Comparative Study on Carded Cotton Yarn Properties Produced by the Conventional Ring and New Modified Ring Spinning System

Buharali Gozde, Omeroglu Sunay

Fibres & Textiles in Eastern Europe

|

2019

|

Vol. 27, no. 2 (134)

45--51

EN

In this paper, the properties of yarns which were produced by using a modified ring spinning system (ProSPIN®) and conventional ring spinning system were comparatively investigated. The modified spinning system which was used in yarn production has basically the characteristic of compact spinning system and is at present used especially in the production of mid-count yarns. In this study, conventional ring yarns and equivalent modifiedring spun yarns were produced with different yarn counts and twists using 100% carded cotton raw material. Tests were conducted to determine the tensile, unevenness, imperfection and hairiness properties of the yarns. It was found that the modified ring spun yarns showed considerable positive differences in some yarn properties compared with conventional ring yarns. The differences in tenacity values were more evident especially in yarns with lower twist coefficients, while differences in hairiness values were more so in finer yarns. Also the unification of two separate and compacted fibre strands during yarn formation ensures better values for both mass irregularity and IPI because of the doubling effect.

PL

W niniejszym artykule porównano właściwości przędz, które zostały wytworzone przy użyciu zmodyfikowanego systemu przędzenia obrączkowego (ProSPIN®) i konwencjonalnego systemu przędzenia obrączkowego. Zmodyfikowany system przędzenia, który był stosowany w produkcji przędzy, ma zasadniczo charakterystykę kompaktowego systemu przędzenia i jest obecnie wykorzystywany w szczególności do produkcji przędzy o średnim numerze. Wytworzono konwencjonalne przędze obrączkowe i zmodyfikowane przędze obrączkowe z różnymi skrętami z użyciem 100% zgrzebnego surowca bawełnianego. Przeprowadzono testy w celu określenia właściwości rozciągania, nierówności, niedoskonałości i włochatości przędz. Stwierdzono, że przędze obrączkowe wytworzone nowym sposobem wykazują znaczne różnice w niektórych właściwościach przędz w porównaniu z konwencjonalnymi przędzami obrączkowymi. Różnice w wartościach wytrzymałości na rozciąganie były bardziej widoczne, zwłaszcza w przędzach o niższych współczynnikach skrętu, podczas gdy różnice we włochatości były bardziej widoczne w cieńszych przędzach. Również ujednolicenie dwóch oddzielnych i sprasowanych pasm włókien podczas tworzenia przędzy zapewnia lepsze wartości zarówno dla nieregularności masy jak i IPI z powodu efektu podwojenia.

2

Investigation on Thermal Comfort Characteristics of Regenerated Bamboo and Cotton Woven Structured Fabrics

Abro Z. A., Chen N., Yifan Z., Cheng-Yu H., Abassi A. M. R., Simair A. A., Ahmed R., Hussain A.

Autex Research Journal

|

2018

|

Vol. 18, no. 4

323--329

EN

In this research work, thermal properties of plain woven fabrics generated from regenerated bamboo and cotton fiber blended yarns were investigated. Seven mixtures of fiber (100% bamboo, 100% cotton, 10:90 bamboo: cotton, 20:80 bamboo: cotton, 30:70 bamboo: cotton, 40:60 bamboo: cotton and 50:50 bamboo: cotton) were developed to create 60 Tex ring spun yarn. The warp yarns were used as 100% regenerated bamboo and the bamboo: cotton blends were used alternatively in weft to produce plain woven fabrics. The plain structured woven fabrics show eminent thermal comfort properties with the blending of regenerated bamboo fibers. The air permeability of 100% regenerated bamboo fiber was recorded higher than the compared blends; the increased key factor contents of bamboo changed the air properties of the fabric. Furthermore, plain woven fabric of bamboo/cotton (50/50) has shown greater thermal conductivity and heat retention properties. The work reported in this paper is ensuring highpoints of thermal comfort properties of regenerated bamboo (100%) and cotton (100%) with plain woven structured fabrics, and potentially, the fabrics can be used for winter suiting apparel products.

