The effectiveness of the “T”-brand coal processing sludge, technical pyrocarbon, and their mixture as adsorbents for the decontamination of drainage water from organic pollutants has been investigated. The contaminated water samples were collected from the ordinary car filling/service station’s drainage system and then treated with the adsorbents. Water absorbance and chemical oxygen demand (COD) were controlled as the water quality and decontamination effectiveness parameters. A 4:1 mixture of coal refinery sludge and technical pyrocarbon was used as the most efficient adsorbent for mixed petrochemical and mechanical pollution agents. It has been found that this composition effectively decontaminates water from mixed organic pollutants. The water cleaning cartridges filled with this composition of adsorbents showed high decontamination performance eliminating about 85 % of petrochemical water pollution agents. This performance does not degrade much, and a 4 kg adsorbent load should be sufficient to treat an amount of wastewater formed at the car filling station for at least one month.
PL
Zbadano skuteczność szlamu z przeróbki węgla marki "T", pirocarbonu technicznego i ich mieszaniny jako adsorbentów do odkażania wody drenażowej z zanieczyszczeń organicznych. Zanieczyszczone próbki wody zostały pobrane z systemu odwadniającego zwykłej stacji obsługi samochodów, a następnie poddane działaniu adsorbentów. Absorpcja wody i chemiczne zapotrzebowanie tlenu (ChZT) były kontrolowane jako parametry jakości wody i skuteczności dekontaminacji. Jako najskuteczniejszy adsorbent dla mieszanych zanieczyszczeń petrochemicznych i mechanicznych zastosowano mieszaninę 4:1 szlamu z rafinerii węgla i pirocarbonu technicznego. Stwierdzono, że kompozycja ta skutecznie odkaża wodę z mieszanych zanieczyszczeń organicznych. Wkłady do oczyszczania wody wypełnione tą kompozycją adsorbentów wykazały wysoką skuteczność odkażania, eliminując około 85% petrochemicznych zanieczyszczeń wody. Wydajność ta nie ulega znacznemu pogorszeniu, a 4 kg adsorbentu powinno wystarczyć do oczyszczenia ilości ścieków powstających na stacji benzynowej przez co najmniej miesiąc.
It has been proven that the use of coal-like adsorbents with the mosaic and hydrophobic surface structure is efficient in cleaning the wastewater from a wide range of pollutants under the condition of their uncontrolled release from various small enterprises. is range includes such environmentally dangerous agents as petrochemicals and other pollutants formed at car filling, carwash stations or other similar facilities. Technical pyrocarbon and the coal refinery sludges are readily available waste materials with high porosity, which exhibit some adsorption activity and can be utilized in water/wastewater treatment solutions. en the adsorbents can be either disposed of at the landfill areas or incinerated as components of some secondary fuels. e highest adsorption performance is achieved for the sorbent mixture of the refinery sludges and technical pyrocarbon with the ratio of the components 4:1. If the wastewater is flowing through this composition, the degree of petrochemicals removal reaches 75-80% for the mixture sludge/ technical pyrocarbon, while the pure pyrocarbon ensures the removal degree of 15-20% only. ough adsorption efficiency under stationary conditions (keeping the adsorbent and the wastewater in contact inside some decontamination pond/vessel for at least 24 h) is higher, this option is hard-to-realize for a small car service/wash station. As an alternative, comparatively small wastewater cleaning cartridges filled with the 4:1 mixture of coal sludge and technical pyrocarbon can be recommended for preliminary decontamination of the wastewater formed at such enterprises before their discharge to the local municipal sewerage lines.
PL
Wykazano, że zastosowanie adsorbentów węglopochodnych o mozaikowej, hydrofobowej strukturze powierzchni skutecznie oczyszcza ścieki z szerokiej gamy zanieczyszczeń. Adsorbowane są niebezpieczne dla środowiska substancje takie jak produkty petrochemiczne i inne zanieczyszczenia powstające na stacjach paliw, myjniach samochodowych lub innych podobnych obiektach. Techniczny karbonizat węglowy i szlamy z rafinerii węgla są łatwo dostępnymi materiałami odpadowymi o wysokiej porowatości, które wykazują pewną aktywność adsorpcyjną i mogą być wykorzystywane do oczyszczania wody/ścieków. Następnie adsorbenty mogą być albo składowane na składowiskach odpadów, albo spalane jako składniki niektórych paliw wtórnych. Najwyższą wydajność adsorpcji uzyskuje się dla mieszaniny sorbentów z osadów rafineryjnych i karbonizatu technicznego o stosunku składników 4:1. Jeżeli ścieki przepływają przez tę kompozycję, stopień usunięcia petrochemikaliów osiąga 75-80% dla mieszaniny osad/karbonizat techniczny, podczas gdy czysty karbonizat zapewnia stopień usunięcia tylko 15-20%. Chociaż wydajność adsorpcji w warunkach stacjonarnych (utrzymywanie adsorbentu i ścieków w kontakcie w naczyniu dekontaminacyjnym przez co najmniej 24 godziny) jest wyższa, ta opcja jest trudna do zrealizowania w przypadku małych stacji obsługi/myjni samochodowych. Jako alternatywę można polecić stosunkowo niewielkie wkłady do oczyszczania ścieków wypełnione mieszaniną mułu węglowego 4:1 i technicznego karbonizatu do wstępnego odkażania powstających w tego typu przedsiębiorstwach ścieków przed ich odprowadzeniem do lokalnych miejskich sieci kanalizacyjnych.
