Evaluation of the possibility of reduction of highly modified binders technological temperatures

Pucułek Marta, Liphardt Adam, Radziszewski Piotr

Archives of Civil Engineering

|

2021

|

Vol. 67, nr 1

557--570

EN

The article presents results of research on the possibility of reduction of technological temperatures of highly modified binders by using as an additive a fluxing agent of plant origin, developed at the Warsaw University of Technology. The work presents the results of dynamic viscosity tests within the temperature range of 90°C to 180°C for original binders and binders aged using the RTFOT method, modified by adding a fluxing agent of plant origin. On the basis of dynamic viscosity test results, process temperatures for production and compaction of mineral-asphalt mixes with the binding agents being analyzed. Moreover, characteristics of binders were assessed, which define their behavior under high technological temperatures on the basis of multiple stress creep recovery (MSCR) tests. The research results obtained indicate that it is possible to reduce the process temperatures of mineral-asphalt mixes with highly modified binders by liquefying the binder with an additive of plant origin while retaining high resistance to permanent deformations. The MSCR test results prove that mineral-asphalt mixes containing binders highly modified with additives of plant origin can meet the requirements for extremely high traffic loads.

PL

Lepiszcza asfaltowe wysokomodyfikowane wykorzystywane budowy do warstw konstrukcyjnych podatnych nawierzchni drogowych wymagają stosowania wysokich temperatur technologicznych w trakcie procesów wytwarzania, wbudowania i zagęszczania mieszanek mineralno-asfaltowych wytworzonych z ich użyciem. Doświadczenia w stosowaniu lepiszczy wysokomodyfikowanych wskazują, że temperatury technologiczne wymagane dla tego rodzaju lepiszczy są nawet o 20°C wyższe niż dla tradycyjnych polimeroasfaltów. Stosowanie wysokich temperatur, szczególnie w trakcie procesu wytwarzania mieszanki mineralno-asfaltowej stwarza ryzyko nadmiernego postarzenia lepiszcza jak również może prowadzić do degradacji zawartego w nim polimeru. Obecnie istnieje szereg metod umożliwiających obniżenie temperatur technologicznych m.in. stosowanie dodatków chemicznych, organicznych, wosków oraz procesu spieniania. Stosowanie dodatków obniżających lepkość asfaltów w zakresie temperatur technologicznych wymaga także oceny wpływu zastosowania tych dodatków na właściwości lepiszcza w zakresie temperatur eksploatacyjnych. Wskazane jest stosowanie dodatków niepowodujących pogorszenia parametrów eksploatacyjnych lepiszcza takich jak odporność na deformacje trwałe, zmęczenie czy spękania niskotemperaturowe. W artykule przedstawiono wyniki badań nad możliwością obniżenia temperatur technologicznych lepiszcza wysokomodyfikowanego poprzez zastosowanie opracowanego w Politechnice Warszawskiej dodatku upłynniającego pochodzenia roślinnego. W pracy przedstawiono wyniki badań lepkości dynamicznej w zakresie temperatur od 90°C do 180°C dla lepiszczy oryginalnych oraz starzonych metodą RTFOT zmodyfikowanych dodatkiem upłynniającym pochodzenia roślinnego. Na podstawie wyników badania lepkości dynamicznej wyznaczone zostały temperatury technologiczne procesów wytwarzania oraz zagęszczania mieszanek mineralno-asfaltowych z analizowanymi lepiszczami. Temperatury technologiczne wyznaczono przyjmując optymalne poziomy lepkości, przy których możliwe jest prawidłowe otoczenie lepiszczem ziaren kruszywa, wynoszący 0,2 Pa·s a także prawidłowe zagęszczenie mieszanki mineralno-asfaltowej w zakresie od 2 Pa·s do 20 Pa·s. Ponad to dokonano oceny właściwości lepiszczy charakteryzujących ich zachowanie w wysokich temperaturach eksploatacyjnych na podstawie badań cyklicznego pełzania z odprężeniem (MSCR). Uzyskane wyniki badań wskazują, że jest możliwe obniżenie temperatur technologicznych mieszanek mineralnoasfaltowych z lepiszczem wysokomodyfikowanym poprzez upłynnienie lepiszcza dodatkiem pochodzenia roślinnego przy jednoczesnym zachowaniu wysokiej odporności na deformacje trwałe. Wyniki badania MSCR dowodzą, że zastosowanie dodatku upłynniającego - Biofluxu, do lepiszczy wysokomodyfikowanych nie powoduje pogorszenia ich właściwości wysokotemperaturowych charakteryzowanych procentowym nawrotem r oraz modułem podatności Jnr.

2

Influence of temperature on the quality of briquettes in the giant miscanthus densification process

Demianiuk L., Demianiuk A. B.

Engineering Transactions

|

2016

|

Vol. 64, iss. 2

171--180

EN

A continuous increase in demand for biomass for energy purposes is the reason why people have begun growing plants known as energy crops, such as common osier, Jerusalem artichoke, giant miscanthus, etc. The power industry most often utilises biomass in the form of pellets and briquettes. One of the basic parameters of the biomass densification process is temperature. This article presents the results of the study about the influence of temperature in the giant miscanthus densification process on the quality of briquettes which are intended for combustion in combined heat and power plants and in stoker furnaces in individual households.