3

Właściwości użytkowe i kierunki zastosowań wyrobów włókienniczych wytwarzanych z przędz bezwrzecionowych nowej generacji

Józkowicz I., Lewandowski S., Czempka K.

Przegląd Włókienniczy - Włókno, Odzież, Skóra

|

2017

|

nr 6

20--26

PL

Przeprowadzono ocenę porównawczą właściwości fizycznych i użytkowych tkanin i dzianin wytworzonych z przędz obrączkowych, rotorowych i przędz pneumatycznych air-jet nowej generacji. Analizowano wygląd gotowych wyrobów, odporność na zmechacenie (pilling) i odporność na ścieranie, zdolność pochłaniania wilgoci i odporność na pranie, skłonność do wydzielania pyłu włókiennego, skurcz tkaniny po praniu, a także trwałość barwy tkaniny po praniu. W drugiej części artykułu zaprezentowano liczne przykłady zastosowań wyrobów włókienniczych wytworzonych z przędz pneumatycznych air-jet VORTEX. Stwierdzono, że wymienione przędze mogą być wykorzystywane, zarówno do wyposażenia gospodarstw domowych, jak również produkcji wszelakiego rodzaju odzieży.

EN

A comparative assessment of the physical and functional properties of fabrics and knitted fabrics produced from classic ring spun yarns, rotor yarns and new generation of air-jet VORTEX yarns. The appearance of finished products, pilling and abrasion resistance, moisture absorption and washing resistance, tendency to produce fiber dust, shrinkage of fabric after washing, and color fastness after washing were analyzed. The second part of the paper presents numerous examples of textile applications made from air-jet VORTEX spun yarns. It has been found that these yarns can be used for both home furnishings and the production of all kinds of clothing.

4

A Comparative Study of Hooks in the Yarns Produced by Different Spinning Technologies

Ghosh A., Das S., Mal P.

Autex Research Journal

|

2015

|

Vol. 15, no. 4

260--265

EN

This article presents a comparative study of hooks’ characteristics of ring, rotor, air-jet and open-end friction spun yarns. Hook types and their extent, spinning in-coefficient and mean fibre extent in the yarns produced on different spinning technologies are investigated. The results show that the hook extents for open-end friction spun yarn are the highest followed by rotor, ring and air-jet spun yarns. Ring and air-jet spun yarns have higher percentage and extent of trailing hook as compared with leading hook, whereas, rotor and friction spun yarns show the reverse trend.

5

Fibre Number of the Cross-section of Ringspun Yarn and its Strength Prediction Model

Zhang H. W., Li Y. L.

Fibres & Textiles in Eastern Europe

|

2014

|

Vol. 22, no. 6 (108)

38--40

EN

A calculation equation of the fibre number on the cross-section of ring-spun yarn was deduced theoretically and verified with test data of 20 representative pure cotton ring spun yarns. The equation is practical and convenient to use by substituting the yarn count, yarn twist, and fibre decitex. On the basis of the above equation, a yarn strength predication model was established. The revising functions of yarn count and twist to yarn strength were deduced in practical tests of the strength of 20 commonly used ring-spun yarns, and were used to revise the yarn strength predication model obtained. Substituting the fibre decitex, fibre strength, yarn count, yarn twist and yarn strength can be precisely calculated with this model.

PL

Przeprowadzając teoretyczne rozważania autorzy opracowali matematyczny wzór dotyczący liczby włókien w przekroju poprzecznym przędzy obrączkowej. We wzorze tym uwzględnili oddziaływanie: kształtu przekroju poprzecznego włókien i przędzy, masy liniowej włókien i przędzy, gęstości właściwej włókien i przędzy. Zaproponowane równanie pozwala projektować zamienniki przędzy pod względem ich masy liniowej (tex), liczby skrętu i masy liniowej włókien (tex). Traktując rozpatrywane równanie jako punkt wyjścia autorzy opracowali model przewidywania wytrzymałości przędzy. Otrzymane zależności teoretyczne zweryfikowano poprzez badania eksperymentalne. Przebadano 20 powszechnie stosowanych przędz obrączkowych. Opracowane modele pozwalają precyzyjnie obliczyć wytrzymałość przędzy obrączkowej.

