano strukturę i zdolność zabezpieczania odlewów ze staliwa GX25NiCrSi36-17 przed nawęglaniem przez powłoki Al-Si, wytwarzane bezpośrednio w formie odlewniczej. Do analizy struktury powłok zastosowano: mikroskopię świetlną i elektronową wraz z mikroanalizą rtg, dyfrakcję rentgenowską, a także ilościową analizę obrazu. Stwierdzono, że w zależności od użytego nośnika krzemu (FeSi or Si) można uzyskać powłoki o strukturze austenitycznej (główny składnik gamma(Cr, Fe, Ni)) lub ferrytyczny (główny składnik alfa(Ni, Cr, Fe)). Ponadto w powłokach występują: betaAlNi. gamma(Fe, Ni), M23C6 i w powłokach ferrytycznych dodatkowo (Cr, Si)3Ni2Si. Nawęglanie i zmęczenie cieplne powoduje powstanie na powierzchni powłok kruchej zgorzeliny. Badane powłoki stanowią więc czasową ochronę materiału odlewu. Ponadto nawęglanie istotnie zmienia strukturę powłok (niezależnie od struktury wyjściowej). Powłoka jest złożona z roztworu gamma(Fe, Ni), mieszaniny beta'AlNi + alpha(Ni, Cr, Fe) + gamma(Cr, Fe, Ni) oraz węglików M23C6 i M7C3. Powłoki o strukturze ferrytycznej niezależnie od tych zmian wykazały o 75%, a austenitycznej o 55% mniejszą głębokość nawęglania niż materiał odlewu niezabezpieczony powłoką.