Influence of protons on oxide compounds applied in optoelectronic devices

Kaczmarek S. M., Wojtkowska J., Moroz Z., Kisielewski J.

Biuletyn Wojskowej Akademii Technicznej

2000

Vol. 49, nr 2

99-113

Changes in optical properties of some oxide compounds (YAG, YAG: Nd³⁺, YAG: Ce³⁺, YAG: Ce³⁺, Mg²⁺, YAG: Cr³⁺, YAG: Cr⁴⁺, SrLaGa₃O₇: Dy³⁺, SrLaGa₃O₇: Cr³⁺, SrGdGa₃O₇:Cr³⁺ and LiNbO₃: Cu²⁺) induced by 21 MeV proton irradiation were studied. In the optical absorption spectra lines which belong to optically active dopants (like Ce³⁺, Cr³⁺, Fe³⁺) and F-type color centers are seen. Influence of proton irradiation on such centers is observed. It seems to be attributed to the ionization and/or recombination of definite centers. Moreover, for relatively high proton fluencies, Frenkel defects are probably created.

Badano zmiany właściwości optycznych materiałów tlenkowych (YAG, YAG: Nd²⁺, YAG: Ce²⁺, YAG: Ce²⁺, Mg²⁺, YAG: Cr²⁺, YAG: Cr ⁴⁺ , SrLaGa₃O₇: Dy²⁺, SrLaGa₃O₇: Cr²⁺, SrGdGa₃O₇:Cr²⁺ oraz LiNbO₃: Cu²⁺) indukowane przez wiązkę protonów o energii 21MeV z cyklotronu. Wśród linii absorpcyjnych obserwowano linie należące do domieszek aktywnych (jak Ce²⁺, Cr²⁺, Fe²⁺) oraz do centrów barwnych typu F. Oddziaływanie protonów na te centra wydaje się być związane z jonizacją i/lub rekombinacją powyższych centrów. Ponadto, dla względnie wysokich strumieni protonów (1014 protonów/cm²), obserwuje się powstawanie defektów Frenkla.

Growth and characterization of Cr:SrGdGa₃O₇ and Cr:SrLaGa₃O₇ single crystals

Kaczmarek S. M., Berkowski M., Jabłoński R., Pracka I., Kwaśny M., Świrkowicz M.

Biuletyn Wojskowej Akademii Technicznej

1998

Vol. 47, nr 7-8

141-151

Growth and recharging processes of chromium ions in SrGdGa₃O₇ and SrLaGa₃O₇ single crystals incorporated during growth or doping by diffusion (only for SrLaGa₃O₇ crystal) were analyzed. The annealing at 1000°C in air and ionizing with gamma rays (doses from 10³ to 10⁵ Gy) and protons (10¹⁴ cm⁻² only for SrGdGa₃O₇ crystal) were performed. Different kinds of chromium ions valency, from two to four, were found. Electron spin resonance measurements in the temperature range 5-300 K with the use of Brucker spectrometer were also done.

Analizowano proces wzrostu i procesy zmiany walecyjności jonów chromu w monokryształach SrGdGa₃O₇ i SrLaGa₃O₇. Chrom wprowadzono podczas procsu wzrostu oraz w wyniku procesu dyfuzji (tylko dla kryształu SrLaGa₃O₇). Przeprowadzono wygrzwanie w temperaturze 1000°C w powietrzu oraz naświetlania kwantami gamma (dawki 10³ - 10⁵ Gy) i protonami (10¹⁴ cm⁻² tylko dla kryształu SrGdGa₃O₇). Stwierdzono występowanie jonów chromu o walencyjności od 2 do 4. Przeprowadzono również pomiary elektronowego rezonansu spinowego w zakresie temperatur 5-300 K z wykorzystaniem spektrometru firmy