6

Mechanical properties of ultrasonic washed organic and traditional cotton yarns

Uzun M., Patel I.

Journal of Achievements in Materials and Manufacturing Engineering

|

2010

|

Vol. 43, nr 2

608--612

EN

Purpose: The demand of natural and eco-friendly products have undergone tremendous growth after the awareness and realization of global ecological concerns. In this study we have used a novel product (organic cotton) and a novel system (ultrasonic), both having critical importance to environmental pollution. Cotton is one of the oldest and most abundant natural, biodegradable and renewable fibres. Although numerous synthetic fibres have been produced, cotton is still the most important fibre because of its unique physical properties like durability, strength and absorbency, furthermore, only 10% of the raw weight is lost during processing. Organic farming does not have any negative impact due to its natural growing abilities, in which the seeds genetic are not modified and no chemicals such as disinfect or fertilizer are used. Ultrasonic washing has many advantages such as the extra cleanliness of textile materials, reducing process time, energy and chemicals which are used in the washing process. In addition ultrasonic agitation brings less fibre migrations than conventional washing. Design/methodology/approach: The experimental section reports on the characterization of the organic and conventional cotton that were washed by using an ultrasonic process. Both of the cotton types that used in this study were Turkish cottons and manufactured by ring spinning system. The yarn samples were applied with two different washing temperatures (30°C and 40°C) and three different washing times (10, 20 and 30 minutes). The following stage of ultrasonic and conventional washing physical properties (yarn count, twist, tensile strength, elongation etc) was investigated and comparisons were made. Findings: The investigation presented in this study indicates benefits of employing ultrasonic washing and organic cotton farming. Research limitations/implications: The properties of yarn washed with ultrasonic energy shows better properties than those of yarns washed with conventional washing technique. The results confirms that ultrasonic washing has some advantages such as less processing time, less chemical and water consumptions compared to conventional washing methods. Originality/value: Organic cotton has a potential to substitute traditional cotton providing crop harvesting cost is significantly reduced.

7

Analysis of the breaking characteristics of twisted yarns

Stepanovic J., Radivojevic D., Petrovic V., Golubovic S.

Fibres & Textiles in Eastern Europe

|

2010

|

Vol. 18, no. 2 (79)

40--44

EN

In many cases single yarns do not fulfill the requirements necessary for the production of certain types of textiles. At the same time, they do not have most of the characteristics that are important for textile production with outstanding quality parameters. Therefore, the twisting process is employed to produce twisted yarns which can be used to produce fabrics for various applications. The breaking properties of twisted yarn depend on the strength of the component yarns, the number of strands, the twisting amount, the friction forces between the yarns, as well as on the twisting method used. The use of known parameters of twisted yarns determines the relations defining their breaking force. The breaking force is here defined as a function of the breaking forces of the component yarns, the number of yarns twisted in the yarn, and their angle to the twisted yarn axis. In addition, based on experimental results and the theoretical equations, real mathematical relations were established which can serve to project the breaking forces of ring and rotor twisted yarns obtained by the method of double layer twisting. This will simplify and improve the technical preparation of the weaving process.

PL

W wielu przypadkach pojedyncze przędze nie spełniają wymagań wytrzymałościowych użytkowników oraz często nie posiadają odpowiednich parametrów jakościowych wymaganych dla produkcji określonych asortymentów. Dlatego stosuje się proces skręcania przędz pojedynczych. Wytrzymałość przędz skręcanych zależy od wytrzymałości przędz składowych, ilości komponentów, wielkości skrętu, sił tarcia pomiędzy przędzami, oraz zastosowanej metody skręcania. Siła zrywania skręconej przędzy została określona jako funkcja wytrzymałości przędz składowych, ich ilości przędz oraz konta skręcania w stosunku do osi przędzy. Na podstawie teoretycznych rozważań oraz obserwacji eksperymentalnych opracowano zależności, które mogą stanowić podstawę określania siły zrywania wytworzonych przez skręcanie przędz obrączkowych i rotorowych. Pozwala to uprościć odpowiednie przygotowanie procesu tkania.