The formation of the pyrocarbon in the roof of the coke-oven battery chamber was examined in many works [1-5]. In order to use the theoretical information in the operating conditions of the coke-oven plant in Tfinec practically, the MS3 device for the continuous monitoring of the temperature changes of pressure and weight of the refractory material in the roof of the coke-oven battery chamber was developed. Carbonisation tests of single components of the coking blend were carried out after the trial tests (possible from the point of view of the coke-oven battery operation). The experiences gained through the trial testing enabled us to plan the tests so that we can meet the constant temperature profile of the coke-oven battery (constant temperature conditions) and to change just the charge quality. The carried out tests approved the statistically significant difference of the pyrocarbon formation during the coking of various coking blend components.
PL
Zjawisko wytwarzania się osadów grafitu w przestrzeni podsklepieniowej komory koksowniczej jest przedmiotem wielu prac badawczych. W celu wykorzystania wyników badań w skali przemysłowej, w zakładzie koksowniczym skonstruowano urządzenie MS3, umożliwiające stale pomiary: temperatury oraz zmian ciśnienia i masy próbki materiału ceramicznego umieszczonego w przestrzeni podsklepieniowej. Po zakończeniu fazy testowania urządzenia przeprowadzono testy koksowania, podczas których obsadzano komory poszczególnymi komponentami wsadu węglowego (uwzględniając bezpieczną eksploatację baterii koksowniczej). Doświadczenia zdobyte podczas fazy testowania urządzenia umożliwiły takie zaplanowanie eksperymentu, aby podczas zmian wsadu węglowego uzyskać stały stan cieplny baterii koksowniczej.
Dokonano histopatologicznej oceny kompozytu węgiel-węgiel pokrytych pirowęglem i hydroksyapatytem. Oceniono zachowanie się kompozytu węgiel-żywica epoksydowa w tkance kostnej królika. Do badań doświadczalnych użyto 24 młode króliki w okresie wzrostu kostnego. Okres obserwacji i prowadzenia doświadczenia wynosił pięć miesięcy. Oceniono histopatologicznie wpływ tych biomateriałów na procesy przebudowy kości. Przeprowadzone badania histopatologiczne wybranych narządów wewnętrznych nie wykazały zmian związanych z procesem degradacji wszczepionego materiału.
EN
Histopathoiogical evaluation of carbon-carbon composites coated with pyrocarbon and hydroxyapatite was performed. The behaviour of carbon-epoxy resin-composite in the bone tissue of a rabbit was evaluated. 24 rabbits in their bone developmental period were used in the experiment. The observation period end the experiment itself lasted 5 months. The influence of these biomaterials on the processes of bone rebuilt was histopatologically evaluated. Histopathological examinations of chosen internal organs did not show any changes related to the process of degradation of the implant.
Podjęte badania kompozytu węglowego na wybranym do doświadczenia modelu zwierzęcym jakim był królik w okresie wzrostu kostnego miały wykazać przydatność tego materiału w chirurgii dziecięcej, szczególnie w traumatologii. Do doświadczenia użyto 16 królików, którym wszczepiono do światła kanału szpikowego grot węglowy. Materiał doświadczalny podzielono na trzy grupy w zależności od sposobu pokrycia podstawowego kompozytu węgiel-węgiel. W pracy przeprowadzono badania strefy rozdziału implant węglowy-tkanka kostna oraz powierzchni bocznej implantu węglowego. Obserwacje prowadzono elektronowym mikroskopie skaningowym DSM - 940 firmy OPTON. Dla potrzeb badań przygotowano przekroje poprzeczne implantu węgłowego łącznie z tkanką kostną. We wszystkich postaciach badanego kompozytu obserwowano postępującą od obwodu implantu biodegradację oraz powstawanie na tym miejscu nowej tkanki kostnej. W oparciu o przeprowadzone obserwacje uzyskano zachęcające wyniki doświadczalne stwarzające kliniczne możliwości zastosowania tych materiałów w traumatologii dziecięcej.
EN
Behaviour of carbon composite implanted in an animal model, being rabbit in the period of the osseous tissue growth, was examined in order to assess the usability of this material in paediatric surgery, especially in traumatology. Sixteen rabbits were used for the experiment in which carbon pin was inserted into the marrow cavity. The experimental material was divided into three groups. depending on the way the basic carbon-carbon composite was coated. Investigations of the carbon implant - bone tissue separation zone and of the lateral surface of the carbon implant were carried out within the project framework. Observations were carried out under the OPTON DSM-940 scanning electron microscope (SEM). Cross-sections of the carbon implant along with the bone tissue were prepared for the examination. In all investigated cases, biodegradation progressing from the implant circumference was observed as well as development of a new bone tissue at the same place. The encouraging experimental results obtained in this work indicate that clinical use of these materials in the paediatric traumatology is possible.