The Effect of Alloying on Mechanical Properties of Advanced High Strength Steels

Kučerová L., Jirkova H., Mašek B.

Archives of Metallurgy and Materials

2014

Vol. 59, iss. 3

1189--1192

Quenching and partitioning process with incorporated incremental deformation was optimized for six high strength steels with various contents of carbon (0.4-0.6%), manganese (0.6-1.2), silicon (2-2.6%) and chromium (0.8-1.3%). The optimization was gradually done for each steel with respect to the final microstructures and properties. The effect of cooling rate, quenching and partitioning temperature on microstructure development was further investigated. Interesting combinations of mechanical properties were obtained, with tensile strength in the region of 1600-2400 MPa and ductility of 6-20%.

Przeprowadzono optymalizacje procesu hartowania i partycjonowania węgla (Quenching and Partitioning – Q&P) w połączeniu ze stopniowymi przyrostami odkształcenia dla sześciu wysokowytrzymałych stali o różnej zawartości węgla (0, 4-0, 6%) manganu (0, 6-1, 2%), krzemu (2-2, 6%) oraz chromu (0, 8-1, 3%). Optymalizacje prowadzono dla kazdej stali stopniowo pod katem końcowej mikrostruktury i właściwości. Następnie przeprowadzono badania wpływ szybkości chłodzenia oraz temperatury hartowania i partycjonowania na rozwój mikrostruktury. W rezultacie otrzymano interesujące kombinacje właściwości mechanicznych stali o wytrzymałości na rozciąganie w zakresie 1600-2400 MPa oraz ciągliwości w zakresie 6-20%.