8

Pilling Performance and Abrasion Characteristics of Plain - Weave Fabrics Made from Open : End and Ring Spun Yarns

Can Y.

Fibres & Textiles in Eastern Europe

|

2008

|

Vol. 16, no. 1 (66)

81--84

EN

In this experimental study, plain fabrics made from100% cotton ring carded, ring combed and OE rotor spun yarns were produced. The weft yarn count, warp yarn count and fabric sett of the fabrics were constant. The pilling and abrasion resistance of the fabrics were investigated. After that the relationships between yarn characteristics and abrasion resistance and pilling were investigated. Finally the relationships between abrasion resistance and pilling were investigated for every group of fabrics. The results show that the arithmetic means of abrasion resistance and pilling performance have a maximum value in fabrics made from OE rotor spun yarns. The arithmetic means of abrasion resistance and pilling performance have a minimum value in fabrics made from ring carded spun yarns. Whereas standard deviations in fabric made from OE rotor spun yarns have a maximum value, standard deviations in fabric made from ring combed spun yarns have a minimum value for both fabric characteristics. The important relationships between yarn hairiness and abrasion resistance and pilling were obtained in all the fabrics. Additionally, the important relationships between abrasion resistance and pilling were obtained for all the fabrics. All correlation coefficients were found as negative. The correlation coefficient of fabrics made from ring combed spun yarns has a maximum value. The correlation coefficient of fabrics made from OE rotor spun yarns has a minimum value without taking into account the fact that it is negative or positive.

PL

Dla testów wyprodukowano tkaniny o splocie płóciennym z przędz rotorowych i obrączkowych ze 100% zgrzeblonej bawełny. Tkaniny wykonano z przędz o tej samej masie liniowej oraz identycznej gęstości osnowy i wątku. Badano odporność na piling i ścieranie wyprodukowanych tkanin. Zależności pomiędzy odpornością na ścieranie i piling były porównywane między każdą z grup tkanin. Stwierdzono, że średnie arytmetyczne wyników testów odporności na ścieranie i piling mają swoje maksimum dla tkanin wykonanych z przędz rotorowych. Podczas gdy minimum leży w zakresie tkanin wykonanych z przędz obrączkowych. Natomiast odchylenia standardowe mają swoje maksimum dla tkanin z przędz rotorowych a minimum dla tkanin z przędz obrączkowych dla obydwu parametrów. Określono również ważną zależność pomiędzy włochatością przędz a odpornością na ścieranie i piling oraz zależność pomiędzy odpornością na ścieranie i pilingiem dla wszystkich tkanin. Wszystkie współczynniki korelacji były ujemne. Współczynnik korelacji tkanin z przędz obrączkowych ma maksimum podczas gdy współczynnik korelacji dla tkanin z przędz rotorowych ma minimum niezależnie od tego czy jest dodatni czy ujemny.

9

Investigation of Regenerated Bamboo Fibre and Yarn Characteristics

Erdumlu N., Ozipek E.

Fibres & Textiles in Eastern Europe

|

2008

|

Vol. 16, no. 4 (69)

43--47

EN

This article presents general characteristics and current applications of regenerated bamboo fibre in the textile industry. In the experimental part of the study, 100% regenerated bamboo yarns of six different counts (11.8, 14.8, 16.4, 19.7, 24.6 and 29.5 tex) were produced from bamboo fibre using ring yarn spinning technology. Subsequently, the physical parameters of related yarns produced in spinning mill conditions were tested, and the results were evaluated according to the parameters of 100% viscose rayon, as well as 100% carded and combed ring spun yarn in Uster statistics. In this way, the aim was to state the strength and weakness of bamboo fibre and to predict its future in the textile industry

