Modeling Viscosity of Converter Slag

Sinelnikov V., Kalisz D.

Archives of Foundry Engineering

2015

Vol. 15, iss. 4 spec.

119--124

The paper is devoted to one of the most important factors influencing steel melting and operation of an oxygen converter, i.e. dynamic viscosity of slag. Knowing typical chemical composition of slag after melting, the viscosity was calculated with the use of Riboud and Urbain empirical models at temperatures 1400 °C to 1700 °C. The obtained mathematical results were compared with the results of simulations obtained with the FactSage program. The discrepancies between these results were caused by model assumptions and the fact that slag in lower temperatures consisted of liquid and solid phases.

Obecna praca poświęcona jest jednemu z najważniejszych czynników wpływających na pracę konwertora tlenowego - lepkości dynamicznej żużla. Znając typowy skład chemiczny żużla uzyskany po wytopie w piecu wykonano obliczenia lepkości żużla przy pomocy empirycznych modeli Ribouda i Urbaina w zakresie temperatur od 1400 °C do 1700 °C. Wykonano również analizę porównawczą wyników obliczeń przy pomocy modeli z wynikami symulacji uzyskanymi z kalkulacji wykonanych za pomocą programu FactSage.

Modeling of Precipitate Oxide and Sulfide Inclusions Formation in Liquid Steel

Didenchuk D., Kalisz D.

Archives of Foundry Engineering

2015

Vol. 15, iss. 4 spec.

19--22

The behaviour of non-metallic inclusions MnO, MnS, FeS, Al2O3, SiO2, Y2O3,Y2S3 in liquid steel were modelled in commercial software FactSage. It allowed for calculating and designing diagrams of dependence of inclusions formation from the concentration of yttrium in determined limits of aluminium and oxygen. As a result, the influence of the increasing yttrium concentration on the precipitations of oxide and sulfide inclusions is observed. The behavior of precipitation the another analyzed oxides and sulfides is also observed in liquid steel, giving a full composition in non-metallic inclusions, formatted in specified conditions. The amounts of mass fractions of Y2O3 and Y2S3 are increasing at the growing Y in liquid steel, which shows the active formation of these inclusions.