Influence Of Cooling Rate On Phase Composition And Magnetic Properties Of Sm12.5Co66.5Fe8Cu11Si2 Alloy In The Form Of Ribbon In As-Quenched State

Dośpiał M., Nabiałek M., Błoch K.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2A

667--670

The fabrication method and magnetic properties of Sm12.5Co66.5Fe8Cu11Si2 alloy are presented in this article. The samples were produced by rapid quenching of the liquid alloy onto a rotating, copper wheel (the so-called ‘melt-spinning’ method) and they had a thin ribbon shape. The microstructure of the samples was investigated by measurements of diffraction patterns for powdered samples, in order to obtain data from the entire volume of the sample. It was found, that samples were composed of different amounts of Sm2Co17, SmCo5 and SmCo7 phases, depending on the linear velocity of the copper wheel used during the fabrication process. The magnetic measurements were performed using a vibrating sample magnetometer (LakeShore VSM) working with an external magnetic field of up to 2 T. It was found that the obtained ribbons displayed relatively good hard magnetic properties, such as remanence μ0MR, and high resistance to demagnetization fields JHC.

W pracy badano wpływ warunków wytwarzania na własności magnetyczne i skład fazowy stopu Sm12.5Co66.5Fe8Cu11Si2 w stanie po zestaleniu. Próbki stopu zostały otrzymane przy użyciu metody szybkiego chłodzenia na miedzianym wirującym bębnie (ang. melt-spinning) i miały postać cienkich taśm. Badania struktury zostały wykonane przy użyciu dyfraktometru rentgenowskiego. W celu otrzymania danych z całej objętości próbki badania składu fazowego zostały przeprowadzone dla sproszkowanych próbek. Dla otrzymanych dyfraktogramów przeprowadzono analizę jakościową i ilościową (Rietvelda) składu fazowego. Na podstawie otrzymanych wyników stwierdzono, że próbki składały się z różnych zawartości faz Sm2Co17, SmCo5 i SmCo7. Nawet niewielkie zmiany w szybkości chłodzenia skutkują znacznymi różnicami w składzie fazowym stopu. Własności magnetyczne próbek zostały wyznaczone przy użyciu magnetometru wibracyjnego (LakeShore VSM), przy zastosowaniu zewnętrznego pola magnetycznego o wartości 2T. Różna zawartość faz oraz rozmiary ziaren w otrzymanych próbkach powodowały znaczne różnice w wartościach parametrów magnetycznych.

Structure and magnetic properties of high coercivity, nanocrystalline alloy based on Nd-Fe-B compound with overstoichiometric Nd content

Dośpiał M., Nabiałek M., Szota M.

Inżynieria Materiałowa

2011

Vol. 32, nr 4

385-387

The production method as well as investigations of the microstructure and magnetic properties of alloy based on Nd-Fe-B compound were presented. The investigated materials were produced in the form of thin ribbons, using melt-spinning method. In order to obtain the relevant magnetic parameters the alloy composition was selected, to include the number of elements corresponding to the overstoichiometric Nd content in comparison to composition of Re2Fe14B phase. The obtained material, due to the presence of thin, isolating layer between the grains with width of about 2 nm, was characterized by a very good functional parameters such as high maximum energy product {BH}max and high resistance to demagnetization fields JHC. Despite of large moderate grain size (of about 160 nm) and presence of isolating layer between grains, resulting in reduction of grains exchange interactions, alloy also showed a relatively high remanence u0Mr.

W pracy przedstawiono metodę produkcji oraz wyniki badań mikrostruktury i własności magnetycznych stopów na bazie związku Nd-Fe-B. Do wytworzenia materiałów wykorzystano metodę szybkiego chłodzenia stopu na miedzianym wirującym bębnie (tzw. melt-spinning). Otrzymany materiał miał postać taśm o niewielkiej grubości. W celu uzyskania odpowiednich parametrów magnetycznych skład stopu dobrano tak, aby zawierał nadmiarowe ilości pierwiastków ziemi rzadkich w stosunku do składu stechiometrycznego fazy Re2Fe14B. Otrzymany materiał charakteryzował się bardzo dobrymi parametrami funkcjonalnymi, tj. znaczną gęstością energii magnetycznej (BH)max i dużą odpornością na zewnętrzne pola odmagnesowujące (tj. dużą koercją JHC). Stop wykazywał również względnie wysoką remanencję.