PL

Przedstawiono ogólną charakterystykę regenerowanych włókien bambusowych oraz możliwości ich zastosowania w przemyśle tekstylnym. Część eksperymentalna przedstawionych badań dotyczyła regenerowanych włókien bambusowych o sześciu masach liniowych (11,8; 14,8; 16,4; 19,7; 24,6 i 29,5 tex). Włókna przędziono na przędzarce obrączkowej, a następnie włókna otrzymane w warunkach określonej przędzalni były badane a wyniki porównywano ze 100% wiskozową przędzą ciągłą oraz zgrzebloną i czesaną przędzą obrączkową, biorąc jako odniesienie charakterystyki Ustera. Badania pozwoliły na określenie zalet i wad włókien bambusowych i możliwości ich zastosowania w przemyśle włókienniczym.

10

A comparative quality optimisation between ring spun and slub yarns by using desirability function

Souid H., Babay A., Sahnoun M., Cheikrouhou M.

Autex Research Journal

|

2008

|

Vol. 8, no. 3

72--76

EN

The present study was conducted to develop a credible approach to determine the quality of ring spun and slub yarns by virtue of criteria incorporating combinations of the fundamental fiber characteristics. Critical yarn parameters are to be investigated. The values of these tested properties were introduced into a database that ranked the quality of the yarn against industry standards. The paper investigates the possibilities of using the global optimization superimposed diagram response surface methodology in order to identify the spinner feasibility conditions across the customer yarn quality requirements. The spinner approach consists of optimizing the yarn count and twist. We have also studied the customer approach to optimize the yarn responses simultaneously by the use of the desirability functions. The response optimizer searches for a combination of input variables that jointly optimize the set of the responses by satisfying the customer requirements for each response in the set.

11

The Prediction of Cotton Ring Yarn Properties from AFIS Fibre Properties by Using Linear Regression Models

Üreyen M. E., Kadoğlu H.

Fibres & Textiles in Eastern Europe

|

2007

|

Vol. 15, no. 4 (63)

63--67

EN

In this paper some models for predicting the most important ring yarn quality characteristics were built by using AFIS (Advanced Fibre Information System) data. Yarn count, twist and roving properties were also selected as predictors because of their great effect on the yarn properties. A total of 180 ring yarns were produced from 15 different cotton blends on the same ring spinning machine, on the same spinning positions and under the same conditions at Ege University Textile and Apparel Research-Application Centre. Each blend was spun in four yarn counts (29.53 tex, 23.63 tex, 19.69 tex, and 16.88 tex) at three different coefficients of twist (αTt 3639, αTt 4022, and αTt 4404). Linear multiple regression methods were used for the estimation of the yarn quality characteristics. The goodness of fit statistics showed that our equations had very large R2 (coefficient of multiple determination) and adjusted R2 values.

PL

Na podstawie pomiarów wykonanych za pomocą AFIS opracowano model regresyjny dla przewidywania najbardziej istotnych właściwości jakościowych bawełnianych przędz obrączkowych, takich jak masa liniowa, skręt i właściwości niedoprzędu. Wyprodukowano 180 przędz obrączkowych z 15 różnych mieszanek bawełny na tej samej przędzarce, z tym samym punkcie przędzącym i przy tych samych warunkach technologicznych. Dla każdej mieszanki bawełny uzyskiwano przędze o 4 różnych masach liniowych (ok.: 29,5 tex, ok. 23,6 tex, ok. 19,7 tex i ok. 16,9 tex) i 3 współczynniki skrętu αTr = 3639, 4022 i 4404. Zastosowano wielowarstwową regresję liniową dla wyznaczenia charakterystyk jakościowych. Na podstawie wszystkich wartości współczynników RZ stwierdzono bardzo dobrą statystycznie zgodność wyników przewidywanych właściwości jakościowych przędz.