3

Kinetyka wzrostu powłoki ochronnej podczas wysoko- i niskotemperaturowego cynkowania zanurzeniowego odlewów z żeliwa sferoidalnego

Kopyciński D., Guzik E., Szczęsny A., Siekaniec D.

Archives of Foundry Engineering

|

2015

|

Vol. 15, iss. 2 spec.

47--50

PL

W pracy przedstawiono porównanie mikrostruktury powłoki cynkowej otrzymanej na powierzchni odlewu z żeliwa sferoidalnego gatunku EN-GJS-5007 podczas zabiegu cynkowania zanurzeniowego w procesie „niskotemperaturowym” 450°C oraz „wysokotemperaturowym” 580°C. Zbadano kinetykę wzrostu powłoki cynkowej, zidentyfikowano wzrastające fazy Fe-Zn oraz występowanie wydzieleń „twardego cynku” w powłoce.

EN

The paper presents a comparison of the zinc coating microstructure obtained on EN-GJS-500-7 grade ductile cast iron surface during the hot dip galvanizing in the "low temperature" 450 °C and "high temperature" 580 °C. The kinetics of growth of the zinc coating was investigated. The phases of Fe-Zn and the presence of precipitates "hard zinc" in the coating have been identified.

4

Sieciowanie kauczuku butadienowo-styrenowego w obniżonej temperaturze pod wpływem układów redoks

Pingot T., Pingot M., Zaborski M.

Polimery

|

2010

|

T. 55, nr 11-12

825-831

PL

W celu określenia możliwości sieciowania kauczuku butadienowo-styrenowego (SBR) w obniżonej temperaturze użyto szeregu układów redoks różniących się między sobą rodzajem utleniacza oraz reduktora; jako czynnik redukujący w tych układach zastosowano sole metali o zmiennej wartościowości. Rozwiązanie to pozwoliło na znaczne zmniejszenie wartości energii aktywacji procesu sieciowania, co umożliwiło prowadzenie procesu sieciowania nawet w temp. 80 °C. Zbadano wpływ składu układów redoks na właściwości reometryczne, przebieg sieciowania, gęstość sieci, a także na właściwości mechaniczne i na proces starzenia pod wpływem UV wulkanizatów nienapełnionych i napełnionych krzemionką. Wykazano istnienie możliwości sieciowania elastomerów SBR w obniżonej temperaturze również za pomocą układów zawierających wodoronadtlenek kumenu (CHP), w których typowy reduktor zastąpiony solą oniową - bromkiem tetrabutyloamoniowym (TBAB) lub tetraoktyloamoniowym (TOAB).

EN

The possibilities of crosslinking styrene butadiene rubber (SBR) at low temperatures with a series of redox systems made up of different types of reducing and oxidizing agents have been explored (Table 1). Transition metal salts were used as reducing agents. A pronounced decrease in the activation energy of the crosslinking process (Fig. 1) was achieved by adopting this method, therefore the crosslinking reaction could be performed at temperatures as low as 80 °C. The influence of the composition of the redox system on rheometrical properties (Table 2), the crosslinking process (Figs. 2 and 3), crosslinking density (Figs. 4-6, Table 3) as well as on mechanical properties was determined. Moreover, the ageing process of unfilled and filled vulcanizates with silicates under UV irradiation was evaluated (Table 4, Figs. 7 and 8). The possibility of crosslinking SBR at low temperatures with the application of systems containing cumene hydroperoxide, in which the reducing agent had been replaced by an ammonium salt - tetrabutylammonium bromide (TBAB) or tetraoctylammonium bromide (TOAB) was also explored.

5

Wpływ wybranych parametrów procesu ekstruzji na zmiany barwy ekstrudatu

Ekielski A., Biller E., Żelaziński T.

Inżynieria Rolnicza

|

2005

|

R. 9, nr 10

65--73

PL

W pracy zbadano zależności pomiędzy zmianami barwy powierzchni ekstrudatu kukurydzianego, a parametrami procesu: wilgotnością surowca, natężeniem przepływu materiału przez ekstruder i temperaturą. Badania polegały na analizie zdjęć próbek ekstrudatu uzyskanego w procesem o znanych wartościach parametrów sterujących. W badaniach wykorzystano program graficzny Adobe Photoshop® 6.0 CE. Na podstawie uzyskanych wyników badań wyliczono zależności pomiędzy parametrami barwy powierzchni ekstrudatu kukurydzianego, a wybranymi warunkami przebiegu procesu ekstruzji.

EN

The study involved research on relations between corn extrudate surface colour changes and process parameters: raw material moisture content, intensity of material flow through the extruder, and temperature. The research involved sample photo analysis of extrudate obtained in the process of known control parameter values. The Adobe Photoshop 6.0 CE graphic application was employed for research purposes. Obtained research results gave grounds to compute relations between corn extrudate surface colour parameters and selected extrusion process run conditions.