12

Study of effect of spinning process variables on the packing density of ring, rotor and air-jet yarns using the Taguchi method

Kumar A., Ishtiaque S. M., Salhotra K. R.

Autex Research Journal

|

2006

|

Vol. 6, no. 3

122--135

EN

The effect of lap hank, card draft, draft/doublings and drafts at speed frame, ring frame, rotor and air-jet on packing density parameters were analysed using the Taguchi method. The trends of change in packing density with process variables are opposite to those of the yarn diameter and helix angle of the ring, rotor and air-jet yarns studied. The packing density is found to be the highest in air-jet yarn and the lowest in rotor yarn. An increase in draft in the air-jet and a decrease in the rotor spinner increases the packing density of the respective yarns.

13

Comparison of the Properties of Knitted Fabrics Produced by Conventional and Compact Ring - Spun Yarns

Çeken F., Göktepe F.

Fibres & Textiles in Eastern Europe

|

2005

|

Vol. 13, no. 1 (49)

47--50

EN

The new compact yarn spinning system appears to eliminate the spinning triangle problem in the conventional ring spinning process, and is claimed to bring many advantages of yarn quality. However, the benefits of this new concept are still to be investigated extensively. In this research work, we produced plain knitted fabrics by using conventional ring-spun and ring-compact yarns. These fabrics were knitted and dyed under identical conditions. We then tested these fabrics for their appearance after different washing cycles, their pilling behaviour, their colour differences and bursting strengths. The change in the surface of the fabrics after washing in different cycles shows that fabrics of compact yarns maintain their appearance, while others seriously deteriorate. Pilling test results show that the pilling tendency of fabrics of compact ring yarns is much better compared to those of conventional yarns, as expected. On the other hand, test results regarding colour difference indicate that there are significant differences, as the fabrics of compact ring yarns have darker shades. Finally, fabrics of compact ring yarn have generally higher bursting strength, but the differences become less significant as the loop lengths increase in the fabrics.

PL

Nowy system przędzenia kompaktowego został wprowadzony dla wyeliminowania problemów związanych z trójkątem przędzącym, powstającym przy konwencjonalnym przędzeniu obrączkowym. Stwierdzono wielokrotnie i jednoznacznie poprawę jakości otrzymywanej przędzy. Niemniej badania nad uściśleniem otrzymywanych korzyści trwają nadal. W opisanej pracy badano wpływ zastosowania obrączkowej przędzy kompaktowej na dzianiny o splocie lewoprawym. Próbki wytwarzane z bawełnianej przędzy konwencjonalnej i kompaktowej były dziane i barwione w tych samych warunkach. Sprawdzano wygląd próbek po różnych cyklach prania; badano piling, różnice wybawień i wytrzymałość na wypychanie Zmiany wyglądu dzianin po praniach wskazują że dzianiny z przędzy kompaktowej utrzymują swój pierwotny wygląd, podczas gdy te wykonane z przędzy konwencjonalnej wykazują objawy zużycia. Jak się spodziewano okazało się, że również tendencja do pilingu jest znacznie mniejsza dla dzianin z przędz kompaktowych. Z drugiej strony stwierdzono, że istnieją znaczne różnice w wybarwialności - dzianiny mają ciemniejsze odcienie. Również odporność na wypychanie tych dzianin jest zasadniczo wyższa, ale tutaj różnice są mniej ważne, ponieważ w dzianinach z przędz kompaktowych zwiększa się długość oczek.

14

A Comparative Study of the Characteristics of Compact Yarn - Based Knitted Fabrics

Özdil N., Özdoğan E., Demirel A., Öktem T.

Fibres & Textiles in Eastern Europe

|

2005

|

Vol. 13, no. 2 (50)

39--43

EN

The compact spinning system was based on the conventional ring-spinning system. The vast majority of previous work deals with the properties of compact yarn in yarn form. In this study, we inspected fabric samples knitted from compact spun yarn in comparison with fabric samples knitted from classic ring-spun yarn. Knitted double jersey fabrics from 100% combed ring-spun and compact cotton yarns of the same raw material blend were used. The pilling properties, bursting strength and abrasion resistance of these fabrics at different process steps were tested. The effects of enzymatic treatment and washing & dyeing on these fabrics were also examined.

PL

System przędzenia kompaktowego oparty jest na zasadzie konwencjonalnego przędzenia obrączkowego. Większość wcześniejszych prac zajmuje się właściwościami przędz kompaktowych jako takich. W tej pracy badaliśmy próbki dzianin wyprodukowanych z przędz kompaktowych, w porównaniu do próbek dzianin otrzymanych z klasycznych przędz obrączkowych. Produkowano dzianinę dwuprawą na maszynach cylindrycznych ze 100% obrączkowej przędzy bawełnianej czesanej klasycznej i kompaktowej, obydwu wykonanych z tego samego surowca. Badano skłonność dzianin do pilingowania, oraz ich wytrzymałość na rozdzieranie i ścieranie przy różnych warunkach testowania. Ponadto badano wpływ obróbki enzymatycznej, prania i barwienia na wyprodukowane dzianiny

15

Selecting cotton bales by spinning consistency index and micronaire using artifical neural networks

Majumdar A., Majumdar P. K., Sarkar B.

Autex Research Journal

|

2004

|

Vol. 4, no. 1

1--8

EN

This paper presents a method of selecting cotton bales to meet the specified ring yarn properties using artificial neural networks. Five yarn properties and yarn count were used as inputs, whereas the Spinning Consistency Index (SCI) and micronaire were the outputs to the neural network models. Bales were selected according to the predicted combinations of SCI and micronaire. The properties of yarns spun from selected bales show good association with the target yarn properties.

16

Influence of the Spinning Process Parameters on Strength Characteristics of Cotton Yarns

Jackowski T., Chylewska B., Cyniak D.

Fibres & Textiles in Eastern Europe

|

2002

|

Vol. 8, no. 3 (38)

27--31

EN

In this paper, the strength parameters of cotton yarns formed on the Rieter R1 spinning machine and on the Textima ring spinning machine were analysed. For the rotor spinning machine, the influence of linear density of the feeding sliver and of yarns on their specific strength, elongation and elasticity was evaluated. For the rotor spinning machine, the following parameters were used: rotational speed of the rotor - 100,000 r/min (1666.7 r/s), rotational speed of the opening roller - 7,000 r/min (116.7 r/s), linear density of yarns: 18, 20, 25, 30 tex. The spinning machine was fed with slivers after the second passage of drawing with the linear densities: 3.5, 4.0, 4.5, 5.0 ktex. On the ring spinning machine, yarns of linear densities of 25 and 40 tex were formed from the roving 400 tex. Analysis of the results for rotor-spun and ring-spun yarns showed that rotor-spun yarns are characterised by higher elasticity, which makes them a very good material for knitting purposes.

PL

W artykule analizowano parametry wytrzymałościowe przędz bawełnianych formowanych na przędzarce Rl firmy Rieter i przędzarce obrączkowej firmy Textima. Dla przędzarki rotorowej oceniano wpływ masy liniowej taśmy zasilającej i masy liniowej przędz na ich wytrzymałość właściwą, wydłużenie i sprężystość. Na przędzarce rotorowej stosowano następujące parametry: prędkość obrotowa rotora -100.000 obr/min (1666,7 obr/s), prędkość obrotowa bębenka rozwłókniającego - 7.000 obr/min (116,7 obr/s), masa liniowa przędz: 18; 20; 25; 30 tex. Przędzarkę zasilano taśmami po drugim pasażu rozciągania o masach liniowych: 3,5; 4,0; 4,5 i 5,0 ktex. Na przędzarce obrączkowej formowano przędze 25 i 40 tex z niedoprzędu 400 tez. Analiza wyników przędz rotorowych i obrączkowych wykazała, że przędze rotorowe charakteryzują się większą sprężystością, co uzasadnia ich główne zastosowanie na cele dziewiarskie.